Thermal electrochemical synthesis method for production of stable colloids of "naked" metal nanocrystals

• US 20060068026A1
• Filed: 06/16/2005
• Published: 03/30/2006
• Est. Priority Date: 08/11/2004
• Status: Abandoned Application

• Current Assignee: UT-Battelle LLC
• Original Assignee: UT-Battelle LLC
• Inventors: Hu, Michael Z., Easterly, Clay E.
• Application Number:
  US11/154,973
• Publication Number:
  US 20060068026A1
• Time in Patent Office: Days
• US Class Current: 424/618
• CPC Class Codes: A01N 2300/00 Combinations or mixtures of active ingredients covered by classes A01N27/00 - A01N65/48 with other active or formulation relevant ingredients, e.g. specific carrier materials or surfactants, covered by classes A01N25/00 - A01N65/48
• CPC Class Codes: A01N 25/04 Dispersions, emulsions, suspoemulsions, suspension concentrates or gels foams A01N25/16
• CPC Class Codes: A01N 25/12 Powders or granules A01N25/26 takes precedence
• CPC Class Codes: A01N 25/34 Shaped forms, e.g. sheets, not provided for in any other sub-group of this main group
• CPC Class Codes: A01N 59/16 Heavy metals; Compounds thereof
• CPC Class Codes: A61K 33/38 Silver; Compounds thereof
• CPC Class Codes: C25C 1/20 of noble metals
• CPC Class Codes: C25C 5/02 from solutions

Abstract

A method of making a colloidally stable suspension of naked metal nanocrystals includes the steps of: at least partly immersing a metallic sacrificial anode and a cathode into a body of essentially contaminant-free water, the metallic sacrificial anode that includes an essentially contaminant-free metal starting material for making nanocrystals; and applying a voltage potential across the anode and the cathode to form a colloidally stable suspension of naked metal nanocrystals composed essentially of metal from the metallic sacrificial anode.

Claims

1. A composition of matter comprising a colloidally stable suspension of naked metal nanocrystals having an average particle size of no more than 100 nm.

2. A composition of matter in accordance with claim 1 wherein said naked metal nanocrystals have an average particle size of no more than 50 nm.

3. A composition of matter in accordance with claim 2 wherein said naked metal nanocrystals have an average particle size of no more than 20 nm.

4. A composition of matter in accordance with claim 3 wherein said naked metal nanocrystals have an average particle size of no more than 10 nm.

5. A composition of matter in accordance with claim 1 wherein said naked metal nanocrystals are essentially discrete.

6. A composition of matter in accordance with claim 1 wherein said metal comprises at least one metal selected from the group consisting of Ag, Au, Pd, Pt, Cu, Ru, Os, Ti, Fe, Cr, Co, Rh, Ni, Cd, Zn, Al, and any alloy comprising any of the foregoing.

7. A composition of matter in accordance with claim 6 wherein said nanocrystals consist essentially of Ag.

8. A method of making a colloidally stable suspension of naked metal nanocrystals comprising the steps of:

a. at least partly immersing a metallic sacrificial anode and a cathode into a body of essentially contaminant-free water, said metallic sacrificial anode comprising an essentially contaminant-free metal starting material for making nanocrystals; and

b. applying a voltage potential across said anode and said cathode to form a colloidally stable suspension of naked metal nanocrystals consisting essentially of metal from said metallic sacrificial anode.

9. A method in accordance with claim 8 wherein said metallic sacrificial anode comprises at least one metal selected from the group consisting of Ag, Au, Pd, Pt, Cu, Ru, Os, Ti, Fe, Cr, Co, Rh, Ni, Cd, Zn, Al, and any alloy comprising any of the foregoing.

10. A method in accordance with claim 9 wherein said metallic sacrificial anode consists essentially of Ag.

11. A method in accordance with claim 8 wherein said voltage potential is a DC voltage potential.

12. A method in accordance with claim 8 wherein said naked metal nanocrystals have an average particle size of no more than 100 nm.

13. A method in accordance with claim 12 wherein said naked metal nanocrystals have an average particle size of no more than 50 nm.

14. A method in accordance with claim 13 wherein said naked metal nanocrystals have an average particle size of no more than 20 nm.

15. A method in accordance with claim 14 wherein said naked metal nanocrystals have an average particle size of no more than 10 nm.

16. A method in accordance with claim 8 wherein said naked metal nanocrystals are essentially discrete.