Method and apparatus for manufacturing sustainable products with a blown, foam structure

• US 10,442,121 B2
• Filed: 03/11/2013
• Issued: 10/15/2019
• Est. Priority Date: 03/12/2012
• Status: Active Grant

• Current Assignee: Paperfoam B.V.
• Original Assignee: Paperfoam B.V.
• Inventors: Huisman, Jan Wietze, Zandstra, Nynke Margaretha, Arentsen, Johan Hendrik Adolf, Geerts, Hugo Mark
• Primary Examiner(s): Khare, Atul P.
• Application Number:
  US14/383,184
• Publication Number:
  US 20150054190A1
• Time in Patent Office: 2,409 Days
• Field of Search: 264 50, 264 51
• CPC Class Codes: B29C 44/08 using several expanding or moulding steps
• CPC Class Codes: B29C 44/3403 Foaming under special conditions, e.g. in sub-atmospheric pressure, in or on a liquid
• CPC Class Codes: B29C 44/3415 Heating or cooling
• CPC Class Codes: B29C 44/3442 Mixing, kneading or conveying the foamable material mixing plastics B29B7/00; mixing in general B01F
• CPC Class Codes: B29C 44/348 by regulating the temperature and/or the pressure, e.g. suppression of foaming until the pressure is rapidly decreased
• CPC Class Codes: B29C 44/3496 The foam being compressed and later released to expand B29C44/3465 takes precedence
• CPC Class Codes: B29C 44/462 provided with pre-foaming devices
• CPC Class Codes: B29C 45/1701 using a particular environment during moulding, e.g. moisture-free or dust-free
• CPC Class Codes: B29K 2003/00 Use of starch or derivatives as moulding material
• CPC Class Codes: B29L 2031/772 Articles characterised by their shape and not otherwise provided for closed loop B29L2031/709; ring-like B29L2031/7096; corrugated B29L2016/00, flat B29L2007/00; hollow B29L2022/00; screw-threaded B29L2001/00; toothed B29L2031/775; corrugated tubes B29L2023/18
• CPC Class Codes: C08L 1/02 Cellulose; Modified cellulose
• CPC Class Codes: C08L 3/02 Starch; Degradation products thereof, e.g. dextrin
• CPC Class Codes: C08L 5/00 Compositions of polysaccharides or of their derivatives not provided for in groups C08L1/00 or C08L3/00

Abstract

A method for manufacturing sustainable products with a blown, foam structure, wherein a mass comprising at least natural polymers such as starch is passed under pressure into a mold cavity (4) or through a mold die, and the mass is heated in the mold in a manner such as to stabilize the foamed structure to form the product, wherein the method comprises prefoaming of the mass prior to injection in the mold. Preferably, the prefoamed mass is kept under pressure until insertion in the mold. The invention further relates to an apparatus to be used in said method.

Claims

1. A method for manufacturing a sustainable product with a blown, foam structure, the method comprising:

prefoaming a liquid batter comprising water and at least one natural polymer to form a pressurized, prefoamed liquid batter, wherein said prefoaming is conducted by introducing an amount of pressurized gas into the liquid batter while pressure is applied to the liquid batter to form gas bubbles in said pressurized liquid batter;

conveying the pressurized, prefoamed liquid batter toward a cavity of a mold;

passing the pressurized prefoamed liquid batter into the cavity of the mold, wherein the pressurized, prefoamed liquid batter is depressurized upon said passing; and

heating the prefoamed liquid batter in the mold to stabilize the prefoamed liquid batter and form the blown, foam structure,

wherein the pressurized, prefoamed liquid batter remains pressurized between said prefoaming and conveying steps and until said passing into the cavity of the mold.

2. The method according to claim 1, wherein a pressure inside the mold cavity is lower than the pressure of the pressurized, prefoamed liquid batter before said passing into the mold cavity.

3. The method according to claim. 1, wherein after said prefoaming, the pressurized, prefoamed liquid batter has a lower density than the liquid batter.

4. The method according to claim 1, wherein the liquid batter is in the form of a suspension or solution of the water and the at least one natural polymer.

5. The method according to claim 1, wherein a ratio of the volume of the pressurized liquid batter with respect to the volume of the prefoamed liquid batter is approximately between 1:

1.6 and 1;

1.2.

6. The method according to claim 1, wherein the pressure of the liquid batter during said prefoaming is approximately between 3×

10⁵ N/m² (3 bar) and 6×

10⁵ N/m² (6 bar).

7. The method according to claim 1, wherein the density of the prefoamed liquid batter is approximately 200-400 grams/liter, measured at atmospheric pressure (1.01×

105 N/m2 (1.01 bar)).

8. The method according to claim 1, wherein the pressure of the pressurized, prefoamed liquid batter between said prefoaming and conveying steps and until said passing into the cavity of the mold is approximately 5×

10⁵ N/m² (5 bar).

9. The method according to claim 8, wherein the prefoamed liquid batter has a density of approximately 700-800 grams/liter at said pressure of approximately 5×

10⁵ N/m² (5 bar).

10. The method according to claim 1, wherein the pressure of the pressurized, prefoamed liquid batter during said conveying, is approximately between 2×

10⁵ N/m² (2 bar) and 4×

10⁵ N/m² (4 bar).

11. The method according to claim 1, wherein the mold is an injection mold.

12. The method according to claim 1, wherein the mold is heated to a baking temperature prior to said passing of the pressurized, prefoamed liquid batter into the mold, and wherein the baking temperature is approximately 180°

C.-240°

C.

13. The method according to claim 1, wherein the liquid batter comprises a blowing agent and at least 10% of weight of said water.

14. The method according to claim 1, wherein the method further comprises inserting one or more additives to the liquid batter during or after said prefoaming.

15. The method according to claim 14, wherein the one or more additives comprises at least one of a cross linker, stabilizer, foaming agent, and colouring agent.

16. The method according to claim 1, wherein the at least one natural polymer comprises starch.

17. The method according to claim 1, wherein the introduced gas is oxygen, nitrogen, or carbon dioxide.

18. The method according to claim 1, wherein the pressure of the liquid batter during said prefoaming is approximately 5×

10⁵ N/m² (5 bar).

19. The method according to claim 1, wherein the pressure of the pressurized, prefoamed liquid batter during said passing is approximately 3×

10⁵ N/m² (3 bar).

20. The method according to claim 1, wherein the mold is heated to a baking temperature prior to said passing of the pressurized, prefoamed liquid batter into the mold, wherein the baking temperature is approximately 180°

C.-225°

C.

21. The method according to claim 1, wherein said passing results in the gas bubbles expanding in the cavity of the mold before said heating, thereby forming a foamed mass from the prefoamed liquid hatter to which said heating is subjected.

22. The method according to claim 1, wherein said prefoaming is conducted by a mixer of a prefoaming means.