Hydrogenated copolymer and composition containing the same

• US 20080194716A1
• Filed: 04/01/2008
• Published: 08/14/2008
• Est. Priority Date: 06/27/2002
• Status: Active Grant

• Current Assignee: Asahi Kasei Chemicals Corporation (Asahi Kasei Corporation)
• Original Assignee: Asahi Kasei Chemicals Corporation (Asahi Kasei Corporation)
• Inventors: Shiraki, Toshinori, Takayama, Shigeki, Suzuki, Katsumi, Sasaki, Shigeru, Sasagawa, Masahiro, Hisasue, Takahiro, Moritou, Kazuo
• Granted Patent: US 7,960,481 B2
• Time in Patent Office: Days
• US Class Current: 521/139
• CPC Class Codes: C08F 297/04 polymerising vinyl aromatic monomers and conjugated dienes
• CPC Class Codes: C08F 8/04 Reduction, e.g. hydrogenation

Abstract

A hydrogenated copolymer obtained by hydrogenating an unhydrogenated copolymer comprising conjugated diene monomer units and vinyl aromatic monomer units, the hydrogenated copolymer containing at least one hydrogenated copolymer block (B) which is obtained by hydrogenating an unhydrogenated random copolymer block comprised of conjugated diene monomer units and vinyl aromatic monomer units, wherein the hydrogenated copolymer has the following characteristics: the hydrogenated copolymer has a content of the vinyl aromatic monomer units of from more than 40% by weight to less than 95% by weight; at least one peak of loss tangent (tan δ) is observed at −10 to 80° C. in a dynamic viscoelastic spectrum obtained with respect to the hydrogenated copolymer; and substantially no crystallization peak ascribed to the copolymer block (B) is observed at −20 to 80° C. in a differential scanning calorimetry (DSC) chart obtained with respect to the hydrogenated copolymer.

Claims

1. a second-order modified, hydrogenated copolymer obtained:

by reacting a first-order modified, hydrogenated copolymer with a second-order modifier,

said first-order modified, hydrogenated copolymer comprising a hydrogenated copolymer and a functional group-containing first-order modifier group bonded to said hydrogenated copolymer,

said second-order modifier having a functional group which is reactive to said functional group of said first-order modifier group of said first-order modified, hydrogenated copolymer,

said hydrogenated copolymer being obtained by hydrogenating an unhydrogenated copolymer comprising conjugated diene monomer units and vinyl aromatic monomer units, said hydrogenated copolymer comprising;

at least one polymer block selected from the group consisting of a polymer block (A) of vinyl aromatic monomer units, and a hydrogenated polymer block (C) which is obtained by hydrogenating an unhydrogenated polymer block of conjugated diene monomer units, said unhydrogenated polymer block of conjugated diene monomer units having a vinyl bond content of less than 30%, and

at least one hydrogenated copolymer block (B) which is obtained by hydrogenating an unhydrogenated random copolymer block comprised of conjugated diene monomer units and vinyl aromatic monomer units, said unhydrogenated random copolymer block having a vinyl bond content of 60% or less as measured with respect to the conjugated diene monomer units in said unhydrogenated random copolymer block,

wherein, when said hydrogenated copolymer contains no hydrogenated polymer block (C), said hydrogenated copolymer contains at least two polymer blocks (A),

said hydrogenated copolymer having the following characteristics (1) to (6);

(1) said hydrogenated copolymer has a content of said vinyl aromatic monomer units of from more than 40% by weight to less than 95% by weight, based on the weight of said hydrogenated copolymer,

(2) said hydrogenated copolymer has a content of said polymer block (A) of 0 to 60% by weight, based on the weight of said hydrogenated copolymer,

(3) said hydrogenated copolymer has a weight average molecular weight of from 30,000 to 1,000,000,

(4) said hydrogenated copolymer has a hydrogenation ratio of 75% or more, as measured with respect to the double bonds in said conjugated diene monomer units,

(5) at least one peak of loss tangent (tan δ

) is observed at −

10 to 80°

C. in a dynamic viscoelastic spectrum obtained with respect to said hydrogenated copolymer, and

(6) when said hydrogenated copolymer contains no hydrogenated polymer block (C), substantially no crystallization peak ascribed to said at least one hydrogenated copolymer block (B) is observed at −

20 to 80°

C. in a differential scanning calorimetry (DSC) chart obtained with respect to said hydrogenated copolymer.

2. The second-order modified, hydrogenated copolymer according to claim 1, wherein said functional group of said second-order modifier comprises at least one member selected from the group consisting of a hydroxyl group, a carboxyl group, an acid anhydride group, an isocyanate group, an epoxy group, a silanol group and an alkoxysilane group.

3. The second-order modified, hydrogenated copolymer according to claim 1, which is a foam.

4. A crosslinked, second-order modified, hydrogenated copolymer obtained by subjecting the second-order modified, hydrogenated copolymer of claim 1 to a crosslinking reaction in the presence of a crosslinking agent.

5. A second-order modified, hydrogenated copolymer composition comprising:

1 to 99 parts by weight, relative to 100 parts by weight of the total of components (a-2) and (b), of (a-2) the second-order modified, hydrogenated copolymer of claim 1, and

99 to 1 part by weight, relative to 100 parts by weight of the total of components (a-2) and (b), of (b) at least one polymer selected from the group consisting of a thermoplastic resin other than the second-order modified, hydrogenated copolymer (a-2) and a rubbery polymer other than the second-order modified, hydrogenated copolymer (a-2).

6. The second-order modified, hydrogenated copolymer composition according to claim 5, which is a foam.

7. A crosslinked, second-order modified, hydrogenated copolymer composition obtained by subjecting the second-order modified, hydrogenated copolymer composition of claim 5 to a crosslinking reaction in the presence of a crosslinking agent.

8. An adhesive composition comprising:

100 parts by weight of the second-order modified, hydrogenated copolymer (a-2) of claim 1, and

20 to 400 parts by weight of a tackifier (n).

9. An asphalt composition comprising:

0.5 to 50 parts by weight of the second-order modified, hydrogenated copolymer (a-2) of claim 1, and

100 parts by weight of an asphalt (o).