REFLECTION PLATE AND LIGHT EMITTING DEVICE

• US 20090212684A1
• Filed: 02/19/2009
• Published: 08/27/2009
• Est. Priority Date: 02/25/2008
• Status: Abandoned Application

• Current Assignee: Sumitomo Chemical Company Limited
• Original Assignee: Sumitomo Chemical Company Limited
• Inventors: HARADA, Hiroshi, SAITO, Shintaro, IWASE, Sadanobu
• Application Number:
  US12/388,821
• Publication Number:
  US 20090212684A1
• Time in Patent Office: Days
• US Class Current: 313/498
• CPC Class Codes: G02B 5/0808 having a single reflecting layer G02B5/0883, G02B5/0891 take precedence

Abstract

The present invention provides a reflection plate made of a resin composition comprising a liquid crystalline polyester, a titanium oxide filler and a silica-based filler containing 85% by weight or more of silicon oxide, wherein the resin composition contains the titanium oxide filler in the amount of from 5 to 80 parts by weight and the silica-based filler in the amount of from 0.01 to 20 parts by weight on the basis of 100 parts by weight of the liquid crystalline polyester. The reflection plate has an excellent reflectance, especially to light in a visible range, while maintaining excellent heat resistance of the liquid crystalline polyester.

Claims

1. A reflection plate made of a resin composition comprising:

(A) a liquid crystalline polyester,

(B) a titanium oxide filler, and

(C) a silica-based filler containing 85% by weight or more of silicon oxide,

wherein the resin composition contains the titanium oxide filler in the amount of from 5 to 80 parts by weight and the silica-based filler in the amount of from 0.01 to 20 parts by weight on the basis of 100 parts by weight of the liquid crystalline polyester.

2. The reflection plate according to claim 1, wherein the silica-based filler is in the shape of substantial particle.

3. The reflection plate according to claim 1, wherein the silica-based filler and the titanium oxide are in the shape of substantial particle.

4. The reflection plate according to claim 2, further comprising:

(D) a fiber-shaped or whisker-shaped inorganic filler other than the titanium oxide filler and the silica-based filler.

5. The reflection plate according to claim 4, wherein the resin composition contains the inorganic filler in the amount of from 5 to 100 parts by weight on the basis of 100 parts by weight of the total amount of the liquid crystalline polyester, the titanium oxide filler and the silica-based filler.

6. The reflection plate according to claim 1, which has a thin wall section having a thickness of 0.01 to 3 mm.

7. The reflection plate according to claim 1, wherein the reflection plate possesses 70% or more of reflectance to light having a wavelength of 460 nm when measured by method A for the measurement of an entire light reflectance in accordance with JIS K7105-1981.

9. A light emitting device having the reflection plate according to claim 1 and a light emitting element.

10. The light emitting device according to claim 9, wherein the light emitting element is a light emitting diode.

8. A method for producing a reflection plate, the method comprising the steps of:

mixing (A) 100 parts by weight of a liquid crystalline polyester, (B) 5 to 80 parts by weight of a titanium oxide filler and (C) 0.01 to 20 parts by weight of a silica-based filler containing 85% by weight or more of silicon oxide to preparing a resin composition; and

injection-molding the resin composition.