Two-package curing type polyurethane coating composition and coated article
First Claim
1. A two package curing type polyurethane coating composition comprising a resin solution containing an acrylic polyol and a curing agent solution containing a polyisocyanate, wherein the resin solution contains urethane resin beads (A) in the amount of 25 to 50 parts by weight and an organic matting agent (B) in the amount of 3 to 10 parts by weight and contains said urethane resin beads (A) and said organic matting agent (B) in total of 30 parts by weight or more, respectively, to 100 parts by weight of solid contents of the resin solution, and said acrylic polyol and said polyisocyanate have OH group/NCO group (equivalent ratio) in the range of (4.5/1) to (1.5/1).
3 Assignments
0 Petitions
Accused Products
Abstract
The present invention aims to give a two package curing type polyurethane coating composition which can form a film having soft, wet and dry feelings simultaneously and which maintain general properties of a coating composition such as the designing property, film strength, resistance to scratching, discoloration resistance, pot life, resistance to stains with fats and oils, and the like and to provide a coated article with such a two package curing type polyurethane coating composition. A two package curing type polyurethane coating composition comprising a resin solution containing an acrylic polyol and a curing agent solution containing a polyisocyanate, wherein the resin solution contains urethane resin beads (A) in the amount of 25 to 50 parts by weight and an organic matting agent (B) in the amount of 3 to 10 parts by weight and contains the urethane resin beads (A) and the organic matting agent (B) in total of 30 parts by weight or more, respectively, to 100 parts by weight of solid contents of the resin solution, and the acrylic polyol and the polyisocyanate have OH group/NCO group (equivalent ratio) in the range of (4.5/1) to (1.5/1).
17 Citations
5 Claims
-
1. A two package curing type polyurethane coating composition comprising a resin solution containing an acrylic polyol and a curing agent solution containing a polyisocyanate,
wherein the resin solution contains urethane resin beads (A) in the amount of 25 to 50 parts by weight and an organic matting agent (B) in the amount of 3 to 10 parts by weight and contains said urethane resin beads (A) and said organic matting agent (B) in total of 30 parts by weight or more, respectively, to 100 parts by weight of solid contents of the resin solution, and said acrylic polyol and said polyisocyanate have OH group/NCO group (equivalent ratio) in the range of (4.5/1) to (1.5/1).
Specification