DAMAGE RESISTANT GLASS ARTICLE FOR USE AS A COVER PLATE IN ELECTRONIC DEVICES

• US 20090197048A1
• Filed: 02/05/2009
• Published: 08/06/2009
• Est. Priority Date: 02/05/2008
• Status: Abandoned Application

• Current Assignee: Corning Incorporated
• Original Assignee: Corning Incorporated
• Inventors: Baca, Adra Smith, Sabia, Robert, Amin, Jaymin, Beall, Lorrie Foley, Bellman, Robert Alan, Ouyang, Mike Xu
• Application Number:
  US12/366,267
• Publication Number:
  US 20090197048A1
• Time in Patent Office: Days
• US Class Current: 428/142
• CPC Class Codes: C03C 17/30 with silicon-containing compounds
• CPC Class Codes: C03C 17/42 at least one coating of an organic material and at least one non-metal coating
• CPC Class Codes: C03C 21/002 to perform ion-exchange between alkali ions C03C21/005 takes precedence
• CPC Class Codes: C03C 2217/42 consisting of particles only
• CPC Class Codes: C03C 2217/732 made of a single layer
• CPC Class Codes: C03C 2217/75 Hydrophilic and oleophilic coatings
• CPC Class Codes: C03C 2217/76 Hydrophobic and oleophobic coatings
• CPC Class Codes: C03C 2217/77 Coatings having a rough surface
• CPC Class Codes: C03C 2218/31 Pre-treatment
• CPC Class Codes: C03C 3/085 containing an oxide of a divalent metal
• CPC Class Codes: C03C 3/087 containing calcium oxide, e.g. common sheet or container glass
• CPC Class Codes: C03C 3/091 containing aluminium
• CPC Class Codes: Y10T 428/24364 with transparent or protective coating
• CPC Class Codes: Y10T 428/24967 Absolute thicknesses specified
• CPC Class Codes: Y10T 428/266 of base or substrate

Abstract

An alkali aluminosilicate glass article, said alkali aluminosilicate glass having a surface compressive stress of at least about 200 MPa, a surface compressive layer having a depth of at least about 30 μm, a thickness of at least about 0.3 mm and an amphiphobic fluorine-based surface layer chemically bonded to the surface of the glass. In one embodiment the glass has an anti-reflective coating applied to one surface of the glass between the chemically strengthened surface of the glass and the amphiphobic coating. In another embodiment the surface of the chemically strengthened glass is acid treated using a selected acid (e.g., HCL, H₂SO₄, HClO₄, acetic acid and other acids as described) prior to placement of the amphiphobic coating or the anti-reflective coating.

Claims

1. An alkali aluminosilicate glass article comprising a base alkali aluminosilicate glass having a length, a width and a thickness, a surface compressive stress of at least about 200 MPa, a surface compressive layer depth in the range of 20-80 μ

m, and having an amphiphobic fluorine-based surface layer chemically bonded to the surface of the glass article to form a coated glass article,

2. The glass article according to claim 1, wherein the bonded fluorine-based surface layer is selected from the group consisting of:

(1) silica —

OH group terminated active surface sites exchanged with a fluorine-based monomer;

(2) an assembled monolayer of a fluorine-terminating molecular chain;

(3) a thin, fluoro-polymeric coating;

(4) silicon compound of general formula (R_F)_nSiX_4-n, where R_F is a perfluorocarbon moiety, X is selected from the group consisting of a non-fluorine halogen and a C₂-C₆ alkoxy group, and n is in the range of 1-3; and

(5) silica soot particles which have previous derived with or treated to have fluorine termination groups.

3. The glass article according to claim 1, wherein said coated glass article has a sliding angle of less than 10°

for fluid substances placed thereon

4. The alkali aluminosilicate glass article according to claim 1 wherein the glass article further comprises a textured or patterned surface layer between the base glass and the amphiphobic fluorine-based surface layer, said amphiphobic fluorine-based surface layer being bonded to the textured or patterned surface layer and any untextured or unpatterned base glass surface;

and

wherein said textured surface has a roughness in the range of 50 nm to 5 μ

m.

5. The alkali aluminosilicate glass article according to claim 1, wherein the compressive stress is at least about 600 MPa, the depth of surface compressive layer is at least 40 μ

m, and the thickness is in a range from about 0.7 mm up to about 1.1 mm.

6. The alkali aluminosilicate glass article according to claim 1, wherein the glass comprises:

64 mol %≦

SiO₂≦

68 mol %;

12 mol %≦

Na₂O≦

16 mol %;

8 mol %≦

Al₂O₃≦

12 mol %;

0 mol %≦

B₂O₃≦

3 mol %;

2 mol %≦

K₂O≦

5 mol %;

4 mol %≦

MgO≦

6 mol %; and

0 mol %≦

CaO≦

5 mol %,

wherein;

66 mol %≦

SiO₂+B₂O₃+CaO≦

69 mol %;

Na₂O+K₂O+B₂O₃+MgO+CaO+SrO>

10 mol %;

mol %≦

MgO+CaO+SrO≦

8 mol %;

(Na₂O+B₂O₃)—

Al₂O₃≦

2 mol %;

2 mol %≦

Na₂O—

Al₂O₃≦

6 mol %; and

4 mol %≦

(Na₂O+K₂O)—

Al₂O₃≦

10 mol %, and

wherein the glass has a liquidus viscosity of at least 130 kpoise.

7. The alkali aluminosilicate glass article according to claim 1, wherein the glass has an anti-reflective coating thereon and the anti-reflective coating is selected from the group consisting of silica, fused silica, F-doped fused silica, HfO₂, TiO₂, ZrO₂, Y₂O₃, and Gd₂O₃.

8. An alkali aluminosilicate glass article comprising an alkali aluminosilicate glass having a length, a width and a thickness of at least 0.3 mm, a surface compressive stress of at least about 200 MPa, a surface compressive layer depth in the range of 20-70 μ

m in which K ions have replaced Na and/or Li ions in the glass, and having an amphiphobic fluorine-based surface layer chemically bonded to a surface of the glass article;

wherein the outer surface of said glass to a depth of <

50 nm is an acid etched surface depleted of the exchanged K ions prior to application of fluorine-based surface layer to the surface of the glass.

9. The alkali aluminosilicate glass article according to claim 8, wherein the bonded fluorine-based surface layer is based on a compound of formula (R_F)_nSiX_4-n, where R_F is a C₁-C₂₂ alkyl perfluorocarbon, n is an integer in the range of 1-3, and X is a hydrolyzable group that has exchanged with the glass terminal OH groups, and thickness of the fluorine-based surface layer is in the range of 1-10 nm.

10. The alkali aluminosilicate glass article according to claim 8, wherein X is selected from the group consisting of a halogen other than fluorine and an alkoxy group (—

OR), where R is a linear or branched hydrocarbon of 1-6 carbon atoms.

11. The alkali aluminosilicate glass article according to claim 8, wherein the compressive stress is at least 600 MPa, the depth of surface compressive layer prior to treatment is at least 40 μ

m, and the thickness of the glass article is in the of 0.7 mm to 1.1 mm.

12. The alkali aluminosilicate glass article according to claim 8, wherein the glass comprises:

64 mol %≦

SiO₂≦

68 mol %;

12 mol %≦

Na₂O≦

16 mol %;

8 mol %≦

Al₂O₃≦

12 mol %;

0 mol %≦

B₂O₃≦

3 mol %;

2 mol %≦

K₂O≦

5 mol %;

4 mol %≦

MgO≦

6 mol %; and

0 mol %≦

CaO≦

5 mol %,

wherein;

mol %≦

SiO₂+B₂O₃+CaO≦

69 mol %;

Na₂O+K₂O+B₂O₃+MgO+CaO+SrO>

10 mol %;

5 mol %≦

MgO+CaO+SrO≦

8 mol %;

(Na₂O+B₂O₃)—

Al₂O₃≦

2 mol %;

2 mol %≦

Na₂O—

Al₂O₃≦

6 mol %; and

4 mol %≦

(Na₂O+K₂O)—

Al₂O₃≦

10 mol %, and

wherein the glass has a liquidus viscosity of at least 130 kpoise.

13. An alkali aluminosilicate glass article, said article comprising

a glass substrate having a length, a width and a thickness of at least 0.3 mm, a surface compressive stress of at least about 200 MPa, a surface compressive layer having a depth of at least between about 20-70 μ

m;

an anti-reflective coating on one surface of said glass; and

an amphiphobic fluorine-based surface layer chemically bonded to the surface of the anti-reflective coating

wherein the glass comprises;

64 mol %≦

SiO₂≦

68 mol %;

12 mol %≦

Na₂O≦

16 mol %;

8 mol %≦

Al₂O₃≦

12 mol %;

0 mol %≦

B₂O₃≦

3 mol %;

2 mol %≦

K₂O≦

5 mol %;

4 mol %≦

MgO≦

6 mol %; and

0 mol %≦

CaO≦

5 mol %,

wherein;

66 mol %≦

SiO₂+B₂O₃+CaO≦

69 mol %;

Na₂O+K₂O+B₂O₃+MgO+CaO+SrO>

10 mol %;

5 mol %≦

MgO+CaO+SrO≦

8 mol %;

(Na₂O+B₂O₃)—

Al₂O₃≦

2 mol %;

2 mol %≦

Na₂O—

Al₂O₃≦

6 mol %; and

4 mol %≦

(Na₂O+K₂O)—

Al₂O₃≦

10 mol %, and

wherein the glass has a liquidus viscosity of at least 130 kpoise.

14. The alkali aluminosilicate glass article according to claim 13, wherein the anti-reflective coating is selected from the group consisting of silica, fused silica, F-doped fused silica and MgF₂;

and

wherein the thickness of the antireflective coating is in the range of anti-reflective coating is in the range of 10-60 μ

m.

15. The alkali aluminosilicate glass article according to claim 13, wherein the anti-reflective coating is selected from the group consisting of HfO₂, TiO₂, ZrO₂, Y₂O₃, and Gd₂O₃, and the thickness of the antireflective coating is in the range of anti-reflective coating is in the range of 10-60 μ

m.

16. The alkali aluminosilicate glass article according to claim 13, wherein the bonded fluorine-based surface layer is selected or formula (R_F)_nSiX_4-n, where R_F from the group consisting of where R_F is a C₁-C₂₂ alkyl perfluorocarbon, n is an integer in the range of 1-3, and X is a hydrolyzable group that can be exchanged with the glass terminal OH groups.

17. The alkali aluminosilicate glass article according to claim 13, wherein X is selected from the group consisting of a halogen other than fluorine and an alkoxy group (—

OR), where R is a linear or branched hydrocarbon of 1-6 carbon atoms.

18. The alkali aluminosilicate glass article according to claim 13, wherein the compressive stress is at least about 600 MPa, the depth of surface compressive layer, prior to treatment is at least 40 μ

m, and the thickness is in a range from about 0.7 mm up to about 1.1 mm.

19. A method of making coated alkali aluminosilicate glass article anti-fingerprint and anti-smudge characteristics, said method comprising the steps of:

providing an alkali aluminosilicate glass substrate having a length, width and thickness;

chemically strengthening the surface of the glass substrate to a depth in the range of 20-80 μ

m;

machining or otherwise finishing the glass surfaces;

ultrasonically cleaning the glass surfaces;

optionally, acid washing at least one surface of the glass using a solution of a strong acid,

plasma cleaning the at least one surface of the glass using O₂;

optionally, coating the class with an anti-reflective coating;

coating cleaned glass surface or the anti-reflecting coating surface with an amphiphobic coating,

curing the amphiphobic coating for a selected time at a selected temperature and a selected humidity; and

inspecting the coated alkali aluminosilicate glass article.

20. The method according to claim 19, wherein coating the glass with an anti-reflective coating means coating with an anti-reflective coating material selected from the group consisting of silica, fused silica and F-doped fused silica.

21. The method according to claim 19, wherein coating the glass with an anti-reflective coating means coating with an anti-reflective coating material selected from the group consisting of HfO₂, TiO₂, ZrO₂, Y₂O₃, and Gd₂O₃.

22. The method according to claim 19, wherein coating the glass with an amphiphobic coating means coating with an amphiphobic coating material of formula (R_F)_nSiX_4-n, where R_F from the group consisting of where R_F is a C₁-C₂₂ alkyl perfluorocarbon, n is an integer in the range of 1-3, and X is a hydrolyzable group that can be exchanged with the glass terminal OH groups;

and

wherein X is selected from the group consisting of a halogen other than fluorine and an alkoxy group (—

OR), where R is a linear or branched hydrocarbon of 1-6 carbon atoms.