ANTIMICROBIAL CONTACT LENSES WITH REDUCED HAZE AND PREPARATION THEREOF
First Claim
Patent Images
1. A method of preparing an antimicrobial lens comprising a metal salt, wherein said method comprises the steps of (a) treating a cured lens, with a solution comprising salt precursor, and (b) treating the lens of step (a) with a solution comprising a metal agent, wherein the molar ratio of said metal agent in its solution to the molar ratio of said salt precursor in its solution is greater than about 0.2.
1 Assignment
0 Petitions
Accused Products
Abstract
This invention relates to antimicrobial lenses containing metals and methods for their production.
-
Citations
16 Claims
-
1. A method of preparing an antimicrobial lens comprising a metal salt, wherein said method comprises the steps of
(a) treating a cured lens, with a solution comprising salt precursor, and (b) treating the lens of step (a) with a solution comprising a metal agent, wherein the molar ratio of said metal agent in its solution to the molar ratio of said salt precursor in its solution is greater than about 0.2.
-
8. A method of preparing an antimicrobial lens comprising a metal salt, wherein said method comprises the steps of
(a) treating a cured lens, with a solution comprising a metal agent, and (b) treating the lens of step (a) with a solution comprising a salt cursor, wherein the molar ratio of said metal agent in its solution to the molar ratio of said salt precursor in its solution is greater than about 0.2.
-
11. An antimicrobial lens comprising a metal salt, made by a method comprising the steps of
(a) treating a cured lens, with a solution comprising salt precursor, and (b) treating the lens of step (a) with a solution comprising a metal agent, wherein the molar ratio of said metal agent in its solution to the molar ratio of said salt precursor in its solution is greater than about 0.2.
-
14. An antimicrobial lens comprising a metal salt, made by a method comprising the steps of
(a) treating a cured lens, with a solution comprising a metal agent, and (b) treating the lens of step (a) with a solution comprising a salt precursor, wherein the molar ratio of said metal agent in its solution to the molar ratio of said salt precursor in its solution is greater than about 0.2.
Specification