Hyaluronic acid anti-adhesion barrier

• US 20040013714A1
• Filed: 03/20/2003
• Published: 01/22/2004
• Est. Priority Date: 07/28/1999
• Status: Abandoned Application

• Current Assignee: United States Surgical Corporation (Medtronic Plc)
• Original Assignee: United States Surgical Corporation (Medtronic Plc)
• Inventors: Zhang, Guanghui
• Application Number:
  US10/404,584
• Publication Number:
  US 20040013714A1
• Time in Patent Office: Days
• US Class Current: 424/443
• CPC Class Codes: A61F 2013/00217 not adhering to the wound with wax A61F2013/00161
• CPC Class Codes: A61L 31/042 Polysaccharides
• CPC Class Codes: A61L 31/146 Porous materials, e.g. foams or sponges
• CPC Class Codes: A61L 31/16 Biologically active materials, e.g. therapeutic substances A61L31/047 takes precedence
• CPC Class Codes: A61P 17/02 for treating wounds, ulcers, burns, scars, keloids, or the like
• CPC Class Codes: C08B 37/0072 Hyaluronic acid, i.e. HA or hyaluronan; Derivatives thereof, e.g. crosslinked hyaluronic acid (hylan) or hyaluronates
• CPC Class Codes: C08L 5/08 Chitin; Chondroitin sulfate; Hyaluronic acid; Derivatives thereof

Abstract

Methods of forming crosslinked hyaluronic acid anti-adhesion barriers, crosslinked hyaluronic acid anti-adhesions barriers, methods for preventing or inhibiting adhesions, and methods of promoting healing of a wound are provided. The method of forming the crosslinked hyaluronic acid anti-adhesion barrier includes freeze-drying a solution including hyaluronic acid to form a hyaluronic acid foam, which is then reacted with a crosslinking agent to form a crosslinked hyaluronic acid foam. The crosslinked hyaluronic acid foam is mixed with a solution containing hyaluronic acid to form an anti-adhesion barrier.

Claims

1. A method of forming an anti-adhesion barrier comprising:

freeze-drying a solution including hyaluronic acid to form a foam;

reacting the foam with a crosslinking agent to form a crosslinked foam; and

mixing the crosslinked foam with an aqueous solution containing hyaluronic acid to form an anti-adhesion barrier.

2. The method according to claim 1 wherein the concentration of the solution including hyaluronic acid is from about 0.5 to about 4.0% by weight hyaluronic acid.

3. The method according to claim 1 wherein during the freeze-drying step the solution including hyaluronic acid is frozen at a temperature of about −

94 to about −

130°

C.

4. The method according to claim 1 wherein the solution including hyaluronic acid is freeze-dried at less than about 50×

10<sup>−

3</sup> torr and about −

10°

C.

5. The method according to claim 1 wherein the crosslinking agent is selected from the group consisting of di-epoxides, polyfunctional epoxides, diisocyanates, polyisocyanates, polyhydric alcohols, water-soluble carbodiimides, diaminoalkanes, diamines, polycarboxylic acids, diacid halides and dimethylol urea.

6. The method according to claim 5 wherein the crosslinking agent is a diacid halide.

7. The method according to claim 6 wherein the diacid halide is diglycolyl chloride.

8. The method according to claim 1 wherein a solution of crosslinking agent contains from about 10 to about 80 % by weight crosslinking agent.

9. The method according to claim 1 wherein the proportion of foam to crosslinking agent is from about 3.0 to about 100 grams foam/gram of crosslinking agent.

10. The method according to claim 1 wherein the aqueous solution containing hyaluronic acid solution contains from about 0.5 to about 4.0% by weight hyaluronic acid.

11. The method according to claim 1 wherein the proportion of the crosslinked foam to the aqueous solution containing hyaluronic acid is from about 0.2 to about 1.0 grams crosslinked foam/ml aqueous solution containing hyaluronic acid.

17. An anti-adhesion barrier produced according to the method of claim 1.

18. The anti-adhesion barrier according to claim 17 wherein the solution including hyaluronic acid contains from about 0.5 to about 4.0% by weight hyaluronic acid.

19. The anti-adhesion barrier according to claim 17 wherein the crosslinking agent is a diacid halide.

20. The anti-adhesion barrier according to claim 19 wherein the diacid halide is diglycolyl chloride.

21. A composition comprising an antiadhesion barrier according to claim 17, and a pharmaceutically acceptable carrier.

22. The composition according to claim 21 further including a medicinal agent.

12. An anti-adhesion barrier which is a gel produced by combining a freeze-dried crosslinked hyaluronic acid foam with an aqueous solution comprising hyaluronic acid.

13. The anti-adhesion barrier according to claim 12 wherein the crosslinked foam is crosslinked with a diacid halide.

14. The anti-adhesion barrier according to claim 13 wherein the diacid halide is diglycolyl chloride.

15. A composition comprising an antiadhesion barrier according to claim 12, and a pharmaceutically acceptable carrier.

16. The composition according to claim 15 further including a medicinal agent.

23. A method of preventing or inhibiting the formation of adhesions comprising applying an effective amount of the anti-adhesion barrier according to claim 12 to a wound site.

24. The method according to claim 23 wherein the crosslinked foam is crosslinked with diglycolyl chloride.

25. A method of promoting healing of a wound comprising applying an effective amount of the anti-adhesion barrier according to claim 12 to the wound.

26. A two-part kit comprising

a first part including a freeze-dried crosslinked hyaluronic acid foam;

and a second part including a solution including hyaluronic acid.

27. The kit according to claim 26 wherein the crosslinked hyaluronic acid foam is crosslinked with a diacid halide.

28. The kit according to claim 27 wherein the diacid halide is diglycolyl chloride.

29. The kit according to claim 26 further including means for combining the crosslinked hyaluronic acid foam and the solution including hyaluronic acid.

30. The kit according to claim 26 further including a medicinal agent.

31. An anti-adhesion barrier comprising a hyaluronic acid foam, a crosslinking agent and an aqueous solution containing hyaluronic acid.

32. The anti-adhesion barrier according to claim 31 wherein the crosslinking agent is selected from the group consisting of di-epoxides, polyfunctional epoxides, diisocyanates, polyisocyanates, polyhydric alcohols, water-soluble carbodiimides, diaminoalkanes, diamines, polycarboxylic acids, diacid halides and dimethylol urea.

33. The anti-adhesion barrier according to claim 32 wherein the crosslinking agent is a diacid halide.

34. The anti-adhesion barrier according to claim 33 wherein the diacid halide is diglycolyl chloride.

35. The anti-adhesion barrier according to claim 31 wherein the solution containing hyaluronic acid contains from about 0.5 to about 4.0% by weight hyaluronic acid.

36. A composition comprising an anti-adhesion barrier according to claim 31, and a pharmaceutically acceptable carrier.

37. The composition according to claim 36 further including a medicinal agent.