Carbon nitride membrane composite material modified by black phosphorus/ metal organic framework, and preparation method thereof and application in waste gas treatment

• US 10,518,252 B1
• Filed: 06/13/2019
• Issued: 12/31/2019
• Est. Priority Date: 06/14/2018
• Status: Active Grant

• Current Assignee: Soochow University (Jiangsu Education Department)
• Original Assignee: Soochow University (Jiangsu Education Department)
• Inventors: Lu, Jianmei, Chen, Dongyun
• Primary Examiner(s): Vanoy, Timothy C
• Application Number:
  US16/440,163
• Publication Number:
  US 20190381487A1
• Time in Patent Office: 201 Days
• CPC Class Codes: B01D 2255/702 Carbon
• CPC Class Codes: B01D 2255/707 Additives or dopants
• CPC Class Codes: B01D 2255/802 Photocatalytic
• CPC Class Codes: B01D 2257/404 Nitrogen oxides other than dinitrogen oxide
• CPC Class Codes: B01D 53/8628 Processes characterised by a specific catalyst
• CPC Class Codes: B01J 23/72 Copper
• CPC Class Codes: B01J 2531/16 Copper
• CPC Class Codes: B01J 27/14 Phosphorus; Compounds thereof
• CPC Class Codes: B01J 27/24 Nitrogen compounds
• CPC Class Codes: B01J 31/1616 Coordination complexes, e.g. organometallic complexes, immobilised on an inorganic support, e.g. ship-in-a-bottle type catalysts catalysts comprising molecular sieves B01J29/00
• CPC Class Codes: B01J 31/1691 Coordination polymers, e.g. metal-organic frameworks [MOF] preparation of metal complexes containing carboxylic acid moieties C07C51/418; MOF's per se C07F
• CPC Class Codes: B01J 31/2213 At least two complexing oxygen atoms present in an at least bidentate or bridging ligand
• CPC Class Codes: B01J 31/2239 Bridging ligands, e.g. OAc in Cr2(OAc)4, Pt4(OAc)8 or dicarboxylate ligands
• CPC Class Codes: B01J 35/33 Electric or magnetic properties
• CPC Class Codes: B01J 35/39 Photocatalytic properties
• CPC Class Codes: B01J 35/59 Membranes
• CPC Class Codes: B01J 37/0209 involving a reaction between the support and a fluid
• CPC Class Codes: B01J 37/082 Decomposition and pyrolysis

Abstract

A carbon nitride membrane composite material modified by black phosphorus/metal organic framework (MOF) and a preparation method and application thereof to waste gas treatment are disclosed. First, taking urea as a raw material to calcine at a high temperature and prepare porous carbon nitride nanosheet; then carrying out surface carboxylation on the porous carbon nitride nanosheet, and modifying metal organic framework (MOF) on the surface of the porous carbon nitride through a layer-by-layer self-assembling method; stripping block black phosphorus materials into a two-dimensional black phosphorus slice by solvent exfoliation method; mixing the MOF-modified porous carbon nitride material with the two-dimensional black phosphorus material, carrying out suction filtration on the mixture under a vacuum pump to obtain the black phosphorus/MOF-modified carbon nitride membrane composite material.

Claims

1. A preparation method of a carbon nitride membrane composite material modified by black phosphorus/metal organic framework, characterized in comprising the following steps:

(1) using urea as a raw material, calcining to prepare porous carbon nitride nanosheet;

(2) carrying out carboxylation on the porous carbon nitride nanosheet, and modifying metal organic framework on it to obtain porous carbon nitride material modified by metal organic framework;

(3) stripping block black phosphorus into a two-dimensional black phosphorus slice by solvent exfoliation method;

(4) dispersing the porous carbon nitride material modified by metal organic framework and the two-dimensional black phosphorus slice in an organic solvent, stirring at room temperature and suction filtrating to obtain the carbon nitride membrane composite material modified by black phosphorus/metal organic framework.

2. The method according to claim 1, wherein in the step (1), the calcination condition is, calcining at 300 to 500°

C. for 3 to 5 hours under air;

the rate of temperature rise is 2 to 15°

C. per minute.

3. The method according to claim 1, wherein in the step (2), at a mass ratio of 1:

(10 to

     20), mixing the porous carbon nitride nanosheet and succinic anhydride in a solvent, carrying out reaction at room temperature for 10-15 hours to complete the carboxylation of the porous carbon nitride nanosheet;

immersing the carboxylated porous carbon nitride nanosheet sequentially in a copper nitrate solution and a trimesic acid solution to complete the modification of metal organic framework;

the mass ratio of the carboxylated porous carbon nitride nanosheet, copper nitrate and trimesic acid is 1;

(2˜

3);

(1˜

2), and the time of immersing in the copper nitrate solution and the trimesic acid solution is respectively 10 to 20 minutes and 25 to 40 minutes.

4. The method according to claim 1, wherein in the step (3), the mass ratio of block black phosphorus and solvent is 1:

(100 to

     150);

performing ultrasonic peeling using a cell pulverizer, and the peeling time is 4 to 8 hours;

the solvent is N-methylpyrrolidone.

5. The method according to claim 1, wherein in the step (4), the mass ratio of the porous carbon nitride material modified by metal organic framework and the two-dimensional black phosphorus slice is 100:

(2 to

     10), stirring at room temperature for 6 to 8 hours, and finally filtrating in to a membrane;

said organic solvent is N-methylpyrrolidone.

14. A carbon nitride membrane composite material modified by black phosphorus/metal organic framework prepared by the preparation method according to claim 1.

15. The application of the carbon nitride membrane composite material modified by black phosphorus/metal organic framework according to claim 14 in the exhaust gas photocatalytic treatment.

6. A preparation method of a porous carbon nitride material modified by metal organic framework, characterized in comprising the following steps:

(1) using urea as a raw material, calcining to prepare porous carbon nitride nanosheet;

(2) carrying out carboxylation on the porous carbon nitride nanosheet, and modifying metal organic framework on it to obtain porous carbon nitride material modified by metal organic framework.

7. The method according to claim 6, wherein in the step (1), the calcination condition is, calcining at 300 to 500°

C. for 3 to 5 hours under air;

the rate of temperature rise is 2 to 15°

C. per minute.

8. The method according to claim 6, wherein in the step (2), at a mass ratio of 1:

(10 to

     20), mixing the porous carbon nitride nanosheet and succinic anhydride in a solvent, carrying out reaction at room temperature for 10-15 hours to complete the carboxylation of the porous carbon nitride nanosheet;

immersing the carboxylated porous carbon nitride nanosheet sequentially in a copper nitrate solution and a trimesic acid solution to complete the modification of metal organic framework;

the mass ratio of the carboxylated porous carbon nitride nanosheet, copper nitrate and trimesic acid is 1;

(2˜

3);

(1˜

2), and the time of immersing in the copper nitrate solution and the trimesic acid solution is respectively 10 to 20 minutes and 25 to 40 minutes.

16. A porous carbon nitride material modified by metal organic framework prepared by the preparation method according to claim 6.

17. The application of the porous carbon nitride material modified by metal organic framework according to claim 16 in the exhaust gas photocatalytic treatment.

9. A method of treating exhaust gas, characterized in comprising the following steps:

(1) using urea as a raw material, calcining to prepare porous carbon nitride nanosheet;

(2) carrying out carboxylation on the porous carbon nitride nanosheet, and modifying metal organic framework on it to obtain porous carbon nitride material modified by metal organic framework;

(3) stripping block black phosphorus into a two-dimensional black phosphorus slice by solvent exfoliation method;

(4) dispersing the porous carbon nitride material modified by metal organic framework and the two-dimensional black phosphorus slice in an organic solvent, stirring at room temperature and suction filtrating to obtain the carbon nitride membrane composite material modified by black phosphorus/metal organic framework;

(5) under illumination, passing the exhaust gas through the carbon nitride membrane composite material modified by black phosphorus/metal organic framework to carry out the gas treatment.

10. The method according to claim 9, wherein in the step (1), the calcination condition is, calcining at 300 to 500°

C. for 3 to 5 hours under air;

the rate of temperature rise is 2 to 15°

C. per minute.

11. The method according to claim 9, wherein in the step (2), at a mass ratio of 1:

(10 to

     20), mixing the porous carbon nitride nanosheet and succinic anhydride in a solvent, carrying out reaction at room temperature for 10-15 hours to complete the carboxylation of the porous carbon nitride nanosheet;

immersing the carboxylated porous carbon nitride nanosheet sequentially in a copper nitrate solution and a trimesic acid solution to complete the modification of metal organic framework;

the mass ratio of the carboxylated porous carbon nitride nanosheet, copper nitrate and trimesic acid is 1;

(2˜

3);

(1˜

2), and the time of immersing in the copper nitrate solution and the trimesic acid solution is respectively 10 to 20 minutes and 25 to 40 minutes.

12. The method according to claim 9, wherein in the step (3), the mass ratio of block black phosphorus and solvent is 1:

(100 to

     150);

performing ultrasonic peeling using a cell pulverizer, and the peeling time is 4 to 8 hours;

the solvent is N-methylpyrrolidone.

13. The method according to claim 9, wherein in the step (4), the mass ratio of the porous carbon nitride material modified by metal organic framework and the two-dimensional black phosphorus slice is 100:

(2 to

     10), stirring at room temperature for 6 to 8 hours, and finally filtrating in to a membrane;

said organic solvent is N-methylpyrrolidone.