DIFFUSION-HARDENED MEDICAL IMPLANT

• US 20090074836A1
• Filed: 10/02/2008
• Published: 03/19/2009
• Est. Priority Date: 12/15/2005
• Status: Active Grant

• Current Assignee: Smith & Nephew Incorporated (Smith & Nephew PLC)
• Original Assignee: Smith & Nephew Incorporated (Smith & Nephew PLC)
• Inventors: Jani, Shilesh C., Pawar, Vivek, Weaver, Carolyn
• Granted Patent: US 7,968,209 B2
• Time in Patent Office: Days
• US Class Current: 424/423
• CPC Class Codes: A61F 2/28 Bones joints A61F2/30
• CPC Class Codes: A61F 2/30767 Special external or bone-contacting surface, e.g. coating for improving bone ingrowth
• CPC Class Codes: A61F 2/3094 Designing or manufacturing processes
• CPC Class Codes: A61F 2/32 for the hip
• CPC Class Codes: A61F 2/38 for elbows or knees
• CPC Class Codes: A61F 2/44 for the spine, e.g. vertebrae, spinal discs
• CPC Class Codes: A61F 2002/30016 differing in hardness, e.g. Vickers, Shore, Brinell
• CPC Class Codes: A61F 2002/30922 Hardened surfaces
• CPC Class Codes: A61F 2002/30929 having at least two superposed coatings
• CPC Class Codes: A61F 2210/0076 multilayered, e.g. laminated structures
• CPC Class Codes: A61F 2250/0019 differing in hardness, e.g. Vickers, Shore, Brinell
• CPC Class Codes: A61F 2250/0041 differing in wear resistance
• CPC Class Codes: A61F 2310/00017 Iron- or Fe-based alloys, e.g. stainless steel
• CPC Class Codes: A61F 2310/00023 Titanium or titanium-based alloys, e.g. Ti-Ni alloys
• CPC Class Codes: A61F 2310/00029 Cobalt-based alloys, e.g. Co-Cr alloys or Vitallium
• CPC Class Codes: A61F 2310/00089 Zirconium or Zr-based alloys
• CPC Class Codes: A61F 2310/00101 Molybdenum or Mo-based alloys
• CPC Class Codes: A61F 2310/00485 Coating made of zirconium or Zr-based alloys
• CPC Class Codes: A61F 2310/00592 Coating or prosthesis-covering structure made of ceramics or of ceramic-like compounds
• CPC Class Codes: A61F 2310/00598 Coating or prosthesis-covering structure made of compounds based on metal oxides or hydroxides
• CPC Class Codes: A61F 2310/00856 : Coating or prosthesis-covering structure made of compounds based on metal nitrides
• CPC Class Codes: A61L 2400/00 : Materials characterised by their function or physical properties
• CPC Class Codes: A61L 27/045 : Cobalt or cobalt alloys
• CPC Class Codes: A61L 27/047 : Other specific metals or alloys not covered by A61L27/042 - A61L27/045 or A61L27/06
• CPC Class Codes: A61L 27/06 : Titanium or titanium alloys
• CPC Class Codes: A61L 27/10 : Ceramics or glasses
• CPC Class Codes: A61L 27/30 : Inorganic materials
• CPC Class Codes: A61L 27/50 : Materials characterised by their function or physical properties , e.g. injectable or lubricating compositions, shape-memory materials, surface modified materials
• CPC Class Codes: C23C 8/12 : using elemental oxygen or ozone
• CPC Class Codes: C23C 8/80 : After-treatment
• CPC Class Codes: Y10T 428/12611 : Oxide-containing component

Abstract

The present invention relates to a new composition and medical implant made therefrom, the composition comprising a thick diffusion hardened zone, and preferably further comprising a ceramic layer. The present invention relates to orthopedic implants comprising the new composition, methods of making the new composition, and methods of making orthopedic implants comprising the new composition.

Claims

1-79. -79. (canceled)

80. A medical implant comprising:

(a) a first implant portion, said first implant portion having a bearing surface;

(b) a second implant portion, said second implant portion having a bearing surface;

(c) wherein the bearing surface of said first implant portion and the bearing surface of said second implant portion each have a size and shape to engage or cooperate with one another;

(d) wherein one or both of the two portions of the medical implant comprises a biocompatible alloy having an elastic modulus less than 200 GPa; and

,

(e) wherein the difference in radius of the mating portions is greater than about 50 microns.

81. The medical implant of claim 80, wherein one or both of said first implant portion and said second implant portion further comprises:

a substrate;

a diffusion hardened zone in contact with said substrate, said diffusion hardened zone comprising a diffusion hardening species, said diffusion hardened zone having a thickness of greater than 2 microns; and

,

a substantially defect-free ceramic layer in contact with said diffusion hardened zone and comprising a surface of said medical implant, said ceramic layer ranging in thickness from 0.1 to 25 microns; and

,

wherein the total thickness of the ceramic layer and the diffusion hardened zone is 5 microns or greater.

82. The medical implant of claim 81, wherein one or both of said first implant portion and said second implant portion further comprises:

the ceramic layer comprises a secondary phase; and

,

the diffusion hardened zone has a layered structure comprising at least two distinct layers under metallographic analysis, the layered structure characterized by;

a first layer directly below the ceramic layer;

an interface between the first layer and the ceramic layer; and

;

a second layer directly below the first layer.

83. The medical implant of claim 80, wherein one or both of said first implant portion and said second implant portion further comprises:

a substrate;

a diffusion hardened zone in contact with said substrate, said diffusion hardened zone comprising a diffusion hardening species, said diffusion hardened zone having a thickness of greater than 5 microns; and

,

wherein the diffusion hardened zone has a layered structure comprising at least two distinct layers under metallographic analysis, said layered structure characterized by;

a first layer on a surface of the implant;

a second layer directly below said first layer; and

,

said diffusion hardened zone having a concentration of diffusion hardening species which decreases in the direction of the substrate, said decrease of concentration of diffusion hardening species being defined by a function selected from the group consisting of an error function, an exponential function, a near uniform distribution function, and any sequential combination thereof.

84. The medical implant of claim 80, wherein one or both of said first implant portion and said second implant portion further comprises:

a substrate;

a diffusion hardened zone in contact with said substrate, said diffusion hardened zone comprising a diffusion hardening species, said diffusion hardened zone having a thickness of greater than 2 microns; and

,

a substantially defect-free ceramic layer in contact with said diffusion hardened zone and comprising a surface of said medical implant, said ceramic layer ranging in thickness from 0.1 to 25 microns; and

,

wherein the total thickness of the ceramic layer and the diffusion hardened zone is 5 microns or greater.

85. The medical implant of claim 80, wherein one or both of said first implant portion and said second implant portion further comprises:

the ceramic layer comprises a secondary phase; and

,

the diffusion hardened zone has a layered structure comprising at least two distinct layers under metallographic analysis, the layered structure characterized by;

a first layer directly below the ceramic layer;

an interface between the first layer and the ceramic layer; and

;

a second layer directly below the first layer.