Composition for in vivo vessel repair
First Claim
Patent Images
1. A biocompatible polymer composition, suitable for in vivo vessel repair, comprising a matrix pre-polymer, a filler and a curing agent, wherein said composition has a viscosity of 2 000 to 12 000 cSt at 25°
- C. and wherein said biocompatible polymer composition is curable in the presence of a curing catalyst at 37°
C. to form a cured material with an elongation until rupture of at least 5% and an elastic modulus of at least 1 mpa.
2 Assignments
0 Petitions
Accused Products
Abstract
The present invention relates to a biocompatible polymer composition, suitable for in vivo vessel repair, comprising a matrix pre-polymer, a filler and a curing agent, wherein said composition wherein said biocompatible polymer composition is curable in the presence of a curing catalyst at 37° C. to form a cured material with an elongation until rupture of at least 5% and an elastic modulus of at least 1 MPa.
42 Citations
23 Claims
-
1. A biocompatible polymer composition, suitable for in vivo vessel repair, comprising a matrix pre-polymer, a filler and a curing agent, wherein said composition has a viscosity of 2 000 to 12 000 cSt at 25°
- C. and wherein said biocompatible polymer composition is curable in the presence of a curing catalyst at 37°
C. to form a cured material with an elongation until rupture of at least 5% and an elastic modulus of at least 1 mpa. - View Dependent Claims (2, 3, 5, 7, 16, 17, 18, 19, 20, 21, 22, 23)
- C. and wherein said biocompatible polymer composition is curable in the presence of a curing catalyst at 37°
-
4. (canceled)
-
6. (canceled)
-
8-15. -15. (canceled)
Specification