Plenum Cable Flame Retardant Layer/Component with Excellent Aging Properties

• US 20080251273A1
• Filed: 03/03/2006
• Published: 10/16/2008
• Est. Priority Date: 03/03/2005
• Status: Abandoned Application

• Current Assignee: Union Carbide Chemicals & Plastics Technology LLC (Dow, Inc.)
• Original Assignee: Union Carbide Chemicals & Plastics Technology LLC (Dow, Inc.)
• Inventors: Jow, Jinder, Brown, Geoffrey D., Cogen, Jeffrey M., Bolz, Kurt A.
• Application Number:
  US11/817,326
• Publication Number:
  US 20080251273A1
• Time in Patent Office: Days
• US Class Current: 174/113R
• CPC Class Codes: H01B 7/295 using material resistant to flame

Abstract

The present invention is a plenum cable component with excellent fire retardant and aging properties. The plenum cable component is prepared from a polyolefin-based composition, containing an olefinic polymer and a surface treated metal hydroxide. Depending upon the surface treatment, the composition may comprise other components. The present invention is also a method for selecting a composition for preparing the plenum cable component as a separator and a method for preparing a communications cable therefrom.

Claims

1. A plenum cable component prepared from a polyolefin-based composition comprising:

a. an olefinic polymer and

b. a metal hydroxide being surface treated with a phosphorous-based composition,

wherein a test specimen prepared from the polyolefin-based composition having a non-aged dissipation factor less than or equal to about 0.006 and an aged dissipation factor less than about 0.009, wherein the dissipation factors being measured at 1.0 MHz, and wherein the aged dissipation factor being measured on an aged test specimen subjected, for two weeks, to a temperature of 90 degrees Fahrenheit and a relative humidity of 90 percent.

2. The plenum cable component prepared according to claim 1 wherein the olefinic polymer having a maleic anhydride graft

3. The plenum cable component prepared according to claim 1 further comprising a nanoclay.

9. The plenum cable component prepared according to claim 1, 4, or 8 wherein the non-aged dissipation factor and the aged dissipation factor being less than about 0.003.

10. The plenum cable component prepared according to claim 1, 4, or 8 wherein the aged dissipation factor ≦

(1.50×

the non-aged dissipation factor).

11. The plenum cable component prepared according to claim 1, 4, or 8 wherein the olefinic polymer of the polyolefin-based composition being substantially halogen free.

12. The plenum cable, component prepared according to claim 1, 4, or 8 wherein the polyolefin-based composition further comprises a silicon polymer.

13. A communication cable comprising:

a. a plurality of twisted pair conductors, each of the twisted pair conductors including a pair of individually insulated metal conductors that are twisted together to form one of the plurality of twisted pair conductors;

b. a separator

(i) being prepared according to any of claims 1-12 and

(ii) having a plurality of outwardly protruding projections angularly spaced about a core, the plurality of outwardly protruding projections protruding radially from the core and defining regions between adjacent ones of the outwardly protruding projections within each of which one of the plurality of twisted pair conductors is contained; and

c. a communication cable jacket enclosing the plurality of twisted pair conductors separated by the plurality of outwardly protruding projections of the separator,

wherein the communication cable passes the requirements of NFPA-262;

4. A plenum cable component prepared from a polyolefin-based composition comprising:

a. an olefinic polymer having a maleic anhydride graft and

b. a metal hydroxide being surface treated,

wherein a test specimen prepared from the polyolefin-based composition having a, non-aged dissipation factor less than or equal to about 0.006 and an aged dissipation factor less than about 0.009,

wherein the dissipation factors being measured at 1.0 MHz, and

wherein the aged dissipation factor being measured on an aged test specimen subjected, for two weeks, to a temperature of 90 degrees Fahrenheit and a relative humidity of 90 percent.

5. The plenum cable component prepared according to claim 4 wherein the polyolefin-based composition being substantially-free of nanoclays.

6. The plenum cable component prepared according to claim 4 wherein the polyolefin-based composition being free of nanoclays.

7. The plenum cable component prepared according to claim 4 wherein the surface treatment being selected from the group consisting of silane-based and oleic acid-based treating agents.

8. A plenum cable component prepared from a polyolefin-based composition comprising:

a. an olefinic polymer,

b. an olefinic polymer having a maleic anhydride graft, and

c. a metal hydroxide being surface treated,

wherein a test specimen prepared from the polyolefin-based composition having a non-aged dissipation factor less than or equal to about 0.006 and an aged dissipation factor less than about 0.009,

wherein the dissipation factors being measured at 1.0 MHz, and

wherein the aged dissipation factor being measured on an aged test specimen subjected, for two weeks, to a temperature of 90 degrees Fahrenheit and a relative humidity of 90 percent.