Welding Forged Steel Single Piece Piston and Its Manufacturing Methods

• US 20070079775A1
• Filed: 04/05/2006
• Published: 04/12/2007
• Est. Priority Date: 10/08/2005
• Status: Abandoned Application

• Current Assignee: Shandong Binzhou Bohai Piston Inc., Ltd.
• Original Assignee: Shandong Binzhou Bohai Piston Inc., Ltd.
• Inventors: Zhang, Guohua, Wang, Hongmin, Ma, Xuejun, Wang, Lixia, Lin, Fenghua, Zhang, Shushan, Zhu, Junkui, Gao, Zhanyu
• Application Number:
  US11/278,715
• Publication Number:
  US 20070079775A1
• Time in Patent Office: Days
• US Class Current: 123/41.350
• CPC Class Codes: F02F 3/003 the parts being connected by casting, brazing, welding or clamping

Abstract

The present invention has provided a welding forged steel single piece piston and its manufacturing methods. A semi-finished head and a semi-finished skirt are forged respectively; the semi-finished head and semi-finished skirt are heat-treated respectively; rough machining is carried out respectively to the semi-finished head and the semi-finished skirt, and a face of weld between the two adjacent ring grooves is higher than the one under the combustion chamber; the head and the skirt are welded together through friction welding; an annular groove, a combustion chamber, a ring groove, a pinhole, an outer annulus and oil inlet/outlet holes are manufactured respectively; and the surface of the piston is phosphorized and graphitized. Compared with one-piece forged piston, it has better processing technology, because the head and skirt are forged respectively and then welded together. Over-all structural rigidity of the piston has been increased, and distortion of the ring groove in high temperature is slight because the cooling oil recess is sealed through welding. As the annular groove is located on the upper part of skirt, the weight of body of the piston is lowered and this kind of structure can accelerate engine oil returning on, decrease the clearance between the piston and the cylinder and reduce the engine oil consumption.

Claims

1. A welding forged steel single piece piston comprising a forged head;

a forged skirt welded and fixed with said forged head as a body of said piston;

a cooling oil recess located in the piston between a ring groove and a combustion chamber, said cooling oil recess is connected with the inner chamber of said piston through oil inlet/outlet holes;

an annular groove located on the upper part of said skirt and under the ring groove, said annular groove is connected with the inner chamber of said piston in the direction of major axis.

2. The welding forged steel single piece piston of claim 1, wherein said head and said skirt are welded together.

3. The welding forged steel single piece piston of claim 2, wherein the face of weld between the two adjacent ring grooves is higher than the face of weld under the combustion chamber, the two said faces are welded together.

4. Method for manufacturing of forged steel single piece piston comprises:

a) forge a semi-finished head and a semi-finished skirt respectively;

b) heat-treat the semi-finished head and the semi-finished skirt respectively;

c) rough machining the semi-finished head and the semi-finished skirt respectively in order to produce an inner chamber, an inner cooling oil recess and faces of friction welding, Meanwhile, the face of weld between two adjacent ring grooves is higher than the face of weld under a combustion chamber;

d) weld the semi-finished head and the semi-finished skirt together through friction welding;

e) manufacture an annular groove, a combustion chamber, a ring groove, a pinhole, an outer annulus and oil inlet/outlet holes respectively;

f) phosphoric and graphitiz the surface of said piston.

5. The method of claim 4, wherein the process of said heat treatment for the piston made of quenched and tempered steel are:

heating for 1-2 hours under 800-850°

C., then oil-cooled, then tempering under temperature 600°

C.±

10°

C. for 1.5-2.5 hours.

6. The method of claim 4, wherein the process of said heat treatment for the piston made of non quenched and tempered steel are:

air-cooled to room temperature, and make sure that the temperature shall be reduced from 1100°

C. (after being forged) to 500°

C. within 3-4 minutes.