Pneumatic tire having an innerliner comprised of butyl rubber and dispersion of corncob granules

• US 20060000532A1
• Filed: 06/30/2004
• Published: 01/05/2006
• Est. Priority Date: 06/30/2004
• Status: Active Grant

• Current Assignee: Goodyear Tire & Rubber Company
• Original Assignee: Goodyear Tire & Rubber Company
• Inventors: Sandstrom, Paul Harry
• Granted Patent: US 7,134,468 B2
• Time in Patent Office: Days
• US Class Current: 152/510
• CPC Class Codes: B60C 1/0008 Compositions of the inner liner
• CPC Class Codes: C08K 3/013 Fillers, pigments or reinforcing additives
• CPC Class Codes: C08L 21/00 Compositions of unspecified rubbers
• CPC Class Codes: C08L 23/22 Copolymers of isobutene; Butyl rubber ; Homo- or copolymers of other iso-olefins
• CPC Class Codes: C08L 2666/02 Organic macromolecular compounds, natural resins, waxes or and bituminous materials
• CPC Class Codes: C08L 2666/26 Natural polymers, natural resins or derivatives thereof according to C08L1/00 - C08L5/00, C08L89/00, C08L93/00, C08L97/00 or C08L99/00
• CPC Class Codes: C08L 97/02 Lignocellulosic material, e.g. wood, straw or bagasse manufacture of articles made from lignocellulosic material by dry processes B27N
• CPC Class Codes: Y10S 152/16 Air impermeable liner

Abstract

The present invention relates to a pneumatic rubber tire having an integral innerliner of a sulfur cured rubber composition. The innerliner rubber composition is comprised of at least one elastomer selected from bromobutyl rubber and chlorobutyl rubber which also contains a dispersion therein of corncob granules.

Claims

1. A pneumatic rubber tire having an integral innerliner of a sulfur cured rubber composition comprised of, based upon parts by weight per 100 parts by weight of total rubber (phr),

(A) 100 phr of elastomers comprised of:

(1) butyl type rubber as;

(a) about 60 to 100 phr of halobutyl rubber selected from at least one of bromobutyl rubber and chlorobutyl rubber and their mixtures, and

(b) zero to about 30 phr of butyl rubber;

(2) zero to about 20 phr of at least one diene-based elastomer selected from polymers of at least one of isoprene and 1,3-butadiene and copolymers of styrene and at least one of isoprene and 1,3-butadiene, and their mixtures, and

(3) zero to about 30 phr of at least one partially depolymerized bromobutyl rubber, chlorobutyl butyl rubber, butyl rubber and their mixtures, and

(B) about 1 to about 30 phr of corncob granules comprised of granules of the woody ring of corncobs, wherein at least 90 percent of said corncob granules have an average diameter in a range of from about 50 to about 500; and

(C) about 30 to about 110 phr of reinforcing filler comprised of;

(1) about 30 to about 110 phr of rubber reinforcing carbon black, or

(2) about 5 to about 70 phr of rubber reinforcing carbon black and from about 5 to about 70 phr of synthetic amorphous precipitated silica aggregates together with a coupling agent having a moiety reactive with hydroxyl groups on said precipitated silica aggregates and another different moiety interactive with said diene-based elastomer(s).

2. The pneumatic rubber tire of claim 1 wherein, for said integral innerliner composition, said (A) 100 phr of elastomers is comprised of:

(A) butyl type rubber as;

(1) about 60 to about 95 phr of halobutyl rubber selected from at least one of bromobutyl rubber and chlorobutyl rubber, and

(2) about 5 to about 20 phr of butyl rubber;

(B) zero to about 20 phr of said diene-based elastomer selected from polymers of at least one of isoprene and 1,3-butadiene and copolymers of styrene and at least one of isoprene and 1,3-butadiene, and their mixtures, and

(C) zero to about 30 phr of said at least one partially depolymerized bromobutyl rubber, chlorobutyl butyl rubber, butyl rubber and their mixtures.

3. The pneumatic tire of claim 1 wherein, for said integral innerliner composition, said (A) 100 phr of elastomers is comprised of:

(A) butyl type rubber as;

(1) about 60 to about 95 phr of halobutyl rubber selected from at least one of bromobutyl rubber and chlorobutyl rubber, and

(2) zero to about 30 phr of butyl rubber;

(B) from about 5 to about 15 phr of said at least one diene-based elastomer selected from polymers of at least one of isoprene and 1,3-butadiene and copolymers of styrene and at least one of isoprene and 1,3-butadiene and their mixtures, and

(C) zero to about 30 phr of said at least one partially depolymerized bromobutyl rubber, chlorobutyl butyl rubber, butyl rubber and their mixtures.

4. The pneumatic tire of claim 1 wherein, for said integral innerliner composition, said (A) 100 phr of elastomers is comprised of:

(A) butyl type rubber as;

(1) about 60 to about 90 phr of halobutyl rubber selected from at least one of bromobutyl rubber and chlorobutyl rubber, and

(2) about 5 to about 20 phr of butyl rubber;

(B) from about 5 to about 15, phr of said at least one diene-based elastomer selected from polymers of at least one of isoprene and 1,3-butadiene and copolymers of styrene and at least one of isoprene and 1,3-butadiene and their mixtures, and

(C) zero to about 30 phr of said at least one partially depolymerized bromobutyl rubber, chlorobutyl butyl rubber, butyl rubber and their mixtures.

5. The pneumatic tire of claim 1 wherein, for said integral innerliner composition, said (A) 100 phr of elastomers is comprised of:

(A) butyl type rubber as;

(1) about 60 to about 95 phr of halobutyl rubber selected from at least one of bromobutyl rubber and chlorobutyl rubber, and

(2) zero to about 30 phr of butyl rubber;

(B) from zero to about 20 phr of said at least one diene-based elastomer selected from polymers of at least one of isoprene and 1,3-butadiene and copolymers of styrene and at least one of isoprene and 1,3-butadiene and their mixtures, and

(C) about 5 to about 20 phr of said at least one partially depolymerized bromobutyl rubber, chlorobutyl butyl rubber, butyl rubber and their mixtures.

6. The pneumatic tire of claim 1 wherein, for said integral innerliner composition, said (A) 100 phr of elastomers is comprised of:

(A) butyl type rubber as;

(1) about 60 to about 90 phr of halobutyl rubber selected from at least one of bromobutyl rubber and chlorobutyl rubber, and

(2) about 5 to about 20 phr of butyl rubber;

(B) from zero to about 20 phr of said at least one diene-based elastomer selected from polymers of at least one of isoprene and 1,3-butadiene and copolymers of styrene and at least one of isoprene and 1,3-butadiene and their mixtures, and

(C) about 5 to about 20 phr of said at least one partially depolymerized bromobutyl rubber, chlorobutyl butyl rubber, butyl rubber and their mixtures.

7. The pneumatic tire of claim 1 wherein, for said integral innerliner composition, said (A) 100 phr of elastomers is comprised of:

(A) butyl type rubber as;

(1) about 60 to about 90 phr of halobutyl rubber selected from at least one of bromobutyl rubber and chlorobutyl rubber, and

(2) zero to about 30 phr of butyl rubber;

(B) about 5 to about 15 phr of said at least one diene-based elastomer selected from polymers of at least one of isoprene and 1,3-butadiene and copolymers of styrene and at least one of isoprene and 1,3-butadiene and their mixtures, and

(C) about 5 to about 20 phr of said at least one partially depolymerized bromobutyl rubber, chlorobutyl butyl rubber, butyl rubber and their mixtures.

8. The pneumatic tire of claim 1 wherein, for said integral innerliner composition, said (A) 100 phr of elastomers is comprised of:

(A) butyl type rubber as;

(1) about 60 to about 85 phr of halobutyl rubber selected from at least one of bromobutyl rubber and chlorobutyl rubber, and

(2) about 5 to about 20 phr of butyl rubber;

(B) about 5 to about 15 phr of said at least one diene-based elastomer selected from polymers of at least one of isoprene and 1,3-butadiene and copolymers of styrene and at least one of isoprene and 1,3-butadiene and their mixtures, and

(C) about 5 to about 20 phr of said at least one partially depolymerized bromobutyl rubber, chlorobutyl butyl rubber, butyl rubber and their mixtures.

9. The tire of claim 1 wherein said integral innerliner composition contains from about 2 to about 20 phr of corncob granules comprised of granules of the woody ring of corncobs, wherein at least 90 percent of said corncob granules have an average diameter in a range of from about 70 to about 200 microns.

10. The tire of claim 2 wherein said integral innerliner composition contains from about 2 to about 20 phr of corncob granules comprised of granules of the woody ring of corncobs, wherein at least 90 percent of said corncob granules have an average diameter in a range of from about 70 to about 200 microns.

11. The tire of claim 3 wherein said integral innerliner composition contains from about 2 to about 20 phr of corncob granules comprised of granules of the woody ring of corncobs, wherein at least 90 percent of said corncob granules have an average diameter in a range of from about 70 to about 200 microns.

12. The tire of claim 4 wherein said integral innerliner composition contains from about 2 to about 20 phr of corncob granules comprised of granules of the woody ring of corncobs, wherein at least 90 percent of said corncob granules have an average diameter in a range of from about 70 to about 200 microns.

13. The tire of claim 5 wherein said integral innerliner composition contains from about 2 to about 20 phr of corncob granules comprised of granules of the woody ring of corncobs, wherein at least 90 percent of said corncob granules have an average diameter in a range of from about 70 to about 200 microns.

14. The tire of claim 6 wherein said integral innerliner composition contains from about 2 to about 20 phr of corncob granules comprised of granules of the woody ring of corncobs, wherein at least 90 percent of said corncob granules have an average diameter in a range of from about 70 to about 200 microns.

15. The tire of claim 7 wherein said integral innerliner composition contains from about 2 to about 20 phr of corncob granules comprised of granules of the woody ring of corncobs, wherein at least 90 percent of said corncob granules have an average diameter in a range of from about 70 to about 200 microns.

16. The tire of claim 8 wherein said integral innerliner composition contains from about 2 to about 20 phr of corncob granules comprised of granules of the woody ring of corncobs, wherein at least 90 percent of said corncob granules have an average diameter in a range of from about 70 to about 200 microns.

17. The tire of claim 1 wherein said integral innerliner composition contains at least one of talc, clay, mica and calcium carbonate, and their mixtures, in a range from about 2 to 25 phr.

18. The tire of claim 1 wherein, for said innerliner composition, said about 30 to about 110 phr of reinforcing filler is rubber reinforcing carbon black.

19. The tire of claim 1 wherein, for said innerliner composition, said about 30 to about 110 phr of reinforcing filler is about 5 to about 70 phr of rubber reinforcing carbon black and from about 5 to about 70 phr of synthetic amorphous precipitated silica aggregates.

20. The tire of claim 1 wherein said innerliner composition contains said precipitated silica reinforcing filler and a coupling agent therefor selected from bis(3-trialkoxysilylpropyl) polysulfides wherein at least two, and optionally all three, of its alkoxy groups are ethoxy groups and its polysulfidic bridge is comprised of an average of from about 2 to about 4, alternatively from about 2 to about 2.6 or an average of from about 3.4 to about 3.8 connecting sulfur atoms, and an alkoxyorganomercaptosilane which optionally has its mercpto moiety blocked with a suitable blocking agent during the mixing thereof with the rubber composition, wherein said alkoxy groups thereof are comprised of ethoxy groups.