Golf ball incorporating highly crosslinked thermoset fluorescent microspheres and methods of making same

• US 10,035,043 B2
• Filed: 12/15/2016
• Issued: 07/31/2018
• Est. Priority Date: 12/15/2016
• Status: Active Grant

• Current Assignee: Acushnet Company (FILA Holdings Corp.)
• Original Assignee: Acushnet Company (FILA Holdings Corp.)
• Inventors: Hogge, Matthew F., Serdahl, Peter L., Cooper, Scott
• Primary Examiner(s): SIMMS JR, JOHN ELLIOTT
• Application Number:
  US15/379,762
• Publication Number:
  US 20180169478A1
• Time in Patent Office: 593 Days
• CPC Class Codes: A63B 37/0024 Materials other than ionomers or polyurethane
• CPC Class Codes: A63B 37/0033 Thickness
• CPC Class Codes: A63B 37/0064 Diameter
• CPC Class Codes: A63B 37/0074 Two piece balls, i.e. cover and core
• CPC Class Codes: A63B 45/00 Apparatus or methods for manufacturing balls working of plastics or substances in a plastic state B29

Abstract

A golf ball comprising at least one layer consisting of a color-stable composition comprising a color concentrate composition comprising a carrier resin, at least one backer pigment and a plurality of highly crosslinked thermoset fluorescent microspheres having a hue that is substantially similar to a hue created by the at least one backer pigment. Each highly crosslinked thermoset fluorescent microsphere may be substantially spherical. Each highly crosslinked thermoset fluorescent microsphere may have a diameter of from about 0.5 micron to about 2.0 microns. The carrier resin may be an ionomer. The color-stable composition may comprise a mixture of the color concentrate composition and a polymer composition, wherein the polymer composition may be an ionomer composition.

Claims

1. A golf ball comprising at least one layer consisting of a color-stable composition comprising a color concentrate composition comprising (i) a carrier resin;

(ii) at least one pigment that does not contain any highly crosslinked thermoset fluorescent microspheres; and

(iii) a plurality of highly crosslinked thermoset fluorescent microspheres;

wherein the plurality of highly crosslinked thermoset fluorescent microspheres has a predominant hue in the CIELAB color space that is the same as a hue created in the CIELAB color space by the at least one pigment that does not contain any highly crosslinked thermoset fluorescent microspheres;

wherein each highly crosslinked thermoset fluorescent microsphere is substantially spherical;

wherein each highly crosslinked thermoset fluorescent microsphere has a diameter of from about 0.5 micron to about 2.0 microns;

wherein the carrier resin is an ionomer; and

wherein the ratio of parts by weight of carrier resin to parts by weight of plurality of highly crosslinked thermoset fluorescent microspheres is about 1.0;

0.20 to 1.0;

3.5.

2. The golf ball of claim 1, wherein the pigment that does not contain any highly crosslinked thermoset fluorescent microspheres includes titanium dioxide and has a hue other than white.

3. The golf ball of claim 2, wherein the ratio of parts by weight of pigment not containing any highly crosslinked thermoset fluorescent microspheres to parts by weight of plurality of highly crosslinked thermoset fluorescent microspheres is about 1.0:

0.5 to 1.0;

2.0.

4. The golf ball of claim 3, wherein the color-stable composition comprises a mixture of the color concentrate composition and a polymer composition.

5. The golf ball of claim 4, wherein the polymer composition is an ionomer composition.

6. The golf ball of claim 5, wherein the mixture comprises about 95 to 98 parts by weight of a blend of the carrier resin and the ionomer composition, about 0.2 to 1.0 parts by weight of at least one backer pigment, and about 0.1 to 2.0 parts by weight of plurality of highly crosslinked thermoset fluorescent microspheres, based on the total weight of the color-stable composition.

7. The golf ball of claim 6, wherein the mixture further comprises about 0.1 to 1.0 parts by weight of at least one ultra violet (UV) absorber, about 0.1 to 1.0 parts by weight of at least one hindered amine light stabilizer (HALS), or a combination thereof.

8. The golf ball of claim 7, wherein the at least one UV absorber selected from the group consisting of triazines, benzoxazinones, benzotriazoles, benzophenones, benzoates, formamidines, cinnamates/propenoates, aromatic propanediones, benzimidazoles, cycloaliphatic ketones, formanilides (including oxamides), cyanoacrylates, benzopyranones, salicylates, substituted acrylonitriles, or combinations thereof.

9. The golf ball of claim 7, wherein the at least one HALS is a derivative of 2,2,6,6-tetraamethylpiperidine.

10. The golf ball of claim 7, wherein the at least one layer is a cover layer having a thickness of from about 0.030 inches to about 0.085 inches disposed about a polybutadiene-based core having a diameter of from about 1.5 inches to about 1.620 inches.

11. A method of making a golf ball comprising:

providing a subassembly;

providing a color-stable composition comprising a color concentrate composition comprising (i) a carrier resin, (ii) at least one pigment not containing any highly crosslinked thermoset fluorescent microspheres, and (iii) a plurality of highly crosslinked thermoset fluorescent microspheres;

wherein the plurality of highly crosslinked thermoset fluorescent microspheres has a predominant hue in the CIELAB color space that is the same as a hue created in the CIELAB color space by the at least one pigment that does not contain any highly crosslinked thermoset fluorescent microspheres; and

forming at least one layer consisting of the color-stable composition about the subassembly;

wherein each highly crosslinked thermoset fluorescent microsphere is substantially spherical;

wherein each highly crosslinked thermoset fluorescent microsphere has a diameter of from about 0.5 micron to about 2.0 microns;

wherein the carrier resin is an ionomer; and

wherein the ratio of parts by weight of carrier resin to parts by weight of plurality of highly crosslinked thermoset fluorescent microspheres is about 1.0;

0.20 to 1.0;

3.5.

12. The method of claim 11, wherein the pigment that does not contain any highly crosslinked thermoset fluorescent microspheres includes titanium dioxide and has a hue other than white.

13. The method of claim 12, wherein the ratio of parts by weight of pigment that does not contain any highly crosslinked thermoset fluorescent microspheres to parts by weight of plurality of highly crosslinked thermoset fluorescent microspheres is about 1.0:

0.5 to 1.0;

2.0.

14. The golf ball of claim 13, wherein the color-stable composition comprises a mixture of the color concentrate composition and an ionomer composition.

15. The method of claim 14, wherein the mixture comprises about 95 to 98 parts by weight of an ionomer blend of the carrier resin and the ionomer composition, about 0.2 to 1.0 parts by weight of at least one backer pigment, and about 0.1 to 2.0 parts by weight of plurality of highly crosslinked thermoset fluorescent microspheres, based on the total weight of the color-stable composition.

16. The method of claim 15, wherein the mixture further comprises about 0.1 to 1.0 parts by weight of at least one ultra violet (UV) absorber, about 0.1 to 1.0 parts by weight of at least one hindered amine light stabilizer (HALS), or a combination thereof.

17. The method of claim 16, wherein at least one UV absorber is selected from the group consisting of triazines, benzoxazinones, benzotriazoles, benzophenones, benzoates, formamidines, cinnamates/propenoates, aromatic propanediones, benzimidazoles, cycloaliphatic ketones, formanilides (including oxamides), cyanoacrylates, benzopyranones, salicylates, substituted acrylonitriles, or combinations thereof.

18. The method of claim 16, wherein at least one HALS is a derivative of 2,2,6,6-tetraamethylpiperidine.

19. The method of claim 16, wherein the at least one layer is a cover layer disposed about a polybutadiene-based core.