Dental mill blanks

• US 20030157357A1
• Filed: 10/31/2002
• Published: 08/21/2003
• Est. Priority Date: 01/08/1999
• Status: Abandoned Application

• Current Assignee: 3M Innovative Properties Company (3M Company)
• Original Assignee: 3M Innovative Properties Company (3M Company)
• Inventors: Carufel, Roger J., Cummings, Kevin M., Rusin, Richard P.
• Application Number:
  US10/285,303
• Publication Number:
  US 20030157357A1
• Time in Patent Office: Days
• US Class Current: 428/542.8
• CPC Class Codes: A61C 13/0022 Blanks or green, unfinished dental restoration parts
• CPC Class Codes: A61K 6/887 Compounds obtained by reactions only involving carbon-to-carbon unsaturated bonds
• CPC Class Codes: A61K 6/891 Compounds obtained otherwise than by reactions only involving carbon-to-carbon unsaturated bonds
• CPC Class Codes: A61K 6/893 Polyurethanes
• CPC Class Codes: C08L 33/00 Compositions of homopolymers or copolymers of compounds having one or more unsaturated aliphatic radicals, each having only one carbon-to-carbon double bond, and only one being terminated by only one carboxyl radical, or of salts, anhydrides, esters, amides, imides or nitriles thereof; Compositions of derivatives of such polymers
• CPC Class Codes: C08L 63/00 Compositions of epoxy resins; Compositions of derivatives of epoxy resins
• CPC Class Codes: C08L 75/16 having terminal carbon-to-carbon unsaturated bonds

Abstract

A dental mill blank comprising a resin and a filler, wherein the blank is fabricated such that it passes a Thermal Shock Test. The mill blank is substantially free of cracks and discontinuities. Further, the blank may have superior cuttability and hardness.

Claims

1. A carvable mill blank for making a dental prosthetic comprising

a) a polymeric resin and

b) a filler,

wherein the blank is substantially free of cracks and fabricated such that the blank passes a Thermal Shock Test.

2. The blank of claim 1 wherein the blank is substantially free of discontinuities in the material that are larger than about 1 millimeter.

3. The blank of claim 1 wherein the blank is substantially free of discontinuities in the material that are larger than about 0.1 millimeter.

4. The blank of claim 1 wherein the blank is substantially free of discontinuities in the material that are larger than about 0.01 millimeter.

5. The blank of claim 1 wherein the blank further comprises a fluoride releasing material.

6. The blank of claim 1 wherein the polymeric resin is made from a material comprising a free radically curable monomer, oligomer or polymer.

7. The blank of claim 1 wherein the polymeric resin is made from a material comprising a cationically curable monomer, oligomer or polymer.

8. The blank of claim 1 wherein the polymeric resin is made from a material comprising a free radically curable monomer, oligomer or polymer and cationically curable monomer, oligomer or polymer.

9. The blank of claim 6 wherein the material is selected from the group consisting of 2,2-bis[4-(2-hydroxy-3-methacryloyloxypropoxy)phenyl]propane (bisGMA), triethyleneglycol dimethacrylate (TEGDMA), 2,2-bis[4-(2-methacryloyloxyethoxy)-phenyl]propane (bisEMA), 2-hydroxy ethyl methacrylate (HEMA), urethane dimethacrylate (UDMA) and any combinations thereof.

10. The blank of claim 7 wherein the material is selected from the group consisting of diglycidyl ether of bisphenol A, 3,4-epoxycyclohexylmethyl-3-4-epoxy cyclohexene carboxylate, bisphenol F epoxides, and polytetrahydrofuran.

11. The blank of claim 1 wherein the resin is made from a material comprising a monomer, oligomer or polymer comprising both a free radically curable functionality and a cationically curable functionality.

12. The blank of claim 1 wherein the filler is selected from the group consisting of barium glass, quartz and zirconia silica.

13. The blank of claim 1 wherein the filler is derived from a sol-gel process.

14. The blank of claim 1 wherein the blank is capable of being further hardened after or during milling by a curing process.

16. A method of making the dental mill blank of claim 1 comprising the steps of

a) mixing a paste comprising a resin and a filler,

b) shaping the paste into a desired configuration,

c) minimizing material discontinuities from the paste

d) curing the paste into a blank, and

e) relieving internal stresses in the blank.

17. The method in claim 16 wherein shaping the paste is performed using a mold and further comprising the steps of

f) trimming excess paste material from the mold, and

g) removing the cured paste from the mold.

18. The method in claim 16 further comprising the step of

f) mounting a handle to the cured paste.

19. The method in claim 16 wherein the curing system is selected from the group consisting of heat, light, microwave, e-beam and chemical cure.

20. The method in claim 16 wherein the stress relieving step comprises slowly heating the cured paste in an oven temperature of at or above Tg of the resin.

21. A method of making the dental mill blank of claim 1 comprising the steps of

a) mixing a paste comprising a resin and a filler,

b) shaping the paste into a desired configuration,

c) minimizing material discontinuities from the paste

d) slow curing the paste on a light box for a sufficient time to effectuate low stress cure, such that the cured paste passes a Thermal Shock Test.

28. The mill blank in claim 1 wherein the wherein the mill blank has a Barcol Hardness value greater than about 0% of the Barcol Hardness of a Standard Fumed Silica Mill Blank, and a Cuttability value greater than about 30% of the Cuttability value of a Standard Fumed Silica Mill Blank.

29. The mill blank in claim 1 wherein the mill blank has a Barcol Hardness value greater than about 5% of the Barcol Hardness of a Standard Fumed Silica Mill Blank.

30. The mill blank in claim 1 wherein the mill blank a Barcol Hardness value greater than about 15% of the Barcol Hardness of a Standard Fumed Silica Mill Blank.

31. The mill blank in claim 1 wherein the mill blank has a Cuttability value greater than about 50% of the Cuttability of a Standard Fumed Silica Mill Blank.

32. The mill blank in claim 1 wherein the mill blank has a Cuttability value greater than about 100% of the Cuttability of a Standard Fumed Silica Mill Blank.

33. The mill blank in claim 1 wherein the filler is at least about 50% by weight of the total weight of the mill blank.

34. The mill blank in claim 1 wherein the filler is at least about 65% by weight of the total weight of the mill blank.

35. The mill blank in claim 1 wherein the filler is at least about 80% by weight of the total weight of the mill blank.

15. A carvable mill blank for making a dental prosthetic comprising

a) a resin component and

b) a fluoride releasing component.

22. A method of making a dental prosthetic comprising the steps of

a) mixing a paste comprising a resin and a filler,

b) shaping the paste into a desired blank configuration,

c) minimizing material discontinuities from the paste,

d) curing the paste into a blank,

e) carving the blank into a desired shape and morphology,

wherein the blank is substantially free of cracks and fabricated such that the blank passes a Thermal Shock Test.

23. The method of claim 22 further comprising the step of:

f) adding additional material to the carved blank.

24. The method of claim 22 further comprising the step of:

f) attaching the carved blank to tooth or bone structure.

25. The method of claim 22 further comprising the steps of:

f) manually changing the morphology of the carved blank and

g) finishing the outer surface of the carved blank.

26. The method of claim 22 wherein an intermediate step between curing and carving the paste comprises attaching a handle to the cured paste and wherein the carving is performed by a milling machine.

27. The method of claim 22 wherein the carving step is performed by a hand-held instrument.