Process for making an abrasion resistant coating onto an organic glass substrate
First Claim
1. A process for making an abrasion-resistant coating onto at least one surface of a substrate made of an organic glass which comprises:
- (a) preparing a polymerizable composition containing a component A comprising at least one silane compound containing at least one epoxy group and at least two alkoxy groups directly bonded to the Si atom of the molecule or a hydrolysate thereof and a component B comprising fine particles of silica, an effective amount of at least one cationic photopolymerization initiator and an effective amount of at least one thermal polymerization catalyst;
(b) coating at least one surface of the substrate with the composition resulting from step (a);
(c) submitting the coated substrate to a photopolymerization step for pre-curing the coating layer; and
thereafter;
(d) submitting the substrate with the pre-cured coating layer thereon to a thermal curing at a predetermined temperature and for a predetermined time to complete curing of the coating layer.
0 Assignments
0 Petitions
Accused Products
Abstract
The process comprises, (a) adding to a polymerizable composition containing a component A comprising at least one silane compound containing at least one epoxy group and at least two alkoxy groups directly bonded to the Si atom of the molecule or hydrolysate thereof and a component B comprising fine particles of silica, an effective amount of at least one cationic photopolymerization initiator and an effective amount of at least one thermal polymerization catalyst, (b) coating at least one surface of the substrate with the composition resulting from step (a), (c) submitting the coated substrate to a photopolymerization step for pre-curing the coating layer; and thereafter, (d) submitting the substrate with the pre-cured coating layer thereon to a thermal curing at a predetermined temperature and for a predetermined time to complete curing of the coating layer.
9 Citations
20 Claims
-
1. A process for making an abrasion-resistant coating onto at least one surface of a substrate made of an organic glass which comprises:
-
(a) preparing a polymerizable composition containing a component A comprising at least one silane compound containing at least one epoxy group and at least two alkoxy groups directly bonded to the Si atom of the molecule or a hydrolysate thereof and a component B comprising fine particles of silica, an effective amount of at least one cationic photopolymerization initiator and an effective amount of at least one thermal polymerization catalyst;
(b) coating at least one surface of the substrate with the composition resulting from step (a);
(c) submitting the coated substrate to a photopolymerization step for pre-curing the coating layer; and
thereafter;
(d) submitting the substrate with the pre-cured coating layer thereon to a thermal curing at a predetermined temperature and for a predetermined time to complete curing of the coating layer. - View Dependent Claims (2, 3, 4, 5, 6, 7, 8, 9, 10, 11, 12, 13, 14)
-
-
15. An abrasion-resistant coating composition which comprises:
-
a component A comprising at least one silane compound containing at least one epoxy group and at least two alkoxy groups directly bonded to the Si atom of the molecule or a hydrolysate thereof;
a component B comprising fine particles of silica;
an effective amount of at least one cationic photopolymerization initiator; and
an effective amount of at least one thermal polymerizsation catalyst. - View Dependent Claims (16, 17, 18, 19, 20)
-
Specification