FLAME RETARDANT POLYURETHANES AND POLYISOCYANURATES, AND ADDITIVES THEREFOR

• US 20030153656A1
• Filed: 01/11/2002
• Published: 08/14/2003
• Est. Priority Date: 01/11/2002
• Status: Abandoned Application

• Current Assignee: Rinus Sjerps
• Original Assignee: Rinus Sjerps
• Inventors: Sjerps, Rinus
• Application Number:
  US10/044,775
• Publication Number:
  US 20030153656A1
• Time in Patent Office: Days
• US Class Current: 524/115
• CPC Class Codes: C08G 18/381 having bromine atoms
• CPC Class Codes: C08G 18/4607 having halogens
• CPC Class Codes: C08G 18/4883 containing cyclic groups having at least one oxygen atom in the ring
• CPC Class Codes: C08G 18/6611 having at least three hydroxy groups
• CPC Class Codes: C08G 2110/0025 rigid
• CPC Class Codes: C08G 2110/005 < 50kg/m3
• CPC Class Codes: C08K 5/00 Use of organic ingredients
• CPC Class Codes: C08K 5/136 Phenols containing halogens
• CPC Class Codes: C08K 5/51 Phosphorus bound to oxygen
• CPC Class Codes: C08L 75/04 Polyurethanes
• CPC Class Codes: C09K 21/12 containing phosphorus
• CPC Class Codes: C09K 21/14 Macromolecular materials

Abstract

A free-flowing, stable liquid flame retardant mixture comprised of or formed by mixing together components comprised of: A) tetrabromobisphenol-A; B) at least one liquid ester of a pentavalent acid of phosphorus; and C) at least one additional organic halogen-containing reactive flame retardant where the halogen is chlorine or bromine or both. Such mixtures can be effectively used in the preparation of flame-retardant polyurethanes including rigid polyurethane foams. It is preferable to include one or more liquid esters of a pentavalent acid of phosphorus in the liquid flame retardant mixture. C) is preferably at least one diester/diol of tetrabromophthalic anhydride, especially a mixed ester of tetrabromophthalic anhydride with diethylene glycol and propylene glycol, which by itself is a relatively viscous substance.

Claims

1. A free-flowing non-viscous liquid flame retardant composition comprised of or formed by mixing together components comprised of:

A) tetrabromobisphenol-A;

B) at least one liquid ester of a pentavalent acid of phosphorus; and

C) at least one additional organic halogen-containing reactive flame retardant where the halogen is chlorine or bromine or both;

in proportions such that the composition has a Brookfield viscosity at 25°

C. of about 5000 centipoises (cP) or less.

2. A composition of claim 1 wherein B) is at least one tri(chloroalkyl) phosphate.

3. A composition of claim 1 wherein B) is a tris(2-chloropropyl)phosphate.

4. A composition of claim 1 wherein B) is a tris(2-chloropropyl)phosphate and a liquid dialkylalkanephosphonate.

5. A composition of claim 1 wherein B) is a tris(2-chloropropyl)phosphate and a liquid trialkylphosphate.

6. A composition of claim 1 wherein C) is at least one organic bromine-containing reactive flame retardant.

7. A composition of claim 6 wherein B) is at least one organic phosphate ester and/or at least one organic phosphonate ester.

8. A composition of claim 6 wherein B) is at least one alkyl or chloroalkyl phosphate ester and/or at least one dialkylalkane phosphonate ester.

9. A composition of claim 1 wherein C) is at least one diester/diol of tetrabromophthalic anhydride.

10. A composition of claim 1 wherein C) a mixed ester of tetrabromophthalic anhydride with diethylene glycol and propylene glycol.

11. A composition of claim 9 wherein B) is at least one organic phosphate ester and/or at least one organic phosphonate ester.

12. A composition of claim 9 wherein B) is at least one alkyl or chloroalkyl phosphate ester and/or at least one dialkylalkane phosphonate ester.

13. A composition of claim 9 wherein B) is a tris(2-chloropropylphosphate or diethylethanephosphonate, or both.

14. A composition of claim 9 wherein B) is (i) a tris(2-chloropropylphosphate, (ii) a tris(2-chloropropylphosphate and diethylethanephosphonate, or (iii) a tris(2-chloropropylphosphate and triethylphosphate.

29. A flame-retardant composition which comprises a polyurethane or polyisocyanurate polymer formed from components comprised of:

a) at least one organic polyisocyanate;

b) at least one isocyanate-reactive compound;

c) a flame retardant amount of a free-flowing non-viscous liquid flame retardant composition as claimed in any of claims 1-27.

40. A process of preparing a rigid polyurethane foam or polyisocyanurate foam, which process comprises polymerizing at least one organic polyisocyanate with at least one isocyanate-reactive compound in the presence of components comprised of or formed from components comprised of at least one polymerization catalyst, at least one blowing agent and a flame retardant amount of a free-flowing non-viscous liquid flame retardant composition as claimed in any of claims 1-28.

15. A free-flowing non-viscous liquid flame retardant composition comprised of or formed by mixing together components comprised of:

A) about 15 to about 55 wt % of tetrabromobisphenol-A;

B) about 15 to about 75 wt % of at least one liquid alkyl or chloroalkyl phosphate or at least one liquid alkyl phosphonate ester, or mixture of any two or more of these;

C) about 5 to about 45 wt % of at least one diester/diol of tetrabromophthalic anhydride;

and optionally

D) at least one phenolic antioxidant;

wherein the percentages of A), B) and C) are based on the total weight of only components A), B) and C).

16. A composition of claim 15 wherein C) is a mixed ester of tetrabromophthalic anhydride with diethylene glycol and propylene glycol.

17. A composition of claim 15 wherein B) is a tris(2-chloropropylphosphate or diethylethanephosphonate, or both.

18. A composition of claim 15 wherein B) is (i) a tris(2-chloropropylphosphate, (ii) a tris(2-chloropropylphosphate and diethylethanephosphonate, or (iii) a tris(2-chloropropylphosphate and triethylphosphate.

19. A composition of claim 15 wherein said flame retardant composition comprised of or formed by mixing together components comprised of A), B), C) and D) thereof, and wherein D) is octadecyl 3,5-di-tert-butyl-4-hydroxyhydrocinnamate.

20. A free-flowing non-viscous liquid flame retardant composition comprised of or formed by mixing together components comprised of:

A) about 20 to about 40 wt % of tetrabromobisphenol-A;

B) about 20 to about 70 wt % of at least one liquid alkyl or chloroalkyl phosphate or at least one liquid alkyl phosphonate ester, or mixture of any two or more of these;

C) about 10 to about 40 wt % of at least one diester/diol of tetrabromophthalic anhydride; and

optionally

D) at least one phenolic antioxidant;

wherein the percentages of A), B) and C) are based on the total weight of only components A), B) and C).

21. A composition of claim 20 wherein C) is a mixed ester of tetrabromophthalic anhydride with diethylene glycol and propylene glycol.

22. A composition of claim 20 wherein B) is a tris(2-chloropropylphosphate or diethylethanephosphonate, or both.

23. A composition of claim 20 wherein B) is (i) a tris(2-chloropropylphosphate, (ii) a tris(2-chloropropylphosphate and diethylethanephosphonate, or (iii) a tris(2-chloropropylphosphate and triethylphosphate.

24. A composition of claim 20 wherein said flame retardant composition comprised of or formed by mixing together components comprised of A), B), C) and D) thereof, and wherein D) is octadecyl 3,5-di-tert-butyl-4-hydroxyhydrocinnamate.

25. A free-flowing non-viscous liquid flame retardant composition comprised of or formed by mixing together components comprised of:

A) about 35 to about 40 wt % of tetrabromobisphenol-A;

B) about 50 wt % of a tris(2-chloropropyl)phosphate;

C) about 10 to about 15 wt % of a mixed ester of tetrabromophthalic anhydride with diethylene glycol and propylene glycol; and

D) optionally up to about 2000 ppm (wt/wt) of at least one phenolic antioxidant;

wherein the total wt % of A), B), and C) adds up to 100 wt %.

26. A composition of claim 25 wherein said composition is comprised of about 35 wt % of A), about 50 wt % of B), and about 15 wt % of C).

27. A free-flowing non-viscous liquid flame retardant composition comprised of or formed by mixing together components comprised of:

A) about 50 wt % of tetrabromobisphenol-A;

B) about 20 wt % of a tris(2-chloropropyl)phosphate;

C) about 20 wt % of diethylethanephosphonate;

D) about 10 wt % of a mixed ester of tetrabromophthalic anhydride with diethylene glycol and propylene glycol; and

E) optionally up to about 2000 ppm (wt/wt) of at least one phenolic antioxidant.

28. A free-flowing non-viscous liquid flame retardant composition comprised of or formed by mixing together components comprised of:

A) about 35 wt % of tetrabromobisphenol-A;

B) about 35 wt % of a tris(2-chloropropyl)phosphate;

C) about 5 wt % of triethylphosphate;

D) about 25 wt % of a mixed ester of tetrabromophthalic anhydride with diethylene glycol and propylene glycol; and

E) optionally up to about 2000 ppm (wt/wt) of at least one phenolic antioxidant.

30. A flame-retardant composition which comprises a polyurethane or polyisocyanurate polymer formed in the presence of flame retardant components comprised of:

1) about 15 to about 55 wt % of tetrabromobisphenol-A;

2) about 15 to about 75 wt % of at least one liquid alkyl or chloroalkyl phosphate or at least one liquid alkyl phosphonate ester, or mixture of any two or more of these;

3) about 5 to about 45 wt % of at least one diester/diol of tetrabromophthalic anhydride; and

optionally

4) at least one phenolic antioxidant;

wherein the percentages of

     1),

     2) and

     3) are based on the total weight of only components

     1),

     2) and

     3).

31. A composition of claim 30 wherein C) is a mixed ester of tetrabromophthalic anhydride with diethylene glycol and propylene glycol.

32. A composition of claim 30 wherein said polymer is formed from components comprised of 1), 2), 3), and 4) thereof.

33. A composition of claim 32 wherein component 4) is octadecyl 3,5-di-tert-butyl-4-hydroxyhydrocinnamate.

34. A composition as claimed in any of claims 30-33 wherein B) is (i) a tris(2-chloropropylphosphate, (ii) a tris(2-chloropropylphosphate and diethylethanephosphonate, or (iii) a tris(2-chloropropylphosphate and triethylphosphate.

35. A flame-retardant composition which comprises a polyurethane or polyisocyanurate polymer formed in the presence of flame retardant components comprised of:

1) about 20 to about 40 wt % of tetrabromobisphenol-A;

2) about 20 to about 70 wt % of at least one liquid alkyl or chloroalkyl phosphate or at least one liquid alkyl phosphonate ester, or mixture of any two or more of these;

3) about 10 to about 40 wt % of at least one diester/diol of tetrabromophthalic anhydride; and

optionally

4) at least one phenolic antioxidant;

wherein the percentages of

     1),

     2) and

     3) are based on the total weight of only components

     1),

     2) and

     3).

36. A composition of claim 35 wherein C) is a mixed ester of tetrabromophthalic anhydride with diethylene glycol and propylene glycol.

37. A composition of claim 35 wherein said polymer is formed from components comprised of 1), 2), 3), and 4) thereof.

38. A composition of claim 37 wherein component 4) is octadecyl 3,5-di-tert-butyl-4-hydroxyhydrocinnamate.

39. A composition as claimed in any of claims 35-38 wherein B) is (i) a tris(2-chloropropylphosphate, (ii) a tris(2-chloropropylphosphate and diethylethanephosphonate, or (iii) a tris(2-chloropropylphosphate and triethylphosphate.

41. A process of preparing a rigid polyurethane foam or polyisocyanurate foam, which process comprises polymerizing at least one organic polyisocyanate with at least one isocyanate-reactive compound in the presence of components comprised of or formed from components comprised of at least one polymerization catalyst, at least one blowing agent and flame retardant components comprised of:

1) about 15 to about 55 wt % of tetrabromobisphenol-A;

2) about 15 to about 75 wt % of at least one liquid alkyl or chloroalkyl phosphate or at least one liquid alkyl phosphonate ester, or mixture of any two or more of these;

3) about 5 to about 45 wt % of at least one diester/diol of tetrabromophthalic anhydride;

wherein the percentages of

     1),

     2) and

     3) are based on the total weight of only components

     1),

     2) and

     3), and wherein said flame retardant components

     1),

     2) and

     3) are added to the polymerization mixture individually and/or as one or more preformed mixtures.

42. A process of claim 41 wherein 3) is a mixed ester of tetrabromophthalic anhydride with diethylene glycol and propylene glycol.

43. A process as claimed in any of claims 41-42 wherein 2) is (i) a tris(2-chloropropylphosphate, (ii) a tris(2-chloropropylphosphate and diethylethanephosphonate, or (iii) a tris(2-chloropropylphosphate and triethylphosphate.

44. A process of claim 41 wherein about 20 to about 40 wt % of 1), about 20 to about 70 wt % of 2), and about 10 to about 40 wt % of 3) are used.