Abrasion resistant coating compositions based on silane hydrolysates and aluminium compounds and corresponding abrasion and shock resistant coated articles

• US 20030165698A1
• Filed: 10/25/2002
• Published: 09/04/2003
• Est. Priority Date: 03/08/1993
• Status: Abandoned Application

• Current Assignee: Anne Robert, Philippe Vaneeckhoutte, Yves Leclaire
• Original Assignee: Anne Robert, Philippe Vaneeckhoutte, Yves Leclaire
• Inventors: Leclaire, Yves, Vaneeckhoutte, Philippe, Robert, Anne
• Application Number:
  US10/281,259
• Publication Number:
  US 20030165698A1
• Time in Patent Office: Days
• US Class Current: 428/447
• CPC Class Codes: C03C 1/008 for the production of films or coatings
• CPC Class Codes: C03C 17/001 General methods for coating; Devices therefor
• CPC Class Codes: C03C 17/007 containing a dispersed phase, e.g. particles, fibres or flakes, in a continuous phase
• CPC Class Codes: C03C 2203/28 functional groups, e.g. vinyl, glycidyl
• CPC Class Codes: C08K 13/02 Organic and inorganic ingredients
• CPC Class Codes: C08K 3/36 Silica
• CPC Class Codes: C08L 83/00 Compositions of macromolecular compounds obtained by reactions forming in the main chain of the macromolecule a linkage containing silicon with or without sulfur, nitrogen, oxygen or carbon only; Compositions of derivatives of such polymers
• CPC Class Codes: C08L 83/06 containing silicon bound to oxygen-containing groups C08L83/12 takes precedence
• CPC Class Codes: C09D 183/06 containing silicon bound to oxygen-containing groups C09D183/12 takes precedence
• CPC Class Codes: G02B 1/105 Protective coatings
• CPC Class Codes: G02B 1/14 Protective coatings, e.g. hard coatings
• CPC Class Codes: Y10T 428/31663 As siloxane, silicone or silane

Abstract

Abrasion resistant coating compositions based on silane hydrolysates and aluminium compounds and corresponding abrasion and shock resistant coated articles

The invention relates to a hardenable composition for an abrasion resistant coating comprising the following constituents:

A—an epoxytrialkoxysilane hydrolysate,

B—a hydrolysate of a silane having formula (I)

where T¹ and T² each react to give a OH group on hydrolysis and Z¹ and Z² are unreactive organic groups,

C—colloidal silica,

D—a specific aluminium catalyst,

E—optionally, an organic solvent with a boiling point between 70° C. and 140° C.;

and to corresponding coated articles, which can have non-reflective treatments.

Claims

1. Hardenable composition for an abrasion resistant coating comprising the following constituents:

A—

a silane hydrolysate containing an epoxy group and three alkoxy groups, the latter groups being directly bonded to the silicon atom,

B—

a silane hydrolysate having formula (I);

where T¹ and T² are groups which will each react to give a OH group on hydrolysis of the silane of formula (I),

Z¹ and Z² are organic groups bonded to the silicon atom by a Si—

C bond which do not contain a group capable of reacting with the hydrolysed silanes present in the composition,

C—

colloidal silica,

D—

an aluminium compound selected from;

aluminium chelates,

compounds having formulated (III) or (IV)

(R′

O)_3-nAl(OSiR″

₃)_n  

 

(IV)

wherein;

R and R′

are linear or branched alkyl groups with 1 to 10 carbon atoms,

R″

is a linear or branched alkyl group with 1 to 10 carbon atoms, a phenyl group, a

group where R has the meaning given above, and n is a whole number from 1 to 3.

2. Composition according to claim 1 characterised in that it further comprises, when the aluminium compound is an aluminium chelate:

E—

an organic solvent whose boiling point T at atmospheric pressure is between 70°

C. and 140°

C.

3. Composition according to claim 1 or claim 2 characterised in that the silane containing an epoxy group has the following formula (V)

4. Composition according to claim 3 characterised in that the silane having formula (V) is γ

-glycidoxypropyltrimethoxysilane.

5. Composition according to any one of the preceding claims characterised in that in formula (I) of constituent B:

T¹ and T² are alkoxy groups with 1 to 10 carbon atoms, and

Z¹ and Z² are selected from alkyl groups with 1 to 10 carbon atoms and aryl groups with 6 to 10 carbon atoms, such as the phenyl group.

6. Composition according to claim 5 characterised in that the silane of formula (I) is selected from dimethyldimethoxysilane, dimethyldiethoxysilane and methylphenyldimethoxysilane.

7. Composition according to any one of the preceding claims characterised in that it further comprises an alcohol type solvent.

8. Composition according to any one of the preceding claims characterised in that the following proportions by weight are employed for the constituents A, B, C, D and E in the composition:

130 to 230 parts of constituent A,

20 to 150 parts of constituent B,

200 to 600 parts of constituent C,

5 to 20 parts of constituent D,

optionally, 20 to 50 parts of constituent E,

9. Composition according to any one of the preceding claims characterised in that it contains at least 1% by weight of water.

10. Composition according to any one of the preceding claims characterised in that the theoretical dry content of the composition is 5% to 20% by weight of solid material from constituent B.

11. Composition according to claim 10 characterised in that said theoretical dry content is 8% to 16% by weight of solid material from constituent B.

12. Composition according to claim 11 characterized in that said theoretical dry content is 10% to 15% by weight of solid material from constituent B.

13. Organic material article bearing an abrasion resistant coating produced by hardening a composition according to any one of the preceding claims.

14. Coated article according to claim 13 characterised in that said article comprises a diethylene glycol di(allylcarbonate) polymer.

15. Coated article according to claim 13 or claim 14 characterised in that it is in the form of an ophthalmic lens.

16. Coated article according to claim 15 characterised in that it comprises at least one nonreflective coating on the surface of the abrasion resistant coating.

17. Coated article according to claim 16 characterised in that the nonreflective coating is constituted by a mono- or multilayer film of metallic oxides.