Electrochromic device including a transparent conductive oxide layer and a bus bar and a process of forming the same

• US 10,222,674 B2
• Filed: 04/13/2017
• Issued: 03/05/2019
• Est. Priority Date: 04/19/2016
• Status: Active Grant

• Current Assignee: Sage Electrochromics, Inc (Compagnie de Saint-Gobain SA)
• Original Assignee: Sage Electrochromics, Inc (Compagnie de Saint-Gobain SA)
• Inventors: Brossard, Sophie
• Primary Examiner(s): Ben, Loha
• Application Number:
  US15/487,133
• Publication Number:
  US 20170299934A1
• Time in Patent Office: 691 Days
• Field of Search: 359265, 359275, 359601, 359603, 359604, 345105
• CPC Class Codes: B32B 17/10385 for ohmic resistance heating
• CPC Class Codes: B32B 17/10513 Electrochromic layer
• CPC Class Codes: E06B 2009/2464 featuring transparency control by applying voltage, e.g. LCD, electrochromic panels
• CPC Class Codes: E06B 3/6722 with adjustable passage of light
• CPC Class Codes: E06B 9/24 Screens or other constructions affording protection against light, especially against sunshine; Similar screens for privacy or appearance; Slat blindsoperating, guiding or securing devices or arrangements for roll-type closures E06B9/56; free-hanging flexible screens A47H23/00
• CPC Class Codes: G02F 1/1345 Conductors connecting electrodes to cell terminals
• CPC Class Codes: G02F 1/15 based on an electrochromic effect
• CPC Class Codes: G02F 1/1523 comprising inorganic material
• CPC Class Codes: G02F 1/1524 Transition metal compounds
• CPC Class Codes: G02F 1/1533 structural features not otherwise provided for
• CPC Class Codes: G02F 1/155 Electrodes
• CPC Class Codes: G02F 1/163 Operation of electrochromic cells, e.g. electrodeposition cells; Circuit arrangements therefor
• CPC Class Codes: G02F 2001/1536 additional, e.g. protective, layer inside the cell
• CPC Class Codes: G02F 2201/50 Protective arrangements
• CPC Class Codes: G02F 2201/501 Blocking layers, e.g. against migration of ions
• CPC Class Codes: G02F 2201/508 Pseudo repairing, e.g. a defective part is brought into a condition in which it does not disturb the functioning of the device
• CPC Class Codes: G09G 3/38 using electrochromic devices
• CPC Class Codes: H01R 25/14 Rails or bus-bars constructed so that the counterparts can be connected thereto at any point along their length supporting elements for lighting devices, displaceable along guiding elements and making electrical contact with conductors running along the guiding elements F21V21/35
• CPC Class Codes: H01R 25/145 Details, e.g. end pieces or joints H01R25/147 takes precedence

Abstract

An electrochromic device can include a substrate, a transparent conductive oxide layer over the substrate, and a bus bar over the substrate. The bus bar can include silver and has a resistivity of at most 6.7×10⁻⁶ Ω*cm, an average adhesion strength to SiO₂ of at least 3N based on 20 measurements, as determined by Method A of ASTM B905-00 (Reapproved 2010), or a classification of at least 4, as determined by Method B of ASTM B905-00 (Reapproved 2010). In another aspect a process of forming an electrochromic device can include forming a transparent conductive oxide layer over a substrate; forming a bus bar precursor over the substrate, wherein the precursor includes silver; and firing the precursor to form a bus bar. Firing can be performed such that the first bus bar is at a temperature of at least 390° C.

Claims

1. An electrochromic device comprising:

a substrate;

a first transparent conductive oxide layer over the substrate; and

a first bus bar over the substrate, wherein the first bus bar includes silver and has;

a resistivity of at most 8.0×

10<sup>−

6</sup> Ω

*cm;

an average adhesion strength to SiO₂ of at least 3N based on 20 measurements, as determined by Method A of ASTM B905-00 (Reapproved

     2010);

an average adhesion strength to SiO₂ of at least 3 based on 20 measurements, as determined by Method B of ASTM B905-00 (Reapproved

     2010);

or

a combination thereof.

2. The electrochromic device of claim 1, further comprising an oxidation-resistant layer (1) between the substrate and the first transparent conductive oxide layer or (2) over the first transparent conductive oxide layer.

3. The electrochromic device of claim 2, wherein the oxidation-resistant layer comprises silicon nitride, aluminum nitride, titanium nitride, tungsten nitride, tantalum nitride, titanium silicon nitride, tungsten silicon nitride, or tantalum silicon nitride.

4. The electrochromic device of claim 2, further comprising an insulating layer overlying the oxidation-resistant layer, wherein the insulating layer comprises an oxide.

5. The electrochromic device of claim 4, further wherein the insulating layer comprises SiO₂.

6. The electrochromic device of claim 1, wherein the first bus bar has a resistivity of at most 6.0×

10<sup>−

6</sup> Ω

*cm.

7. The electrochromic device of claim 1, wherein the first bus bar has an average adhesion strength to SiO₂ of at least 5 N based on 20 measurements as determined by Method A of ASTM B905-00 (Reapproved 2010).

8. The electrochromic device of claim 1, wherein the first bus bar has a classification of at least 4 as determined by Method B of ASTM B905-00 (Reapproved 2010).

9. The electrochromic device of claim 1, wherein the first transparent conductive oxide layer comprises a doped metal oxide.

10. The electrochromic device of claim 9, wherein the doped metal oxide comprises a tin oxide doped with a Group 13 element, a zinc oxide doped with a Group 13 element, or any combination thereof.

11. The electrochromic device of claim 1, further comprising:

a first electrode that is an electrochromic electrode or a counter electrode;

a second electrode that is the other of the electrochromic electrode or a counter electrode;

a ceramic electrolyte layer disposed between the first electrode and the second electrode; and

a second transparent conductive oxide layer that is closer to the second electrode than to the first electrode,

wherein the first transparent conductive oxide layer is closer to the first electrode than to the second electrode.

12. The electrochromic device of claim 1, wherein the substrate is flexible.

13. A process of forming an electrochromic device comprising:

forming a first transparent conductive oxide layer over a substrate;

forming a bus bar precursor over the substrate, wherein the bus bar precursor includes silver; and

firing the bus bar precursor to form a first bus bar, wherein firing is performed such that the first bus bar is at a temperature of at least 390°

C.

14. The process of claim 13, further comprising forming an oxidation-resistant layer, such that the oxidation-resistant layer is (1) between the substrate and the first transparent conductive oxide layer or (2) over the first transparent conductive oxide layer.

15. The process of claim 14, wherein forming the oxidation-resistant layer is performed by a sputter deposition technique.

16. The process of claim 13, wherein firing the bus bar precursor is performed such that the first bus bar is at a temperature of greater than 400°

C.

17. The process of claim 13, further comprising removing other organic material from the bus bar precursor after forming the bus bar precursor over the substrate and before firing the bus bar precursor.

18. The process of claim 17, wherein removing the other organic material is performed at a temperature of at most 350°

C.

19. The process of claim 13, wherein firing the bus bar precursor is performed after forming the first transparent conductive oxide layer.

20. The process of claim 13, further comprising shaping the electrochromic device after firing the bus bar precursor, wherein bending is performed at a temperature of at least 600°

C.