METHOD OF APPLYING A THERMALLY SETTABLE COATING TO A PATTERNED SUBSTRATE

• US 20080182016A1
• Filed: 10/25/2007
• Published: 07/31/2008
• Est. Priority Date: 12/03/2002
• Status: Active Grant

• Current Assignee: Flint Acquisition Corp.
• Original Assignee: Integrated Paving Concepts Inc.
• Inventors: Juristovski, Alan, Wiley, Patrick Carl
• Granted Patent: US 8,133,540 B2
• Time in Patent Office: Days
• US Class Current: 427/136
• CPC Class Codes: E01C 19/43 Machines or arrangements for roughening or patterning freshly-laid paving courses, e.g. indenting rollers
• CPC Class Codes: E01C 23/028 Positioning or producing markings, e.g. by forcing marking materials into the surface, by scoring
• CPC Class Codes: E01C 23/14 for heating or drying foundation, paving, or materials thereon, e.g. paint E01C23/03 takes precedence; heating or drying devices incorporated in the paving E01C11/26; surface soil stabilisation by fusing, calcining or burning soil in situ E01C21/02; for street cleaning E01H1/08; melting snow or ice on surfacing E01H5/10
• CPC Class Codes: E01F 9/512 Preformed road surface markings, e.g. of sheet material; Methods of applying preformed markings

Abstract

This application relates to a method of applying a thermally settable coating to a patterned substrate, such as an asphalt surface. The coating is applied in one or more preformed thermoplastic sheets and heated in situ to conform the thermoplastic material to the pattern formed in the underlying substrate. In one embodiment of the invention a pattern is formed in the asphalt surface using a removable template which is impressed into the asphalt when it is in a pliable state. The pre-formed sheets are then applied to the patterned surface and gradually heated. In an alternative embodiment of the invention the template is impressed into the pre-formed sheet and asphalt surface simultaneously after the sheet has been heated to a suitable temperature in situ. A bond reduction agent may be used to minimize adhesion between the template and the heated thermoplastic material. In a further alternative embodiment of the invention the thermoplastic material may be stamped after it has melted and partially cooled to cause the thermoplastic to more precisely conform to the underlying pattern.

Claims

1. A method of applying a coating to a substrate comprising:

(a) forming a first pattern in said substrate;

(b) placing a first pre-formed thermally settable sheet on said substrate; and

(c) heating said sheet in situ to a temperature sufficient for said sheet to adhere to said substrate in a configuration conforming to said first pattern.

2. The method as defined in claim 1, wherein said sheet is formed of thermoplastic material.

3. The method as defined in claim 2, wherein said substrate is an asphalt surface.

4. The method as defined in claim 3, wherein said thermoplastic material is coated on said asphalt surface in a thickness between 30-150 mil.

5. The method as defined in claim 3, wherein said sheet comprises a first surface which is placed in contact with said asphalt surface and a second surface which is not placed in contact with said asphalt surface and wherein the step of heating said thermoplastic sheet in situ comprises gradually increasing the temperature of said sheet to enable said first surface of said sheet to bond consistently to said asphalt surface.

6. The method as defined in claim 5, further comprising providing a heating apparatus having a support frame extending over said sheet, wherein said heater is mounted for movement on said support frame in a travel path which periodically passes over said sheet to thereby gradually increase the temperature thereof.

7. The method as defined in claim 6, wherein said sheet is heated to a temperature between approximately 150-450°

F.

8. The method as defined in claim 7, wherein said sheet is heated to a temperature between approximately 300-400°

F.

9. The method as defined in claim 3, wherein said step of forming said first pattern comprises:

(a) heating said asphalt surface until said surface is pliable;

(b) placing a template on said asphalt surface;

(c) imprinting said template into said asphalt surface to form said first pattern; and

(d) removing said template from said asphalt surface.

10. The method as defined in claim 3, wherein said step of forming said first pattern comprises:

(a) forming said asphalt surface from pliable asphalt;

(b) placing a template on said asphalt surface;

(c) imprinting said template into said asphalt surface to form said first pattern; and

(d) removing said template from said asphalt surface.

11. The method as defined in claim 3, wherein said sheet is formed in a second pattern matching said first pattern and alignable therewith.

12. The method as defined in claim 3, wherein said sheet is subdividable into a plurality of discrete sections.

13. The method as defined in claim 3 comprising:

(a) providing at least one further pre-formed thermally settable sheet;

(b) placing said first pre-formed sheet and said at least one further pre-formed sheet on said asphalt surface in an aligned configuration; and

(c) gradually heating the sheets to bond said sheets to said asphalt surface in a configuration conforming to said first pattern.

14. The method as defined in claim 13, wherein said sheets are aligned adjacent one another in non-overlapping relation, wherein edges of adjacent sheets are contiguous.

15. The method as defined in claim 13, wherein said sheets are aligned adjacent one another in overlapping relation.

16. The method as defined in claim 14, wherein said first pattern comprises a plurality of impressions simulating grout lines and wherein said edges of adjacent sheets are aligned with said simulated grout lines.

17. The method as defined in claim 13, wherein said sheets are aligned such that one of said sheets at least partially surrounds another one of said sheets.

18. The method as defined in claim 3, wherein said sheet has a continuous upper surface.

19. The method as defined in claim 3, wherein said sheet has at least one opening formed therein.

23. The method as defined in claim 19, further comprising applying a bond reduction agent to at least one of said second surface of said sheet and said template to substantially prevent adherence of said sheet to said template.

20. A method of applying a thermally settable coating to a substrate comprising:

(a) placing a pre-formed thermally settable sheet on said substrate, said sheet having a first surface in contact with said substrate and a second surface not in contact with said substrate;

(b) heating said sheet in situ to a temperature sufficient for said first surface of said sheet to adhere to said substrate; and

(c) imprinting said sheet and said substrate to form a first pattern therein.

21. The method as defined in claim 20, wherein said imprinting step comprises:

(a) placing a template on said second surface of said sheet;

(b) compressing said template to form an impression in said first pattern in said sheet and said substrate; and

(c) removing said template from said second surface of said sheet to expose said first pattern.

22. The method as defined in claim 21, further comprising cooling said second surface of said sheet prior to placing said template thereon to substantially prevent adherence of said sheet to said template.

24. The method as defined in claim 20, wherein said sheet is formed from thermoplastic material.

25. The method as defined in claim 24, wherein said substrate is an asphalt surface.

26. The method as defined in claim 25, wherein said sheet is between approximately 30-150 mil in thickness.

27. The method as defined in claim 26 wherein said sheet is between approximately 50-125 mil in thickness.

28. The method as defined in claim 20, further comprising providing a heating apparatus having a support frame extending over said sheet, wherein said heater is mounted for movement on said support frame in a travel path which periodically passes over said sheet to thereby gradually increase the temperature thereof.

29. The method as defined in claim 28, wherein said sheet is heated to a temperature between approximately 150-450°

F.

30. The method as defined in claim 29, wherein said sheet is heated to a temperature between approximately 300-400°

F.

31. A method of applying a thermoplastic coating to an asphalt surface comprising:

(a) forming a first pattern in said asphalt surface;

(b) placing a pre-formed thermoplastic sheet having a thickness between 50-125 mil on said asphalt surface; and

(c) heating said thermoplastic sheet in situ to a temperature sufficient for said sheet to adhere to said asphalt surface in a configuration conforming to said first pattern.

32. A method of applying a thermoplastic coating to a substrate comprising:

(a) providing a pre-existing substrate having a first pattern formed therein;

(b) placing a pre-formed thermoplastic sheet having a thickness between 50-125 mil on said substrate; and

(c) heating said thermoplastic sheet in situ to a temperature sufficient for said sheet to adhere to said substrate in a configuration conforming to said first pattern.

33. The method as defined in claim 32, wherein the step of providing said pre-existing substrate having a first pattern formed therein comprises compressing a template into said substrate corresponding to said first pattern.

34. The method as defined in claim 33, wherein said template is compressed into said substrate when said substrate is in a heated state and said substrate is thereafter allowed to cool.

35. The method as defined in claim 32, wherein said coating is decorative.

36. A method of applying a thermoplastic coating to an asphalt substrate comprising:

(a) forming a first pattern in said substrate using a first template;

(b) placing a first pre-formed thermally settable sheet on said substrate;

(c) heating said sheet in situ to a temperature sufficient for said sheet to adhere to said substrate in a configuration conforming to said first pattern; and

(d) stamping said thermoplastic using a second template to cause said thermoplastic to more precisely conform to said first pattern.

37. The method as defined in claim 36, wherein said first template and said second template are formed from a plurality of elongated elements defining said first pattern, and wherein said elongated elements in said second template are slightly smaller in diameter than said elongated elements in said first template.

38. The method as defined in claim 37, wherein said elongated elements in said second template are approximately ¼

inches in diameter and said elongated elements in said first template are approximately ⅜

inches in diameter.

39. The method as defined in claim 36, wherein said thermoplastic material is coated on said asphalt surface in a thickness between 150-250 mil.

40. The method as defined in claim 39, wherein said thermoplastic material is coated on said asphalt surface in a thickness between 175-225 mil

41. The method as defined in claim 39, further comprising applying a particulate bond breaker to said thermoplastic prior to said stamping, wherein said stamping impregnates said bond breaker in said thermoplastic.

42. The method as defined in claim 41, wherein said particulate bond breaker is sand.

43. The method as defined in claim 42, wherein sand has an aggregate size exceeding 120 mil.

44. The method as defined in claim 36, comprising allowing said thermoplastic to partially cool after said heating and prior to said stamping said thermoplastic using said second template.