Method and composition for coating mat and articles produced therewith

• US 20060035032A1
• Filed: 08/11/2004
• Published: 02/16/2006
• Est. Priority Date: 08/11/2004
• Status: Abandoned Application

• Current Assignee: Atlas Roofing Corporation (Hood Cos., Inc.)
• Original Assignee: Atlas Roofing Corporation (Hood Cos., Inc.)
• Inventors: Blanpied, Robert H., Murphy, Freddie Lee, Diller, Charles E.
• Application Number:
  US10/915,694
• Publication Number:
  US 20060035032A1
• Time in Patent Office: Days
• US Class Current: 427/389.900
• CPC Class Codes: B05D 1/28 performed by transfer from the surfaces of elements carrying the liquid or other fluent material, e.g. brushes, pads, rollers
• CPC Class Codes: B05D 2203/35 Glass
• CPC Class Codes: B05D 2252/02 of indefinite length
• CPC Class Codes: B32B 17/04 bonded with or embedded in a plastic substance
• CPC Class Codes: C03C 25/12 General methods of coating; Devices therefor
• CPC Class Codes: C03C 25/20 Contacting the fibres with applicators, e.g. rolls
• CPC Class Codes: C03C 25/465 Coatings containing composite materials
• CPC Class Codes: C03C 25/475 containing colouring agents
• CPC Class Codes: D06N 3/0022 Glass fibres
• CPC Class Codes: D06N 3/0063 Inorganic compounding ingredients, e.g. metals, carbon fibres, Na2CO3, metal layers; Post-treatment with inorganic compounds

Abstract

A coated glass mat is formed by applying a coating mixture to a surface of a glass mat substrate, and then by drying the coated glass mat. As a result of the coating composition, the resultant mat attains a predetermined target spectral characteristic, e.g., a desired or target color. The coating mixture is formed by mixing together a mineral pigment filler, a solvent, a binder (e.g., organic latex binder), (optionally) a dispersing agent, and (optionally) a colorant. The type and amount of the mineral pigment filler is judiciously chosen to impart the predetermined spectral characteristic to the coated glass mat upon drying. In fact, although the coating mixture may include a separate, optional colorant, the mineral pigment filler is chosen as a primary color determinate for the completed coated glass mat. The primary determinative influence of the mineral pigment filler on the spectral characteristic of the coated glass mat is evident by the relative amounts of the mineral pigment filler and the colorant. In particular, a maximum ratio of “as received weight” of colorant to “dry weight” of filler is less than about 0.003; a ratio of “dry weight” of colorant to “dry weight” of the coating mixture does not exceed 0.4%. Advantageously, use of the inexpensive mineral pigment filler as the primary color determinate for the completed coated glass mat obviates the need is for larger amounts of more expensive colorant, thereby providing economy as well as efficiency in production.

Claims

1. A method of making a coated glass mat comprising:

forming a coating mixture by mixing together a mineral pigment filler, a solvent, and a binder;

applying the coating mixture to a surface of a glass mat substrate to form a coated glass mat;

drying the coated glass mat;

the mineral pigment filler having been chosen to impart a predetermined spectral characteristic to the coated glass mat upon drying.

7. The method of claim 1, claim 3, claim 4, or claim 5, wherein the target or predetermined spectral characteristic is different than a pre-mixture spectral characteristic of the mineral pigment filler.

8. The method of claim 1, claim 3, claim 4, or claim 5, wherein the spectral characteristic of the coated glass mat upon drying is a source-indicative spectral characteristic.

9. The method of claim 7, wherein the pre-mixture spectral characteristic of the mineral pigment filler is characterized by coordinates in L*a*b color space wherein color space coordinate b is greater than or equal to +7.0, on average.

10. The method of claim 1, 2, or claim 4, wherein the coating mixture further comprises a colorant, and wherein a ratio of a dry weight amount of any colorant to a dry weight amount of the mineral pigment filler included in the coating mixture is less than about 0.002 and preferably less than about 0.001.

11. The method of claim 1, 2, claim 4, or claim 5, wherein the coating mixture further comprises a colorant, and wherein a dry weight amount of any colorant does not exceed 0.4% of total dry weight of the coating mixture.

12. The method of claim 1, 2, claim 4, or claim 5, wherein the mineral pigment filler is limestone.

13. The method of claim 12, wherein the limestone is characterized by coordinates in L*a*b color space wherein color space coordinate b is greater than or equal to +7.0, on average.

14. The method of claim 1, 2, or 4, wherein the binder is an organic latex.

15. The method of claim 1, claim 3, claim 4, or claim 5, wherein the spectral characteristic of the mineral pigment filler is a yellow color characterized by coordinates in L*a*b color space wherein color space coordinate b is greater than or equal to +7.0, on average.

16. The method of claim 1, claim 3, claim 4, or claim 5, wherein the spectral characteristic of the coated glass mat product is a yellow color characterized by coordinates in L*a*b color space having the following ranges:

L=+75≦

L≦

+85;

−

1.0≦

a≦

+1.5; and

, +50≦

b≦

+58.

17. The method of claim 16, wherein a pre-mixture spectral characteristic of the mineral pigment filler is characterized substantially by coordinates in L*a*b color space having the following ranges:

+82≦

L≦

+92;

0≦

a≦

+1.5; and

, +2.0≦

b≦

+8.5.

18. The method of claim 16, wherein the mineral pigment filler is obtained from a geographical region in or around Lowell, Fla.

19. The method of claim 16, wherein the mineral pigment filler is obtained from a geographical region in or around and Crawford, Tex.

20. The method of claim 16, wherein the spectral characteristic of the coated glass mat product is characterized substantially by the following coordinates in L*a*b color space:

L=+78.6;

a=+1.2; and

b=+52.2.

21. The method of claim 16, wherein the spectral characteristic of the coated glass mat product is characterized substantially by the following coordinates in L*a*b color space:

L=+83.87;

a=+0.44; and

b=+53.45.

22. The method of claim 1, claim 3, claim 4, or claim 5, wherein the spectral characteristic of the coated glass mat product is a blue color characterized substantially by coordinates in L*a*b color space having the following ranges:

+65≦

L≦

+75;

−

15≦

a≦

−

4.0; and

, −

25≦

b −

5.0.

23. The method of claim 22, wherein the spectral characteristic of the coated glass mat product is characterized substantially by the following coordinates in L*a*b color space:

L=+73.15;

a=−

10.49; and

b=−

8.75.

24. The method of claim 22, wherein the spectral characteristic of the coated glass mat product is characterized substantially by the following coordinates in L*a*b color space:

L=+67.58;

a=−

8.48; and

b=−

7.68.

25. The method of claim 1, claim 3, claim 4, or claim 5, wherein the spectral characteristic of the coated glass mat product is a silver color characterized substantially by coordinates in L*a*b color space having the following ranges:

+40≦

L≦

+70;

0≦

a≦

+1.0; and

, +1.0≦

b≦

+5.0.

26. The method of claim 25, wherein the spectral characteristic of the mineral pigment filler is characterized substantially by the following coordinates in L*a*b color space:

L=+65.63;

a=+0.50; and

b=+4.10.

27. The method of claim 1, claim 3, claim 4, or claim 5, wherein the spectral characteristic of the coated glass mat product is a pink color characterized by coordinates in L*a*b color space having the following ranges:

+60≦

L≦

+75;

+10≦

a≦

+20; and

, +2.0≦

b≦

+5.0.

28. The method of claim 26, wherein the spectral characteristic of the coated glass mat product is characterized substantially by the following coordinates in L*a*b color space:

L=+69.09;

a=+12.81; and

b=+3.99.

29. The method of claim 26, wherein the spectral characteristic of the coated glass mat product characterized substantially by the following coordinates in L*a*b color space:

L=+64.44;

a=+19.91; and

b=+3.41.

2. A method of making a coated glass mat comprising:

forming a coating mixture by mixing together a mineral pigment filler, a solvent, and a binder;

applying the coating mixture to a surface of a glass mat substrate to form a coated glass mat;

drying the coated glass mat;

the mineral pigment filler having been chosen as a primary color determinate for the coated glass mat.

3. The method of claim 2, wherein the mineral pigment filler is chosen as the primary color determinate for imparting a predetermined spectral characteristic to the coated glass mat.

4. A method of making a coated glass mat comprising:

determining a target spectral characteristic for a completed coated glass mat;

forming a coating mixture by mixing together a mineral pigment filler, a solvent, and a binder;

applying the coating mixture to a surface of a glass mat substrate to form a coated glass mat;

drying the coated glass mat and thereafter obtaining the completed coating glass mat;

the mineral pigment filler having been chosen to achieve the target spectral characteristic.

5. A method of making a coated glass mat comprising:

forming a coating mixture by mixing together a mineral pigment filler, a solvent, a binder, and a colorant;

applying the coating mixture to a surface of a glass mat substrate to form a coated glass mat;

drying the coated glass mat;

a type of the mineral pigment filler, an amount of the mineral pigment filler, and an amount of the colorant being chosen to impart a predetermined spectral characteristic to the coated glass mat upon drying; and

wherein a ratio of a dry weight amount of the colorant to a dry weight amount of the mineral pigment filler included in the coating mixture is less than 0.002.

6. The method of claim 5, wherein the colorant is a pre-dispersed liquid colorant, and wherein the ratio of an as-received weight amount of the pre-dispersed liquid colorant to the dry weight amount of the mineral pigment filler included in the coating mixture is less than about 0.004.