Dual cure coating composition and process for using the same

• US 20030077394A1
• Filed: 08/28/2001
• Published: 04/24/2003
• Est. Priority Date: 08/28/2001
• Status: Abandoned Application

• Current Assignee: BASF Corporation (BASF SE)
• Original Assignee: BASF Corporation (BASF SE)
• Inventors: Caillouette, Lyle, OʼDonnell, Ryan F., Bradford, Christophen J., Zimmer, Marcy, Rischke, Jennifer A.
• Application Number:
  US09/941,295
• Publication Number:
  US 20030077394A1
• Time in Patent Office: Days
• US Class Current: 427/407.1
• CPC Class Codes: B05D 3/0209 Multistage baking
• CPC Class Codes: B05D 3/0254 After-treatment
• CPC Class Codes: B05D 3/067 Curing or cross-linking the coating
• CPC Class Codes: B05D 7/02 to macromolecular substances, e.g. rubber treatment or coating of shaped articles made of macromolecular substances C08J7/00
• CPC Class Codes: B05D 7/53 Base coat plus clear coat type
• CPC Class Codes: B05D 7/54 No clear coat specified
• CPC Class Codes: C08J 3/243 Two or more independent types of crosslinking for one or more polymers
• CPC Class Codes: C08L 2666/18 Polyesters or polycarbonates according to C08L67/00 - C08L69/00; Derivatives thereof
• CPC Class Codes: C09D 175/16 having terminal carbon-to-carbon unsaturated bonds

Abstract

The dual cure coating composition requires both radiation and heat energy to cure and comprises a radiation curable component (a1), a thermally curable binder component (a2), and a thermally curable crosslinking component (a3). Radiation curable component (a1) is polymerizable upon exposure to radiation and comprises at least two functional groups (a11) comprising at least one bond activatable with radiation. Thermally curable binder component (a2) is polymerizable upon exposure to heat, and comprises (a21) at least two functional groups which are reactive with functional groups (a31), and a polydispersity of less than 4.0. Thermally curable crosslinking component (a3) comprises functional groups (a31) which are reactive with functional groups (a21). The invention further comprises methods of making coated surfaces that have both optimum porosity sealing and adhesion.

Claims

1. A coating composition curable upon exposure to both UV radiation and thermal energy, the composition comprising

(a1) a radiation curable component which polymerizes upon exposure to UV radiation, comprising

(a11) at least two functional groups comprising at least one bond activatable upon exposure to IN radiation,

(a2) a thermally curable binder component which polymerizes upon exposure to heat, comprising

(a21) at least two functional groups reactive with the functional groups (a31) of component (a3), and

(a22) a polydispersity of less than 4.0, and

(a3) a thermally curable crosslinking component comprising

(a31) two or more functional groups reactive with functional groups (a21).

2. The coating composition of claim 1 wherein the thermally curable component (a2) has a polydispersity of less than 3.5.

3. The coating composition of claim 2 wherein the thermally curable component (a2) has a polydispersity of from 1.5 to less than 3.5.

4. The coating composition of claim 3 wherein the thermally curable component (a2) has a polydispersity of from 1.75 to less than 3.0.

5. The coating composition of claim 1 wherein thermally curable crosslinking component (a3) comprises at least 2.0 isocyanate groups (a31) per molecule.

6. The coating composition of claim 1 wherein thermally curable binder component (a2) comprises at least two isocyanate-reactive groups (a21).

7. The coating composition of claim 1 wherein the thermally curable component (a2) has at least two isocyanate reactive groups (a21) per molecule and is selected from the group consisting of polyesters, epoxy functional materials, acrylics, and mixtures thereof.

8. The coating composition of claim 6 wherein isocyanate-reactive functional groups (a12) and (a21) are hydroxyl groups.

9. The coating composition of claim 7 wherein thermally curable component (a2) is a polyester.

10. The coating composition of claim 9 wherein isocyanate-reactive functional groups (a12) and (a21) are hydroxyl groups.

11. The coating composition of claim 1 wherein the ratio of NCO groups to the sum of functional groups (a12) and (a21) is less than 1.30.

12. The coating composition of claim 11 wherein the ratio of NCO groups to the sum of isocyanate-reactive functional groups (a12) and (a21) is from 0.50 to 1.25.

13. The coating composition of claim 12 wherein the ratio of NCO groups to the sum of isocyanate-reactive functional groups (a12) and (a21) is from 0.75 to 1.10.

14. The coating composition of claim 13 wherein the ratio of NCO groups to the sum of isocyanate-reactive functional groups (a12) and (a21) is less than 1.00.

15. The coating composition of claim 14 wherein the ratio of NCO groups to the sum of isocyanate-reactive functional groups (a12) and (a21) is from 0.75 to 1.00.

16. The coating composition of claim 1 wherein thermally curable binder component (a2) comprises less than 5% by weight of aromatic ring moieties, based on the nonvolatile weight of thermally curable binder component (a2)

17. The coating composition of claim 16, wherein thermally curable binder component (a2) has no more than 2% by weight of aromatic ring moieties, based on the nonvolatile weight of thermally curable binder component (a2).

18. The coating composition of claim 17 wherein thermally curable binder component (a2) has between 0 to less than 2% by weight of aromatic ring moieties, based on the nonvolatile weight of thermally curable binder component (a2).

19. The coating composition of claim 1 wherein radiation curable component (a1) further comprises (a12) one or more isocyanate-reactive functional groups.

20. A method of making a coated substrate, comprising applying the coating composition of claim 1 to a substrate to provide a coated substrate.

21. The method of claim 20 further comprising subjecting the coated substrate to UV radiation to provide a UV cured coated substrate.

22. The method of claim 21 further comprising subjecting the UV cured coated substrate to heat to provide a UV and thermally cured coated substrate.

23. The method of claim 1 wherein the substrate comprises a plastic.

24. The method of claim 23 wherein the plastic substrate is a fiber-reinforced plastic substrate.

25. The method of claim 23 wherein the plastic substrate is SMC or BMC.

26. The method of claim 22 wherein the UV and thermally cured coated substrate is coated with one or more coating compositions to provide a coated UV and thermally cured coated substrate.

27. The method of claim 26 wherein the UV and thermally cured coated substrate is coated with at least one basecoat coating composition.

28. The method of claim 26 wherein the UV and thermally cured coated substrate is coated with at least one clearcoat coating composition.

29. The method of claim 26 wherein the coated UV and thermally cured coated substrate is substantially free of surface defects resulting from vaporous substrate emissions.

30. A coated substrate made by the method of claim 20.