Fire retarded polymer composition

• US 20050075442A1
• Filed: 11/27/2002
• Published: 04/07/2005
• Est. Priority Date: 11/29/2001
• Status: Abandoned Application

• Current Assignee: Bromine Compounds Limited (ICL Group Ltd.)
• Original Assignee: Bromine Compounds Limited (ICL Group Ltd.)
• Inventors: Peled, Michael, Titelman, Grigory I, Bron, Samuel
• Application Number:
  US10/496,912
• Publication Number:
  US 20050075442A1
• Time in Patent Office: Days
• US Class Current: 524/495
• CPC Class Codes: C08K 3/04 Carbon
• CPC Class Codes: C08K 5/0066 Flame-proofing or flame-retarding additives

Abstract

A fire retarded polymer composition is disclosed, which comprises a polymer component, at least one halogen-containing fire retardant and a heat expandable graphite. The polymer component is selected from among polystyrenes, polyesters and polyolefins. The halogen of the fire retardant is bromine or chlorine, and the total amount of the fire retardant and the heat expandable graphite is from about 6.5 to about 40% by weight. The composition may also contain a metal oxide fire retardant, such as antimony trioxide, but if so, it contains it in amounts much lower than those required in prior art compositions to achieve the same degree of fire retardancy. It is preferred that the heat expandable graphite be such as to expand 50 times or more on shock heating from room temperature to 900° C. The process by which the expandable graphite is produced is not critical, and it is known, for example, to produce it by oxidation of natural or artificial graphite.

Claims

1. A fire retardant polymer composition comprising heat expandable graphite (HEG) and at least one halogen-containing fire retardant, wherein the polymer component of said composition is selected from the group consisting of polystyrenes, polyesters, polyethylene, polypropylene and copolymers of propylene with ethylene.

2. A fire retardant composition according to claim 1, wherein the halogen-containing fire retardant is a bromine fire-retardant.

3. A fire retardant compositions according to claim 1, wherein the halogen containing fire retardant is a chlorine-fire retardant.

4. A fire retardant composition according to any one of claims 1 to 3, wherein the heat expandable graphite (HEG) and the halogen-containing fire-retardant are contained in the polymer composition in a total amount ranging from about 6.5 to about 40% by weight.

5. A fire retardant composition according to claim 4, wherein the polymer is selected from the group consisting of polystyrens and polyesters and the heat expandable graphite (HEG) and the halogen-containing fire-retardant are contained in the polymer composition in a total amount ranging from about 6.5 to about 30% by weight.

6. A fire retardant composition according to claim 4, wherein the polymer is a polyolefin and the heat expandable graphite (HEG) and the halogen-containing fire-retardant are contained in the polymer composition in a total amount ranging from about 24.3 to about 40% by weight.

7. A fire retardant composition according to any one of claims 1 to 6, further comprising a metal oxide fire retardant.

8. Fire retardant composition according to claim 7, wherein the metal oxide fire retardant is selected from the group consisting of antimony oxide, zinc oxide, zinc borate, and ferric oxide.

9. Fire retardant composition according to claim 8, wherein the antimony oxide fire retardant is antimony trioxide or antimony pentaoxide.

10. A fire retardant composition according to any one of claims 7 to 9, wherein the heat expandable graphite (HEG), the halogen-containing fire-retardant and the metal oxide are contained in the polymer composition in a total amount ranging from about 7.2 to about 34% by weight.

11. A fire retardant composition according to claim 10, wherein the polymer is selected from the group consisting of polystyrens and polyesters and the heat expandable graphite (HEG), the halogen-containing fire-retardant and the metal oxide are contained in the polymer composition in a total amount ranging from about 7.2 to about 21.5% by weight.

12. A fire retardant composition according to claim 11, wherein the polymer is selected from the group consisting of polystyrens and polyesters and the heat expandable graphite (HEG), the halogen-containing fire-retardant and the metal oxide are contained in the polymer composition in a total amount ranging from about 7.2 to about 16.7% by weight.

13. A fire retardant composition according to claim 10, wherein the polymer is polyolefin and the heat expandable graphite (HEG), the halogen-containing fire-retardant and the metal oxide are contained in the polymer composition in a total amount ranging from about 13.9 to about 34% by weight.

14. A fire retardant composition according to claim 13, wherein the polymer is polyolefin and the heat expandable graphite (HEG), the halogen-containing fire-retardant and the metal oxide are contained in the polymer composition in a total amount ranging from about 16 to about 20% by weight.

15. A fire retarded polymer composition according to any one of claims 1 to 5 and 7 to 12 comprising:

(a) a polymer selected from the group consisting of polystyrenes or polyesters at a percent weight which totals to 100% by weight the composition;

(b) from about 2 to about 15 percent by weight of heat expandable graphite,

(c) a halogen-containing fire retardant in an amount corresponding to from about 2 to about 11% by weight of halogen; and

, optionally,

(d) 0 to about 3.4 percent by weight of a metal oxide.

16. A fire retarded polymer composition according to claim 15 comprising:

(a) a polymer selected from the group consisting of polystyrenes or polyesters at a percent weight which totals to 100% by weight the composition;

(b) from about 2 to about 6 percent by weight of heat expandable graphite,

(c) a halogen-containing fire retardant in an amount corresponding to from about 2 to about 8.5% by weight of halogen; and

, optionally,

(d) 0 to about 2.2 percent by weight of a metal oxide.

17. A fire retarded polymer composition according to any one of claims 1 to 4, 6 to 10 and 13 to 14 comprising:

(a) a polyolefin polymer at a percent weight which totals to 100% by weight the composition;

(b) from about 5 to about 13.5 percent by weight of heat expandable graphite,

(c) a halogen-containing fire retardant in an amount corresponding to from about 4 to about 22% by weight of halogen; and

optionally,

(d) 0 to about 7 percent by weight of a metal oxide.

18. A fire retarded polymer composition according to claim 17 comprising

(a) a polyolefin polymer at a percent weight which totals to 100% by weight the composition;

(b) from about 6 to about 8 percent by weight of heat expandable graphite,

(c) a halogen-containing fire retardant in an amount corresponding to from about 5 to about 15% by weight of halogen; and

optionally,

(d) 0 to about 4 percent by weight of a metal oxide.

19. A fire retardant composition according to any one of claims 1 to 18, wherein the heat expandable graphite is obtained by any conventional route from a natural graphite or artificial graphite.

20. A fire retardant composition according to claim 19, wherein the heat expandable graphite, produced by oxidation of a natural graphite or artificial graphite in sulfuric acid or in nitric acid, can be additionally allowed to neutralize with a basic material.

21. A fire retardant composition according to any one of claims 19 and 20, wherein the heat expandable graphite is obtained by any conventional route from a natural graphite or artificial graphite, and which upon rapid heating from room temperature to 900°

C. has a weight loss of 10-40%.

22. A fire retardant composition according to any one of claims 19 to 21, wherein the heat expandable graphite is obtained by any conventional route from a natural graphite or artificial graphite, and which upon rapid heating from room temperature to 900°

C. has a specific volume expansion of not less than 50 times.

23. A fire retardant composition according to any one of claims 19 to 22, wherein the heat expandable graphite has such a particle size distribution that not more than 25% by weight of graphite particles pass through a 75 mesh sieve.

24. A fire retardant composition according to any one of claims 1 to 23, wherein the heat expandable graphite particles is surface treated with a coupling agent.

25. A fire retardant composition according to any one of claims 1 to 24, wherein the halogen-containing fire retardant is selected from the group consisting of decabromodiphenyl oxide, decabromodiphenyl ethane, brominated trimethylphenyl indane, chlorine- or bromine containing cycloaliphatic compounds, tetrabromobisphenol A or tetrabromobisphenol A bis(2,3 dibromopropyl ether) or tetrabromobisphenol A based epoxy, chlorinated paraffin, chlorinated polethylene, pentabromobenzyl acrylate or poly(pentabromobenzyl acrylate), and compounds containing phosphorus, nitrogen or sulfur heteroatoms in the molecule

26. A fire retardant composition according to claim 25, wherein the halogen-containing fire retardant which contains phosphorus, nitrogen or sulfur heteroatoms in the molecule is tris(tribromoneopentyl) phosphate, tris(tribromophenyl)triazine or tetrabromobisphenol-S-bis(2,3dibromopropyl ether).

27. A fire retarded polymer composition according to any one of claims 1 to 26, wherein the polymer, the halogen-containing fire retardant and optionally, the metal oxide, each consists of either a single component or a mixture of components of the same category.

28. A fire retarded polymer composition according to any one of claims 1 to 27, wherein the polymer is a polymer or mixture of polymers characterized in neither autonomously forming char, nor cross-linking themselves under flame.

29. A fire retarded polymer composition according to any one of claims 1 to 5, 7 to 12, 15, 16 and 19 to 28, wherein the polymer is selected from the group consisting of homopolymers of styrene, rubber modified high-impact polystyrenes (HIPS), and acrylonitrile-butadiene-styrene copolymers (ABS).

30. A fire retarded polymer composition to any one of claims 1 to 5, 7 to 12, 15, 16 and 19 to 28, wherein the polymer is selected from the group consisting of polybutylene terphthalate and polyethylene terphthalate.

31. A fire retarded polymer composition according to any one of claims 1 to 4, 6 to 10, 13, 14, 17, 18 and 19 to 28, wherein the polyolefin polymer is selected from the group consisting of homopolymers of ethylene comprising high density polyethylene (HDPE), low density polyethylene (LDPE), linear low density polyethylene (LLDPE), homopolymers of polypropylene (PP homo-polymers), and block or random copolymers of propylene with ethylene (UP co-polymers).

32. A fire retarded polymer composition according to any one of claims 1 to 5, 7 to 12, 15, 16 and 19 to 30, wherein the polymer is selected from the group consisting of mixtures of two or more of polystyrenes and/or polyesters with one another or with polymer or polymers of different types.

33. A fire retarded polymer composition according to any one of claims 1 to 4, 6 to 10, 13, 14, 17, 18 and 19 to 28, 31 and 32, wherein the polymer is selected from the group consisting of mixtures of two or more of polyolefines with one another or with polymer or polymers of different types.

34. A fire retarded polymer composition according to any one of claims 1 to 33, further comprising additives chosen from the group consisting of metal hydroxides, colorants, antioxidants, light stabilizers, light absorbing agents, process oils, coupling agents, lubricants, blowing agents and fillers, anti-dripping agents and cross-linking agents.

35. A Fire retarded polymer composition according to any one of claims 1 to 34, further comprising at least one coupling agent.

36. A fire retardant composition, substantially as described.