REVERSIBLE THERMOSENSITIVE RECORDING MATERIAL, IC CARD, MAGNETIC CARD AND METHOD FOR PRODUCING REVERSIBLE THERMOSENSITIVE RECORDING MATERIAL

• US 20090029854A1
• Filed: 07/23/2008
• Published: 01/29/2009
• Est. Priority Date: 07/24/2007
• Status: Active Grant

• Current Assignee: Ricoh Company Limited
• Original Assignee: Ricoh Company Limited
• Inventors: Arai, Satoshi, Maruyama, Jun
• Granted Patent: US 8,148,299 B2
• Time in Patent Office: Days
• US Class Current: 503/214
• CPC Class Codes: B41M 2205/04 Direct thermal recording [DTR]
• CPC Class Codes: B41M 2205/40 Cover layers; Layers separated from substrate by imaging layer; Protective layers; Layers applied before imaging protective layers applied after imaging B41M7/00
• CPC Class Codes: B41M 5/305 with reversible electron-donor electron-acceptor compositions
• CPC Class Codes: B41M 5/426 characterised by inorganic compounds, e.g. metals, metal salts, metal complexes
• CPC Class Codes: B41M 5/44 characterised by the macromolecular compounds

Abstract

A reversible thermosensitive recording material including a support, a reversible thermosensitive recording layer, and a gas barrier layer, the reversible thermosensitive recording layer and gas barrier layer being laid over the support, wherein the reversible thermosensitive recording layer is formed of a reversible thermosensitive composition containing a mixture of an electron-accepting compound and an electron-donating color-forming compound whose color-developed state varies depending upon at least one of a heating temperature and a cooling rate after heating, and wherein the gas barrier layer contains an inorganic layered compound and a gas barrier resin which is at least one selected from the group consisting of polyvinyl alcohol polymers and ethylene-vinyl alcohol copolymers.

Claims

1. A reversible thermosensitive recording material comprising:

a support,

a reversible thermosensitive recording layer, and

a gas barrier layer,

the reversible thermosensitive recording layer and gas barrier layer being laid over the support,

wherein the reversible thermosensitive recording layer is formed of a reversible thermosensitive composition containing a mixture of an electron-accepting compound and an electron-donating color-forming compound whose color-developed state varies depending upon at least one of a heating temperature and a cooling rate after heating, and

wherein the gas barrier layer contains an inorganic layered compound and a gas barrier resin which is at least one selected from the group consisting of polyvinyl alcohol polymers and ethylene-vinyl alcohol copolymers.

2. The reversible thermosensitive recording material according to claim 1, wherein the inorganic layered compound is at least one selected from the group consisting of kaolinite minerals, antigorite minerals, smectite minerals, vermiculite minerals and mica minerals.

3. The reversible thermosensitive recording material according to claim 1, wherein the inorganic layered compound is a synthetic product of a swelling clay mineral.

4. The reversible thermosensitive recording material according to claim 1, wherein the mass ratio of the gas barrier resin to the inorganic layered compound in the gas barrier layer is in the range of 30:

70 to 99;

1.

5. The reversible thermosensitive recording material according to claim 1, wherein the length and the width of the inorganic layered compound are in the range of 5 nm to 5,000 nm each, and the thickness of the inorganic layered compound is 1/10 to 1/10,000 of the length.

6. The reversible thermosensitive recording material according to claim 1, wherein the inorganic layered compound comprises an ion of at least one selected from the group consisting of alkali metals and alkaline earth metals.

7. The reversible thermosensitive recording material according to claim 1, wherein the ethylene-vinyl alcohol copolymer contains an ethylene component by 20 mol % to 60 mol %, the saponification degree of a vinyl acetate component of the ethylene-vinyl alcohol copolymer is 95 mol % or more, and the ethylene-vinyl alcohol copolymer is insoluble in water.

8. The reversible thermosensitive recording material according to claim 1, wherein the gas barrier layer further comprises an adhesiveness improver for improving its adhesiveness to other layers adjacent thereto.

9. The reversible thermosensitive recording material according to claim 8, wherein the adhesiveness improver contains at least one selected from the group consisting of silane coupling agents, isocyanate compounds, aziridine compounds and carbodiimide compounds.

10. The reversible thermosensitive recording material according to claim 1, wherein the gas barrier layer is a layer obtained by mixing the inorganic layered compound into a solution of the gas barrier resin and dispersing the inorganic layered compound under a pressure of 1 MPa to 100 MPa to prepare a resin composition, and forming the resin composition into a film and drying the resin composition.

11. The reversible thermosensitive recording material according to claim 1, wherein the gas barrier layer has a thickness of 0.1 μ

m to 5.0 μ

m.

12. The reversible thermosensitive recording material according to claim 1, further comprising at least one intermediate layer between the reversible thermosensitive recording layer and the gas barrier layer so as to improve adhesiveness between the reversible thermosensitive recording layer and the gas barrier layer.

13. The reversible thermosensitive recording material according to claim 12, wherein the intermediate layer contains an ester polyol resin.

14. The reversible thermosensitive recording material according to claim 1, further comprising at least one undercoat layer between the support and the reversible thermosensitive recording layer.

15. An IC card comprising:

an IC chip, and

a reversible thermosensitive recording material which comprises a support in which the IC chip is provided, a reversible thermosensitive recording layer, and a gas barrier layer,

the reversible thermosensitive recording layer and gas barrier layer being laid over the support,

wherein the reversible thermosensitive recording layer is formed of a reversible thermosensitive composition containing a mixture of an electron-accepting compound and an electron-donating color-forming compound whose color-developed state varies depending upon at least one of a heating temperature and a cooling rate after heating, and

wherein the gas barrier layer contains an inorganic layered compound and a gas barrier resin which is at least one selected from the group consisting of polyvinyl alcohol polymers and ethylene-vinyl alcohol copolymers.

16. A method for producing a reversible thermosensitive recording material, comprising:

forming a reversible thermosensitive recording layer by coating a support with a reversible thermosensitive composition containing a mixture of an electron-accepting compound and an electron-donating color-forming compound whose color-developed state varies depending upon at least one of a heating temperature and a cooling rate after heating, and

forming a gas barrier layer by coating the formed reversible thermosensitive recording layer with a gas barrier resin mixed solution containing an inorganic layered compound and a gas barrier resin which is at least one selected from the group consisting of polyvinyl alcohol polymers and ethylene-vinyl alcohol copolymers.

17. The method according to claim 16, wherein the gas barrier resin mixed solution is prepared by dispersing the inorganic layered compound in a solution containing the gas barrier resin under a pressure of 1 MPa to 100 MPa.