Hemostatic wound dressings and methods of making same

• US 20040193088A1
• Filed: 03/25/2003
• Published: 09/30/2004
• Est. Priority Date: 03/25/2003
• Status: Active Grant

• Current Assignee: Dwayne Lee Looney, Guanghui Zhang, Jian Xin Guo, John Crilley, Sanyog Manohar Pendharkar
• Original Assignee: Dwayne Lee Looney, Guanghui Zhang, Jian Xin Guo, John Crilley, Sanyog Manohar Pendharkar
• Inventors: Zhang, Guanghui, Guo, Jian Xin, Looney, Dwayne Lee, Pendharkar, Sanyog Manohar, Crilley, John
• Granted Patent: US 7,019,191 B2
• Time in Patent Office: Days
• US Class Current: 602/48
• CPC Class Codes: A61L 15/28 Polysaccharides or their derivatives A61L15/225 takes precedence
• CPC Class Codes: A61L 15/425 Porous materials, e.g. foams or sponges
• CPC Class Codes: A61L 2400/04 Materials for stopping bleeding

Abstract

The present invention is directed to methods of making wound dressings that include the steps of providing a solution of a water-soluble or water-swellable biocompatible polymer dissolved in a solvent for the polymer, providing a fabric substrate having a first surface and a second surface opposing the first surface, the fabric having properties effective for use as a hemostat and containing fibers prepared from a biocompatible polymer, contacting the fabric substrate with the polymer solution under conditions effective to distribute the polymer solution substantially homogenously on the first and second surfaces and through the fabric substrate, transferring the fabric substrate having the polymer solution substantially homogenously distributed there through to a lyophilization unit under conditions effective to maintain the homogeneous distribution on and throughout the substrate, and lyophilizing the fabric having the polymer solution distributed there through, thereby providing a porous, polymeric matrix substantially homogeneously distributed on the first and second surfaces and through the fabric, the matrix being made-up of the lyophilized water-soluble or water-swellable polymer.

Claims

1. A process for the manufacture of a hemostatic wound dressing, comprising:

providing a polymer solution comprising a water-soluble or water-swellable biocompatible polymer dissolved in a solvent for said polymer,

providing a fabric substrate comprising a first surface and a second surface opposing said first surface, said fabric having properties effective for use as a hemostat and comprising fibers prepared from a biocompatible polymer,

contacting said fabric substrate with said polymer solution under conditions effective to distribute said polymer solution substantially homogenously on said first and second surfaces and through said fabric substrate,

transferring said fabric substrate having said polymer solution substantially homogenously distributed there through to a lyophilization unit under conditions effective to maintain said homogeneous distribution on and throughout said substrate; and

lyophilizing said fabric having said polymer solution distributed there through;

thereby providing a porous, polymeric matrix substantially homogeneously distributed on said first and second surfaces and through said fabric substrate, said matrix comprising said lyophilized water-soluble or water-swellable polymer.

2. The method of claim 1 wherein said water-soluble or water-swellable polymer is selected from the group consisting of polysaccharides, polyacrylic acids, polymethacrylic acids, polyamines, polyimines, polyamides, polyesters, polyethers, polynucleotides, polynucleic acids, polypeptides, proteins, poly (alkylene oxides), polythioesters, polythioethers, polyvinyls and polymers comprising lipids.

3. The method of claim 2 wherein said water-soluble or water-swellable polymer is a polysaccharide.

4. The method of claim 3 wherein said polysaccharide is selected from the group consisting of cellulose, cellulose derivatives, chitin, carboxymethyl chitin, hyaluronic acid, salts of hyaluronic acid, alginate, alginic acid, propylene glycol alginate, glycogen, dextran, dextran sulfate, curdlan, pectin, pullulan, xanthan, chondroitin, chondroitin sulfates, carboxymethyl dextran, carboxymethyl chitosan, heparin, heparin sulfate, heparan, heparan sulfate, dermatan sulfate, keratin sulfate, carrageenans, chitosan, starch, amylose, amylopectin, poly-N-glucosamine, polymannuronic acid, polyglucuronic acid, polyguluronic acid and derivatives of the above.

5. The method of claim 4 wherein said polysaccharide comprises sodium carboxymethyl cellulose.

6. The method of claim 5 wherein the weight ratio of said sodium carboxymethyl cellulose to said fabric in said wound dressing is from about 1:

99 to about 20;

80.

7. The method of claim 1 wherein said biocompatible fiber comprises collagen, calcium alginate, chitin, polyester, polypropylene, polysaccharides, polyacrylic acids, polymethacrylic acids, polyamines, polyimines, polyamides, polyesters, polyethers, polynucleotides, polynucleic acids, polypeptides, proteins, poly (alkylene oxide), polyalkylenes, polythioesters, polythioethers, polyvinyls and polymers comprising lipids.

8. The method of claim 7 wherein said biocompatible polymer comprises an oxidized polysaccharide.

9. The method of claim 8 wherein said biocompatible polymer comprises oxidized regenerated cellulose.

10. The method of claim 9 wherein said oxidized regenerated cellulose comprises aldehyde-oxidized regenerated cellulose.

11. The method of claim 9 wherein said oxidized regenerated cellulose comprises carboxylic-oxidized regenerated cellulose.

12. The method of claim 6 wherein said biocompatible polymer comprises carboxylic-oxidized regenerated cellulose.

13. The method of claim 12 wherein prior to contacting said fabric substrate with said polymer solution said fabric substrate is exposed to a temperature of from about 4°

C. to about 90°

C., at a relative humidity of from about 10% to about 90%, for a time of from about 1 hour to about 48 months.

14. The method of claim 13 wherein said fabric substrate is exposed to a temperature of from about 18°

C. to about 50°

C., at a relative humidity of from about 60% to about 80%, for a time of from about 72 hours to about 366 hours.

15. The method of claim 14 wherein said fabric substrate is exposed to a temperature of about 50°

C., at a relative humidity of about 70%, for a time of about 168 hours.

16. The method of claim 1 wherein said contacting is conducted in a container comprising said polymer solution and said fabric substrate disposed therein.

17. The method of claim 1 wherein said transferring of said fabric substrate having said polymer solution substantially homogeneously distributed there through is conducted by transferring said fabric substrate having said polymer solution substantially homogeneously distributed there through onto a support means and placing said support means having said fabric disposed thereon into the lyophilization unit, said support means comprising properties effective to substantially prevent physical deformation of said fabric substrate during said transfer and said lyophilization.

18. The method of claim 17 wherein said support means comprises a polymer.

19. The method of claim 18 wherein said support means comprises a sheet of high-density polyethylene having a thickness of from about 50 mils to about 200 mils.

20. The method of claim 19 wherein said support means comprises a sheet of high-density polyethylene having a thickness of from about 60 mils to about 150 mils.

21. The method of claim 17 wherein said fabric substrate comprising said polymer solution substantially homogeneously distributed there through is transferred onto the support means at a rate of from about 8 inches per minute to about 2 inches per minute and is contacted with said support means such that the angle of incidence between said fabric substrate and said support means ranges from about 20°

to about 90°

.

22. The method of claim 21 wherein the rate of transfer is about 7 inches per minute and the angle of incidence is about 45°

.

23. The method of claim 1 further comprising the step of forming said wound dressing into a desired shape from said fabric substrate having said porous, polymeric matrix substantially homogenously distributed on said first and second surfaces and there through.

24. A wound dressing prepared according to the method of claim 1.