Artificial breast implant provided on the surface thereof with silicone open cell foam layer, and method for producing the same

• US 10,085,831 B2
• Filed: 06/21/2013
• Issued: 10/02/2018
• Est. Priority Date: 11/19/2009
• Status: Active Grant

• Current Assignee: Won Seok Yu
• Original Assignee: Won Seok Yu
• Inventors: Yu, Won Seok
• Primary Examiner(s): Tucker, Philip C
• Assistant Examiner(s): Blades, John
• Application Number:
  US13/923,984
• Publication Number:
  US 20130302510A1
• Time in Patent Office: 1,929 Days
• Field of Search: 156242, 427 224
• CPC Class Codes: A61F 2/0077 Special surfaces of prostheses, e.g. for improving ingrowth A61F2/30767 takes precedence
• CPC Class Codes: A61F 2/12 Mammary prostheses and implants
• CPC Class Codes: B29C 41/14 Dipping a core B29C41/10 takes precedence
• CPC Class Codes: B29C 44/005 Avoiding skin formation; Making foams with porous surfaces
• CPC Class Codes: B29C 67/202 comprising elimination of a solid or a liquid ingredient
• CPC Class Codes: B29K 2083/005 LSR, i.e. liquid silicone rubbers, or derivatives thereof
• CPC Class Codes: B29L 2031/7532 Artificial members, protheses

Abstract

Disclosed are an artificial breast implant in which the surface thereof is formed or modified with a silicone open cell (open pore) foam layer, and a method for producing the same. More specifically, disclosed are an artificial breast implant that has a surface including an open cell foam layer made of silicone and thus minimizes side effects such as in vivo rejection, which may occur after implantation of the implant into the body, in particular, the occurrence of capsular contracture to achieve superior biocompatibility and safety, and a method for producing the same.

Claims

1. A method for producing an artificial breast implant comprising the processes of:

dipping a breast-shaped mold in a silicone solution;

drying and curing the silicon solution adhered to the mold, and thereby forming a cured silicone shell;

forming an open cell foam layer on an outer surface of the cured silicone shell;

forming an aperture on a bottom of the cured silicone shell, and removing the cured silicone shell from the mold through the aperture, thereby obtaining an artificial breast shell; and

adhering a silicone film including a leakage prevention film to the aperture to seal the aperture,

wherein said forming the open cell foam layer process includes the steps of;

(a) dipping the cured silicone shell adhered to the mold in a second silicone solution, and taking the cured silicone shell out to form a silicone solution film on the outer surface of the cured silicone shell;

(b) scattering or spraying solid particles or powder with an appropriate size to the surface of the silicone solution film such that the silicone solution film loses flowability;

(c) spraying or applying by dipping an organic solvent on a resultant product of said step (b); and

(d) re-scattering or re-spraying solid particles or powder on a resultant product of said step (c),

wherein, in said forming the open cell foam layer process, the solid particles or powder is not dissolved in the silicone solution and does not affect physical properties of the silicone solution, and is dissolved in a washable solvent and removed thereby,

wherein said forming the open cell foam layer process is repeated until the open cell foam layer has a desired thickness, in which the desired thickness of the open cell foam layer is obtained by controlling (e) a concentration of silicone solution, (f) an average size of solid particles or powders, the average size being changeable at selected repetition steps of said forming, and (g) an organic solvent spraying speed,

wherein, in said forming the open cell foam layer process, the treated solid particles or powder for formation of the open cell are removed by treating the artificial breast shell using washing with water, treating with water vapor, heating and high-pressure vapor treating the artificial breast shell provided with dried and cured open cell foam layer in the presence of 140°

C. water and 1.4 atm vapor pressure, for about 30 hours, to remove incompletely removed solid particles or powder from the artificial breast shell.

2. The method of claim 1, wherein the solid particles or powder is sodium chloride, ammonium carbonate, ammonium phosphate, or ammonium chloride.

3. The method of claim 1, wherein the organic solvent is benzene, toluene, or xylene.

4. The method of claim 1, wherein the washable solvent is water.

5. The method of claim 1, wherein said forming the open cell foam layer process further includes drying and curing the formed open cell foam layer.

6. A method for producing an artificial breast implant comprising the processes of:

dipping a breast-shaped mold in a silicone solution;

drying and curing the silicon solution adhered to the mold, and thereby forming a cured silicone shell;

forming an open cell foam layer on an outer surface of the cured silicone shell;

forming an aperture on a bottom of the cured silicone shell, and removing the cured silicone shell from the mold through the aperture, thereby obtaining an artificial breast shell; and

adhering a silicone film including a leakage prevention film to the aperture to seal the aperture,

wherein said forming the open cell foam layer process includes the steps of;

(a) dipping the cured silicone shell adhered to the mold in a second silicone solution, and taking the cured silicone shell out to form a silicone solution film on the outer surface of the cured silicone shell;

(b) scattering or spraying solid particles or powder with an appropriate size to the surface of the silicone solution film such that the silicone solution film loses flowability;

(c) spraying or applying by dipping an organic solvent on a resultant product of said step (b); and

(d) re-scattering or re-spraying solid particles or powder on a resultant product of said step (c),

wherein, in said forming the open cell foam layer process, the solid particles or powder is not dissolved in the silicone solution and does not affect physical properties of the silicone solution, and is dissolved in a washable solvent and removed thereby,

wherein said forming the open cell foam layer process is repeated until the open cell foam layer has a desired thickness, in which the desired thickness of the open cell foam layer is obtained by controlling (e) a concentration of silicone solution, a size of solid particles or powders, and an organic solvent spraying speed,

wherein, in said forming the open cell foam layer process, the treated solid particles or powder for formation of the open cell are removed by treating the artificial breast shell using washing with water, treating with water vapor, heating and high-pressure vapor treating the artificial breast shell provided with dried and cured open cell foam layer in the presence of 140°

C. water and 1.4 atm vapor pressure, for about 30 hours, to remove incompletely removed solid particles or powder from the artificial breast shell.