Chain-extended polydimethylsiloxane vinylic crosslinkers and uses thereof

• US 10,301,451 B2
• Filed: 10/09/2017
• Issued: 05/28/2019
• Est. Priority Date: 10/11/2016
• Status: Active Grant

• Current Assignee: Alcon Incorporated
• Original Assignee: Novartis Ag
• Inventors: Jing, Feng, Chang, Frank
• Primary Examiner(s): Loewe, Robert S
• Application Number:
  US15/727,666
• Publication Number:
  US 20180100053A1
• Time in Patent Office: 596 Days
• Field of Search: None
• CPC Class Codes: C08F 2810/20 leading to a crosslinking, either explicitly or inherently
• CPC Class Codes: C08G 77/14 containing silicon bound to oxygen-containing groups C08G77/045 takes precedence
• CPC Class Codes: C08G 77/20 containing silicon bound to unsaturated aliphatic groups C08G77/045 takes precedence
• CPC Class Codes: C08G 77/38 Polysiloxanes modified by chemical after-treatment C08G77/045 takes precedence
• CPC Class Codes: C08G 77/388 containing nitrogen
• CPC Class Codes: C08G 77/392 containing sulfur
• CPC Class Codes: C08K 3/04 Carbon
• CPC Class Codes: C08K 5/0025 Crosslinking or vulcanising agents; including accelerators
• CPC Class Codes: C08K 5/5419 containing at least one Si—C bond
• CPC Class Codes: C08K 7/06 Elements
• CPC Class Codes: G02C 7/04 Contact lenses for the eyes disinfection or sterilisation of contact lenses A61L12/00

Abstract

The invention provides a chain-extended polydiorganosiloxane vinylic crosslinker which comprises (1) a polymer chain comprising at least two polydiorganosiloxane segments and one hydrophilized linker between each pair of polydiorganosiloxane segements, wherein each polydiorganosiloxane comprises at least 5 dimethylsiloxane units in a consecutive sequence, wherein the hydrophilized linker is a divalent radical having at least two (meth)acrylamide moieties; (2) two terminal (meth)acryloyl groups, wherein the chain-extended polydiorganosiloxane vinylic crosslinker has an average molecular weight of at least about 1500 Daltons. The present invention is also related to a silicone hydrogel contact lens, which comprises repeating units derived from a chain-extended polydiorganosiloxane vinylic crosslinker of the invention. In addition, the invention provides a method for making silicone hydrogel contact lenses using a lens-forming formulation comprising a chain-extended polydiorganosiloxane vinylic crosslinker of the invention.

Claims

1. A chain-extended polydiorganosiloxane vinylic crosslinker, comprising:

(1) a polymer chain comprising at least two polydiorganosiloxane segments and one hydrophilized linker (designated “

hpL”

) between each pair of polydiorganosiloxane segements, wherein each polydiorganosiloxane comprises at least 5 dimethylsiloxane units in a consecutive sequence, wherein the hydrophilized linker is a divalent radical of formula (I) or (II)

2. The chain-extended polydiorganosiloxane vinylic crosslinker according to claim 1, wherein the chain-extended polydiorganosiloxane vinylic crosslinker is defined by one of formula (VI) to (VIII)

3. The chain-extended polydiorganosiloxane vinylic crosslinker according to claim 2, wherein the chain-extended polydiorganosiloxane vinylic crosslinker is defined by formula (VI).

4. The chain-extended polydiorganosiloxane vinylic crosslinker according to claim 2, wherein the chain-extended polydiorganosiloxane vinylic crosslinker is defined by formula (VII).

5. The chain-extended polydiorganosiloxane vinylic crosslinker according to claim 2, wherein the chain-extended polydiorganosiloxane vinylic crosslinker is defined by formula (VIII).

6. The chain-extended polydiorganosiloxane vinylic crosslinker according to claim 1, wherein Y₁ is a divalent radical of formula (III).

7. The chain-extended polydiorganosiloxane vinylic crosslinker according to claim 1, wherein Y₁ is a divalent radical of formula (IV).

8. The chain-extended polydiorganosiloxane vinylic crosslinker according to claim 1, wherein the chain-extended polydiorganosiloxane vinylic crosslinker is free of unstable bonds selected from the group consisting of ester bond with a tertiary carbon atom adjacent to the carbonyl group of the ester bond, urea bond, urethane bond, polyethylene glycol segment, and combinations thereof, in the polymer chain of the chain-extended polydiorganosiloxane vinylic crosslinker between the two terminal (meth)acryloyl groups.

9. A silicone hydrogel contact lens comprising a crosslinked polymeric material which comprises:

units of a chain-extended polydiorganosiloxane vinylic crosslinker claim 1;

units of a siloxane-containing vinylic monomer;

units of at least one hydrophilic vinylic monomer,

wherein the silicone hydrogel contact lens, when being fully hydrated, has an oxygen permeability (Dk) of at least about 70 barrers, a water content of from about 25% to about 70% by weight, and an elastic modulus of from about 0.2 MPa to about 1.2 MPa.

10. The silicone hydrogel contact lens according to claim 9, wherein the hydrophilic vinylic monomer is selected from the group consisting of N-vinylpyrrolidone, N,N-dimethyl (meth)acrylamide, (meth)acrylamide, hydroxylethyl (meth)acrylamide, hydroxyethyl (meth)acrylate, glycerol methacrylate (GMA), polyethylene glycol (meth)acrylate, polyethylene glycol C₁-C₄-alkyl ether (meth)acrylate having a weight average molecular weight of up to 1500, N-vinyl formamide, N-vinyl acetamide, N-vinyl isopropylamide, N-vinyl-N-methyl acetamide, N-methyl-3-methylene-2-pyrrolidone, 1-ethyl-3-methylene-2-pyrrolidone, 1-methyl-5-methylene-2-pyrrolidone, 1-ethyl-5-methylene-2-pyrrolidone, 5-methyl-3-methylene-2-pyrrolidone, 5-ethyl-3-methylene-2-pyrrolidone, (meth)acrylic acid, ethylacrylic acid, and combinations thereof.

11. The silicone hydrogel contact lens according to claim 10, wherein the crosslinked polymeric material further comprises units of a hydrophobic vinylic monomer free of silicone, units of a non-silicone vinylic crosslinker, units of a UV-absorbing vinylic monomer, or a combination thereof.

12. The silicone hydrogel contact lens according to claim 11, wherein the silicone hydrogel contact lens a thermal stability as characterized by having an autoclave-induced change,

13. A method for producing silicone hydrogel contact lenses, comprising the steps of:

preparing a lens-forming composition which is clear at room temperature and/or at a temperature of from 0 to about 4°

C., wherein the lens-forming composition comprises (a) from about 5% to about 35% by weight of a chain-extended polydiorganosiloxane vinylic crosslinker of claim 1, (b) a siloxane-containing vinylic monomer, (c) from about 30% to about 60% by weight of at least one hydrophilic vinylic monomer, (d) at least one free-radical initiator, provided that the above-listed polymerizable components and any additional polymerizable components add up to 100% by weight;

introducing the lens-forming composition into a mold, wherein the mold has a first mold half with a first molding surface defining the anterior surface of a contact lens and a second mold half with a second molding surface defining the posterior surface of the contact lens, wherein said first and second mold halves are configured to receive each other such that a cavity is formed between said first and second molding surfaces; and

curing thermally or actinically the lens-forming composition in the lens mold to form a silicone hydrogel contact lens, wherein the silicone hydrogel contact lens has an oxygen permeability (Dk) of at least about 70 barrers, a water content of from about 25% to about 70% by weight, an elastic modulus of from about 0.2 MPa to about 1.2 MPa.

14. The method according to claim 13, wherein the lens-forming composition is a solventless liquid mixture and comprises a blending vinylic monomer selected from the group consisting of a C₁-C₁₀ alkyl methacrylate, isobornylmethacrylate, isobornylacrylate, cyclopentylmethacrylate, cyclopentylacrylate, cyclohexylmethacrylate, cyclohexylacrylate, styrene, 2,4,6-trimethylstyrene (TMS), and t-butyl styrene (TBS), and combinations thereof.

15. The method according to claim 13, wherein the lens-forming composition comprises an organic solvent.

16. The method according to claim 13, wherein the total amount of all silicone-containing polymerizable components present in the lens-forming composition is about 65% or less.

17. The method according to claim 16, wherein the hydrophilic vinylic monomer is a hydrophilic N-vinyl monomer.

18. The method according to claim 16, wherein the lens-forming composition further comprises a non-silicone vinylic crosslinker selected from the group consisting of ethyleneglycol di-(meth)acrylate, diethyleneglycol di-(meth)acrylate, triethyleneglycol di-(meth)acrylate, tetraethyleneglycol di-(meth)acrylate, glycerol di-(meth)acrylate, 1,3-propanediol di-(meth)acrylate, 1,3-butanediol di-(meth)acrylate, 1,4-butanediol di-(meth)acrylate, glycerol 1,3-diglycerolate di-(meth)acrylate, ethylenebis[oxy(2-hydroxypropane-1,3-diyl)] di-(meth)acrylate, bis[2-(meth)acryloxyethyl] phosphate, trimethylolpropane di-(meth)acrylate, 3,4-bis[(meth)acryloyl]tetrahydrofuan, diacrylamide, dimethacrylamide, N,N-di(meth)acryloyl-N-methylamine, N,N-di(meth)acryloyl-N-ethylamine, N,N′

-methylene bis(meth)acrylamide, N,N′

-ethylene bis(meth)acrylamide, N,N′

-dihydroxyethylene bis(meth)acrylamide, N,N′

-propylene bis(meth)acrylamide, N,N′

-2-hydroxypropylene bis(meth)acrylamide, N,N′

-2,3-dihydroxybutylene bis(meth)acrylamide, 1,3-bis(meth)acrylamidepropane-2-yl dihydrogen phosphate, piperazine diacrylamide, vinyl methacrylate, allylmethacrylate, allylacrylate, N-allyl-methacrylamide, N-allyl-acrylamide, tetraethyleneglycol divinyl ether, triethyleneglycol divinyl ether, diethyleneglycol divinyl ether, ethyleneglycol divinyl ether, triallyl isocyanurate, triallyl cyanurate, trimethylopropane trimethacrylate, pentaerythritol tetramethacrylate, bisphenol A dimethacrylate, and combinations thereof.

19. The method according to claim 18, wherein the siloxane-containing vinylic monomer is selected from the group consisting of 3-(meth)acryloxy-2-hydroxypropyloxy) propylbis(trimethylsiloxy)methylsilane, 3-(meth)acryloxyethoxypropyloxypropylbis(trimethylsiloxy)methylsilane, 3-(meth)acrylamidopropyl-bis(trimethylsiloxy)methylsilane, 3-N-methyl (meth)acrylamidopropylbis(trimethylsiloxy) methylsilane, mono-(meth)acryloxy-terminated polydimethylsiloxanes of various molecular weight, mono-(meth)acrylamido-terminated polydimethylsiloxanes of various molecular weight, and combinations thereof.

20. The method according to claim 18, wherein the step of curing is carried out thermally.