POLYMER TRANSFER APPARATUS, METHODS, AND COMPOSITE WEBS

• US 20070176325A1
• Filed: 04/10/2007
• Published: 08/02/2007
• Est. Priority Date: 03/13/2003
• Status: Abandoned Application

• Current Assignee: 3M Innovative Properties Company (3M Company)
• Original Assignee: 3M Innovative Properties Company (3M Company)
• Inventors: Becker, Dennis, Alberg, Randall, Pavlis, Roger, Jackson, Byron, Wood, Leigh
• Application Number:
  US11/733,272
• Publication Number:
  US 20070176325A1
• Time in Patent Office: Days
• US Class Current: 264/288.400
• CPC Class Codes: A44B 18/0049 obtained by moulding processes compression moulding or articles of indefinite length characterised by the shape of the surface B29C43/222; screen moulding B29C67/08
• CPC Class Codes: A44B 18/0061 Male or hook elements A44B18/0053 takes precedence
• CPC Class Codes: B29C 43/222 characterised by the shape of the surface
• CPC Class Codes: B29C 43/28 incorporating preformed parts or layers, e.g. compression moulding around inserts or for coating articles
• CPC Class Codes: B29L 2031/729 Hook and loop-type fasteners
• CPC Class Codes: B32B 2274/00 Thermoplastic elastomer material thermoplastic elastomer fibres B32B2262/0215, thermoplastic elastomer particles B32B2264/0221, thermoplastic elastomer foam B32B2266/0292
• CPC Class Codes: B32B 2307/51 Elastic
• CPC Class Codes: B32B 27/12 next to a fibrous or filamentary layer
• CPC Class Codes: B32B 3/02 characterised by features of form at particular places, e.g. in edge regions non-uniform thickness B32B3/263
• CPC Class Codes: B32B 3/28 characterised by a layer comprising a deformed thin sheet , i.e. the layer having its entire thickness deformed out of the plane, e.g. corrugated, crumpled B32B29/08 takes precedence
• CPC Class Codes: B32B 37/025 Transfer laminating
• CPC Class Codes: B32B 5/04 characterised by a layer being specifically extensible by reason of its structure or arrangement , e.g. by reason of the chemical nature of the fibres or filaments
• CPC Class Codes: Y10T 428/249955 Void-containing component partially impregnated with adjacent component
• CPC Class Codes: Y10T 428/249991 Synthetic resin or natural rubbers

Abstract

Composite webs having one or more polymeric structures located on a substrate, methods of manufacturing the composite webs, and systems for manufacturing the composite webs are disclosed. The polymeric structures are formed using thermoplastic compositions deposited into one or more depressions on a forming tool. The forming tool is maintained at a temperature that is below the melt processing temperature of the thermoplastic composition.

Claims

1. A method for producing a composite web, the method comprising:

providing a forming tool comprising an exterior surface that comprises one or more depressions formed therein;

delivering a molten thermoplastic composition onto the exterior surface of the forming tool;

maintaining the exterior surface of the forming tool at a roll temperature that is below a melt processing temperature of the thermoplastic composition;

wiping the molten thermoplastic composition on the exterior surface of the forming tool, wherein at least some of the molten thermoplastic composition enters the one or more depressions;

transferring the thermoplastic composition in the one or more depressions to a substrate by contacting a first major surface of the substrate to the molten thermoplastic composition in the one or more depressions;

separating the substrate and the thermoplastic composition in the one or more depressions from the forming tool after the transferring, wherein a composite web is formed that comprises one or more polymeric structures of the thermoplastic composition located on the first major surface of the substrate, wherein the thermoplastic composition comprises one or more elastomeric polymeric components such that the one or more polymeric structures on the substrate exhibit elastic behavior; and

stretching the composite web and the one or more polymeric structures located thereon such that the substrate exhibits permanent elongation after the stretching and such that a portion of the one or more polymeric structures detaches from the first major surface of the substrate.

2. A method according to claim 1, wherein a portion of the thermoplastic composition in the one or more depressions that is proximate surfaces of the one or more depressions falls below the melt processing temperature of the thermoplastic composition after the depositing and before the thermoplastic composition in the one or more depressions contacts the first major surface of the substrate.

3. A method according to claim 1, wherein a portion of the thermoplastic composition in the one or more depressions that is distal from surfaces of the one or more depressions remains at or above the melt processing temperature at least until the thermoplastic composition in the one or more depressions contacts the first major surface of the substrate.

4. A method according to claim 1, wherein a first portion of the thermoplastic composition in the one or more depressions that is proximate surfaces of the one or more depressions falls below the melt processing temperature of the thermoplastic composition after the depositing and before the thermoplastic composition in the one or more depressions contacts the first major surface of the substrate,

and wherein a second portion of the thermoplastic composition in the one or more depressions that is distal from the surfaces of the one or more depressions remains at or above the melt processing temperature of the thermoplastic composition at least until the thermoplastic composition in the one or more depressions contacts the first major surface of the substrate.

5. A method according to claim 1, wherein the roll temperature is 20 degrees Celsius or more below a molten thermoplastic composition temperature at which the molten thermoplastic composition is delivered to the exterior surface of the forming tool.

6. A method according to claim 1, wherein delivering the molten thermoplastic composition onto the exterior surface of the forming tool comprises extruding the molten thermoplastic composition into an interface between the exterior surface of the forming tool and a doctor blade.

7. A method according to claim 1, wherein delivering the molten thermoplastic composition onto the exterior surface of the forming tool comprises extruding the molten thermoplastic composition onto a doctor blade, wherein the molten thermoplastic composition flows down a surface of the doctor blade to an interface between the doctor blade and the exterior surface of the roll.

8. A method according to claim 1, wherein the first major surface of the substrate comprises a porous surface, and wherein the transferring further comprises forcing a portion of the first major surface of the substrate against the thermoplastic composition in the one or more depressions, wherein a portion of the thermoplastic composition in at least some depressions of the one or more depressions infiltrates the porous surface.

9. A method according to claim 8, wherein the porous surface of the substrate comprises fibers, and further wherein the transferring further comprises encapsulating at least a portion of at least some of the fibers in the thermoplastic composition in the one or more depressions.

10. A method according to claim 1, wherein the first major surface of the substrate comprises fibers, and further wherein the transferring further comprises encapsulating at least a portion of at least some of the fibers in the thermoplastic composition by forcing the first major surface of the substrate against the thermoplastic composition in the one or more depressions.

11. A method according to claim 1, wherein the substrate comprises polymeric material with a melt processing temperature at or below the melt processing temperature of the thermoplastic composition.

12. A method according to claim 1, wherein the wiping leaves some of the molten thermoplastic composition on the exterior surface of the forming tool outside of the one or more depressions.

13. A method according to claim 1, wherein depositing the molten thermoplastic composition on the exterior surface of the forming tool comprises depositing two or more different molten thermoplastic compositions on the exterior surface of the forming tool.