SOLID EXPANDABLE COMPOSITIONS

• US 20090239962A1
• Filed: 03/19/2009
• Published: 09/24/2009
• Est. Priority Date: 09/20/2006
• Status: Abandoned Application

• Current Assignee: Henkel AG & Co KGaA
• Original Assignee: Henkel AG & Co KGaA
• Inventors: Dobashi, Masaaki
• Application Number:
  US12/407,291
• Publication Number:
  US 20090239962A1
• Time in Patent Office: Days
• US Class Current: 521/95
• CPC Class Codes: C08J 2201/024 Preparation or use of a blowing agent concentrate, i.e. masterbatch in a foamable composition
• CPC Class Codes: C08J 2300/104 containing oxygen atoms
• CPC Class Codes: C08J 2351/04 grafted on to rubbers
• CPC Class Codes: C08J 2461/00 Characterised by the use of condensation polymers of aldehydes or ketones; Derivatives of such polymers
• CPC Class Codes: C08J 9/0061 characterized by the use of several polymeric components
• CPC Class Codes: C08J 9/06 by a chemical blowing agent
• CPC Class Codes: C08J 9/10 developing nitrogen , the blowing agent being a compound containing a nitrogen-to-nitrogen bond

Abstract

Solid expandable compositions useful for the manufacture of cavity filler inserts and the like are obtained by combining at least one anhydride-functionalized thermoplastic, at least one amine-functionalized latent curing agent, and at least one latent blowing agent. Such compositions may be formulated so as to provide a highly expanded foam upon heating to activate the blowing agent wherein the foam is resistant to sagging and tolerant of over baking conditions.

Claims

1. A solid expandable composition comprising:

a) at least one anhydride-functionalized thermoplastic;

b) at least one amine-functionalized latent curing agent; and

c) at least one latent blowing agent.

2. The solid expandable composition of claim 1, additionally comprising at least one epoxy-functionalized thermoplastic.

3. The solid expandable composition of claim 1, comprising at least one copolymer comprised of ethylene, maleic anhydride, and at least one monomer selected from the group consisting of vinyl acetate, acrylic acid, methacrylic acid, and C1 to C6 alkyl esters of acrylic acid and methacrylic acid.

4. The solid expandable composition of claim 1, additionally comprising at least one ketimine.

5. The solid expandable composition of claim 1, additionally comprising at least one ethylenically unsaturated crosslinking agent.

6. The solid expandable composition of claim 1, comprising at least one amine-functionalized latent curing agent selected from the group consisting of amine-epoxy adducts.

7. The solid expandable composition of claim 1, comprising at least one amine-functionalized latent curing agent in finely divided form having a melting point of from 105 to 150 degrees C.

8. The solid expandable composition of claim 1, comprising at least one latent blowing agent selected from the group consisting of azo compounds and hydrazide compounds.

9. The solid expandable composition of claim 1, wherein said solid expandable composition is comprised of from 35 to 80 weight percent of one or more anhydride-functionalized thermoplastics.

10. The solid expandable composition of claim 1, wherein said solid expandable composition is comprised of from 0.1 to 5 weight percent of one or more amine-functionalized curing agents.

11. The solid expandable composition of claim 1, wherein said solid expandable composition is comprised of from 5 to 20 weight percent of one or more latent blowing agents.

12. The solid expandable composition of claim 1, additionally comprising at least one phenolic compound and/or at least one phenol-formaldehyde resin.

14. A method of blocking off a hollow cavity of a structural member, said method comprising:

d) positioning a portion of the solid expandable composition of claim 1, optionally in combination with a carrier, within a hollow cavity of a structural member; and

e) heating said portion of the solid expandable composition to a temperature effective to activate said latent blowing agent, thereby causing the solid expandable composition to expand and block off said hollow cavity.

15. A cavity filler insert comprising a carrier in combination with a portion of the solid expandable composition of claim 1.

13. A solid expandable composition comprising:

a) from 35 to 80 weight percent of one or more anhydride-functionalized thermoplastics selected from the group consisting of copolymers of ethylene, maleic anhydride, and one or more comonomers selected from the group consisting of vinyl acetate, acrylic acid, methacrylic acid, and C1 to C6 alkyl esters of acrylic acid and methacrylic acid;

b) from 0.1 to 5 weight percent of one or more amine-epoxy adducts having a melting point of from 105 to 150 degrees C.; and

c) from 5 to 20 weight percent of one or more latent chemical blowing agents selected from the group consisting of azo compounds and hydrazide compounds.