• US 20050179150A1
• Filed: 03/22/2005
• Published: 08/18/2005
• Est. Priority Date: 01/06/2003
• Status: Abandoned Application

• Current Assignee: Koninklijke Philips Electronics N.V. (Koninklijke Philips N.V.)
• Original Assignee: Koninklijke Philips Electronics N.V. (Koninklijke Philips N.V.)
• Inventors: Couzin, Dennis I., Cornelissen, Hugo Johan, Edwards, David N., Mehrabi, Reza, Bharadwaj, Rishikesh K.
• Application Number:
  US11/086,511
• Publication Number:
  US 20050179150A1
• Time in Patent Office: Days
• US Class Current: 264/1.340
• CPC Class Codes: B29C 2035/0811 using induction
• CPC Class Codes: B29C 2035/0822 using IR radiation
• CPC Class Codes: B29C 2035/0838 using laser
• CPC Class Codes: B29C 2035/0855 using microwave
• CPC Class Codes: B29C 2035/0861 using radio frequency
• CPC Class Codes: B29C 2059/023 Microembossing
• CPC Class Codes: B29C 35/0272 using lost heating elements, i.e. heating means incorporated and remaining in the formed article for preforms with internal stresses B29C61/0625; joining using lost heating elements B29C65/34; making electrically conductive articles B29C70/882
• CPC Class Codes: B29C 35/0805 using electromagnetic radiation
• CPC Class Codes: B29C 35/0888 using transparant moulds
• CPC Class Codes: B29C 59/02 by mechanical means, e.g. pressing B29C59/007 takes precedence; embossing expanded porous articles B29C44/5627
• CPC Class Codes: B29C 59/04 using rollers or endless belts
• CPC Class Codes: B29L 2011/00 Optical elements, e.g. lenses, prisms
• CPC Class Codes: B32B 2307/412 Transparent
• CPC Class Codes: B32B 2307/42 Polarizing, birefringent, filtering
• CPC Class Codes: B32B 2307/516 mono-axially
• CPC Class Codes: B32B 2307/704 Crystalline
• CPC Class Codes: B32B 2307/706 Anisotropic
• CPC Class Codes: B32B 2398/20 Thermoplastics
• CPC Class Codes: B32B 27/08 of synthetic resin
• CPC Class Codes: B32B 27/308 comprising acrylic (co)polymers
• CPC Class Codes: B32B 27/36 : comprising polyesters
• CPC Class Codes: B32B 3/30 : characterised by a layer formed with recesses or projections, e.g. hollows, grooves, protuberances, ribs apertured layer B32B3/266; layer with cavities or internal voids B32B3/26
• CPC Class Codes: B32B 38/06 : Embossing
• CPC Class Codes: B32B 7/12 : using interposed adhesives or interposed materials with bonding properties
• CPC Class Codes: G02B 5/3083 : Birefringent or phase retarding elements G02B5/3008, G02B5/3016 take precedence; systems for polarisation control G02B27/286; manufacturing phase modulating patterns by lithographic processes G03F7/001
• CPC Class Codes: Y10T 428/24479 : including variation in thickness
• CPC Class Codes: Y10T 428/2457 : Parallel ribs and/or grooves

Abstract

A method of making an embossed optical sheet material includes: providing an optically anisotropic, uniaxially oriented polymer substrate having a first major surface and a second major surface; heating a patterned tool using radiant energy from a radiant energy source, wherein the pattern comprises a plurality of parallel raised microstructures having a longitudinal direction; pressing the tool against the first major surface of the polymer substrate such that the longitudinal direction of the raised microstructures is substantially parallel to the direction of orientation of the polymer substrate, to soften the first major surface of the polymer substrate and emboss groove-shaped microchannels into the polymer substrate; cooling the embossed polymer substrate; and separating the tool from the polymer substrate; wherein the orientation of the polymer substrate is unchanged throughout the polymer substrate and first major surface.

Claims

1. A method of making an embossed optical sheet material comprising:

providing an optically anisotropic, uniaxially oriented polymer substrate having a first major surface and a second major surface;

heating a patterned tool using radiant energy from a radiant energy source, wherein the pattern comprises a plurality of parallel raised microstructures having a longitudinal direction;

pressing the tool against the first major surface of the polymer substrate such that the longitudinal direction of the raised microstructures is substantially parallel to the direction of orientation of the polymer substrate, to soften the first major surface of the polymer substrate and emboss groove-shaped microchannels into the polymer substrate;

cooling the embossed polymer substrate;

separating the tool from the polymer substrate;

wherein the orientation of the polymer substrate is unchanged throughout the polymer substrate and first major surface.

2. The method of claim 1 wherein the uniaxially oriented polymer substrate is a birefringent film having a birefringence in the range of 0.1 to 0.5.

3. The method of claim 1 wherein the polymer substrate comprises a semi-crystalline thermoplastic polymer.

4. The method of claim 1 wherein the polymer substrate comprises an amorphous glassy thermoplastic polymer.

5. The method of claim 1, wherein the radiantly heating, the pressing, and the separating, are all performed as parts of a roll-to-roll process.

6. The method of claim 5, wherein the tool is part of a patterned belt that includes a patterned tool surface and a flexible backing.

7. The method of claim 6, wherein the flexible backing is thermally insulative relative to the patterned tool surface.

8. The method of claim 7, wherein the patterned tool surface includes a metallic surface.

9. The method of claim 8, wherein the metallic surface includes a nickel surface.

10. The method of claim 1, wherein the patterned tool surface includes a metallic surface.

11. The method of claim 10, wherein the metallic surface includes a nickel surface.

12. The method of claim 10, wherein the metallic surface is backed with a relatively thermally insulative material.

13. The method of claim 1, wherein the patterned tool surface includes a nonmetallic surface.

14. The method of claim 13, wherein the nonmetallic surface includes a semiconductor surface.

15. The method of claim 13, wherein the nonmetallic surface is backed with a relatively thermally insulative material.

16. The method of claim 1, wherein the pressing the patterned tool against the sheet commences after the radiantly heating.

17. The method of claim 1, wherein the radiant energy from the radiant energy source has most of its energy in a wavelength range of between 0.4 to 2 μ

m (microns).

18. The method of claim 1, wherein the radiant energy source includes a blackbody emitter.

19. The method of claim 18, wherein the blackbody emitter has a temperature of at least 2000 K.

20. The method of claim 18, wherein the blackbody emitter has a temperature of at least 3000 K.

21. The method of claim 18, wherein the blackbody emitter has a temperature of about 3200 K.

22. The method of claim 1, further including passing the radiant energy through a relatively radiantly transparent roller.

23. The method of claim 22, wherein the passing the energy through the roller includes focusing the radiant energy.