Thermal storage medium, process for producing the same and thermal storage system using the same

• US 20040046147A1
• Filed: 04/25/2003
• Published: 03/11/2004
• Est. Priority Date: 04/26/2002
• Status: Abandoned Application

• Current Assignee: Nippon Shokubai Company Limited
• Original Assignee: Nippon Shokubai Company Limited
• Inventors: Ieuji, Tomomi, Matsuda, Yasuhiro
• Application Number:
  US10/423,031
• Publication Number:
  US 20040046147A1
• Time in Patent Office: Days
• US Class Current: 252/70
• CPC Class Codes: C09K 5/063 Materials absorbing or liberating heat during crystallisation; Heat storage materials
• CPC Class Codes: F28D 20/02 using latent heat
• CPC Class Codes: Y02E 60/14 Thermal energy storage

Abstract

The present invention is a thermal storage medium obtained by dispersing, in an oil-in-water manner, a mixture comprising an oil substance having a thermal storing property by phase change, an aqueous medium and a dispersant, wherein an amount of change in a volume average particle diameter of a dispersion of said oil substance after carrying out a 50 times of repetition of solidification/melting by phase change is within ±50% relative to a volume average particle diameter before carrying out the repetition of solidification/melting.

Claims

1. A thermal storage medium obtained by dispersing, in an oil-in-water manner, a mixture comprising an oil substance having a thermal storing property by phase change, an aqueous medium and a dispersant,

wherein an amount of change in a volume average particle diameter of a dispersion of said oil substance after carrying out a 50 times of repetition of solidification/melting by phase change is within ±

50% relative to a volume average particle diameter before carrying out the repetition of solidification/melting.

2. The thermal storage medium according to claim 1,

wherein said thermal storage medium comprises a nucleating agent.

3. The thermal storage medium according to claim 1,

wherein said dispersant comprises a nonionic surfactant.

4. The thermal storage medium according to claim 1,

wherein said dispersant comprises a surfactant,

said surfactant comprising one having an index of hydrophile-lipophile balance of less than 12 and one having an index of hydrophile-lipophile balance of not less than 12.

5. The thermal storage medium according to claim 4,

wherein said surfactant has an index of hydrophile-lipophile balance of whole surfactant of not less than 5 but not more than 15,

the index being determined from a mass fraction of each surfactant constituting said surfactant.

6. The thermal storage medium according to claim 1,

wherein, in said thermal storage medium, a concentration of the dispersant in a dispersant aqueous solution comprising said aqueous medium and said dispersant at a thermal storage temperature is 0.01 to 4 times as compared to a saturated concentration of the dispersant.

7. The thermal storage medium according to claim 1,

wherein said dispersant comprises at least one species selected from the group consisting of polyoxyethylene alkyl ether and polyoxyethylene sorbitan alkyl ester,

said polyoxyethylene alkyl ether having an average molar number of addition of ethylene oxide of not less than 20 and a total number of carbon atoms of not less than 15, and

said polyoxyethylene sorbitan alkyl ester having an average molar number of addition of ethylene oxide of not less than 20 and a total number of carbon atoms of not less than 15.

8. The thermal storage medium according to claim 1,

wherein said oil substance is constituted by two or more components.

9. The thermal storage medium according to claim 1, wherein a viscosity of said dispersion is 5 to 2,000 mPa·

s at 4°

C., with a content of said oil substance in said dispersion being 50% by mass.

10. The thermal storage medium according to claim 1,

wherein a viscosity of said dispersion is 5 to 2,000 mPa·

s at 4°

C., with a content of said oil substance in said dispersion being 50% by mass after carrying out phase change of solidification/melting on said oil substance in said dispersion.

11. The thermal storage medium according to claim 1,

wherein said dispersion comprises a surfactant and a polymer dispersant.

12. The thermal storage medium according to claim 1,

wherein said thermal storage medium is used under contact with or in the presence of metal.

13. A process for producing the thermal storage medium according to claim 1,

which comprises subjecting the thermal storage medium to phase change and then re-dispersing the same,

said thermal storage medium being obtained by dispersing, in an oil-in-water manner, a mixture comprising said oil substance, said aqueous medium and said dispersant.

14. A process for producing the thermal storage medium according to claim 1,

which comprises a step of dispersing said oil substance by using a line mixer.

15. A process for producing the thermal storage medium according to claim 1,

which comprises subjecting the thermal storage medium to phase change and then re-dispersing the same by using a static mixer,

said thermal storage medium being obtained by dispersing, in an oil-in-water manner, a mixture comprising said oil substance, said aqueous medium and said dispersant.

16. A thermal storage apparatus or a thermal storage system,

which is obtained by using the thermal storage medium according to claim 1 or a thermal storage medium produced by the process for producing the thermal storage medium according to any one of claims 13 to 15.