METHOD AND APPARATUS TO COAT OBJECTS WITH PARYLENE AND BORON NITRIDE

• US 20090263581A1
• Filed: 04/16/2008
• Published: 10/22/2009
• Est. Priority Date: 04/16/2008
• Status: Abandoned Application

• Current Assignee: HzO, Inc.
• Original Assignee: Northeast Maritime Institute, Inc.
• Inventors: Dawicki, Angela Michele, Martin, Sidney Edward III, Dawicki, Eric Roger
• Application Number:
  US12/104,080
• Publication Number:
  US 20090263581A1
• Time in Patent Office: Days
• US Class Current: 427/255.395
• CPC Class Codes: C23C 14/0647 Boron nitride
• CPC Class Codes: C23C 14/12 Organic material
• CPC Class Codes: C23C 14/5806 Thermal treatment
• CPC Class Codes: Y10T 428/26 Web or sheet containing structurally defined element or component, the element or component having a specified physical dimension
• CPC Class Codes: Y10T 428/264 Up to 3 mils
• CPC Class Codes: Y10T 428/31544 Addition polymer is perhalogenated
• CPC Class Codes: Y10T 428/31855 Of addition polymer from unsaturated monomers

Abstract

The present inventions relates to an improved and novel Parylene compositions with has improved heat transfer and durability qualities, as well as a methods and apparatus to coat objects with the novel Parylene compositions, and objects coated with the novel Parylene compositions. The novel Parylene composition of the invention comprises Parylene and boron nitride. The invention also includes objects coated with at least one polymer coat and a boron nitride coat.

Claims

1. A Parylene composition, comprising Parylene and boron nitride.

2. The Parylene composition of claim 1, wherein the Parylene and boron nitride are inter-dispersed.

3. The Parylene composition of claim 1, wherein the Parylene is selected from a group consisting of Parylene D, Parylene C, Parylene N and Parylene HT®

.

4. The Parylene composition of claim 3, wherein the Parylene is Parylene C.

5. The Parylene composition of claim 1, wherein the boron nitride has a hexagonal plate structure.

6. The Parylene composition of claim 1, which has greater thermal conductivity than the Parylene alone.

8. The Parylene composition of claim 1, which has a greater hardness than the Parylene alone.

10. The Parylene composition of claim 1, wherein the weight of boron nitride to the total weight of Parylene and boron nitride is less then about 80%.

28. A Parylene-coated object, which comprises an object coated with the composition of claim 1.

29. The Parylene-coated object of claim 28, wherein the boron nitride is inter-dispersed the Parylene in the coating.

30. The Parylene-coated object of claim 28, wherein the object is one that benefits from thermal conductivity through the Parylene coating.

31. The Parylene-coated objected of claim 30, wherein the object is generates heat or absorbs heat.

32. The Parylene-coated object of claim 31, wherein the object is selected from the group consisting of electronics equipment, heat packs, refrigeration devices, heaters, and drilling equipment.

33. The Parylene-coated object of claim 28, wherein the object is expected to be subjected to harsh physical impact during its lifetime.

34. The Parylene-coated object of claim 28, wherein the Parylene is selected from the group consisting of Parylene C, Parylene N, Parylene D and Parylene HT®

.

35. The Parylene-coated object of claim 34, wherein the polymer is Parylene C.

36. The Parylene-coated object of claim 28, wherein the coating is about 0.0025 mm to about 0.050 mm thick.

7. The Parylene composition of claim 7, which has greater than about 10% thermal conductivity than the Parylene alone.

9. The Parylene composition of claim 9, which has greater than about 10% hardness than the Parylene alone.

11. A method to apply a coating of Parylene and boron nitride to an object, comprising the steps of:

A. vaporizing Parylene dimers by heating them to about 150 to about 200 degrees C. to form gaseous Parylene dimers;

B. cleaving gaseous Parylene dimers to gaseous Parylene monomers by heating gaseous Parylene dimers to about 650 to about 700 degrees C.;

C. injecting boron nitride into the gaseous Parylene monomers of Step B; and

D. contacting the object to be coated with Parylene with the gaseous Parylene monomers and boron nitride of Step C for sufficient time to deposit coat of Parylene and boron nitride of a final thickness.

12. The method of claim 11, wherein the Parylene is selected from a group consisting of Parylene D, Parylene C, Parylene N and Parylene HT®

.

13. The method of claim 12, wherein the Parylene is Parylene C.

14. The method of claim 11, wherein in Step C, the boron nitride is injected into the gaseous Parylene monomers as a powder.

15. The method of claim 14, wherein the boron nitride powder is between about 18 micron and about 25 micron.

16. The method of claim 11, wherein Step D takes place at about 5 degrees to about 30 degrees C.

17. The method of claim 11, wherein the final thickness of the coat is between about 100 Angstrom to about 3.0 millimeters.

18. The method of claim 11, which has an additional Step E wherein the object to be coated is contacted with a silane composition until the object is coated with silane.

19. The method of claim 11, wherein the object to be coated is selected from the group consisting of electronics equipment, circuit boards, paper, textiles, ceramics, plastics, frozen liquids, batteries, speakers, solid fuel, medical devices, and space suits.

20. The method of claim 11, wherein the object to be coated is one that generates or consumes heat.

21. The method of claim 11, wherein the object to be coated is one that requires a rugged coating.

22. Objects coated by the method of claim 11.

23. An apparatus to apply a coating of a polymer and a powder, comprising

a vaporization chamber;

operably linked to a pyrolysis chamber;

a vacuum chamber and

a connection comprising a T-port operably linking the pyrolysis chamber to the vacuum chamber.

24. The apparatus of claim 23, wherein the connection operably linking the pyrolysis chamber and the vacuum chamber is a means for transmitting gas from the pyrolysis chamber to the vacuum chamber.

25. The apparatus of claim 23, wherein the T-port is operably connected to a means for injecting a powder into the gas transmitted through the connection.

26. The apparatus of claim 23, where the vacuum chamber is comprised of a deposition chamber operably linked to the pyrolysis chamber and a vacuum means.

27. The apparatus of claim 26, wherein the vacuum means is one or more vacuum pumps.

37. A polymer-coated object, which comprises an object coated with at least one coat of a polymer and at least one coat of boron nitride.

38. The polymer-coated object of claim 37, wherein the polymer is selected from the group consisting of polynaphtahlene, diamine, polytetrafluoroethylene, polyimides, silicas, titania, aluminum nitride, and lanthanum hexaboride, Parylene C, Parylene N, Parylene D and Parylene HT®

.

39. The polymer-coated object of claim 38, wherein the polymer is Parylene C.

40. The polymer coated object of claim 37, wherein the boron nitride coat is closer to the object that the polymer coat.

41. The polymer-coated object of claim 37, wherein the polymer coat is closer to the object that the boron nitride coat.

42. The polymer-coated object of claim 37, where in the coatings of boron nitride and polymer are at least about 0.05 mm thick each.

43. The polymer-coated object of claim 37, wherein the object generates heat or absorbs heat.

44. The polymer-coated object of claim 43, wherein the object is selected from the group consisting of cold packs, frozen liquids and gases and heat pumps.

45. The polymer-coated object of claim 37, wherein the object is expected to be subjected to harsh physical impact during its lifetime.