METHOD FOR PRODUCTION OF MODIFIED WATER ABSORBENT RESIN

• US 20090298963A1
• Filed: 12/09/2005
• Published: 12/03/2009
• Est. Priority Date: 12/10/2004
• Status: Abandoned Application

• Current Assignee: Nippon Shokubai Company Limited
• Original Assignee: Nippon Shokubai Company Limited
• Inventors: Flohr, Andreas, Torii, Kazushi, Ikeuchi, Hiroyuki, Matsumoto, Makoto, Mitsukami, Yoshiro, Lindner, Torsten, Iwamura, Taku
• Application Number:
  US11/721,285
• Publication Number:
  US 20090298963A1
• Time in Patent Office: Days
• US Class Current: 522/59
• CPC Class Codes: C08F 20/06 Acrylic acid; Methacrylic acid; Metal salts or ammonium salts thereof
• CPC Class Codes: C08F 8/44 Preparation of metal salts or ammonium salts
• CPC Class Codes: C08J 2300/14 Water soluble or water swellable polymers, e.g. aqueous gels
• CPC Class Codes: C08J 2333/02 Homopolymers or copolymers of acids; Metal or ammonium salts thereof
• CPC Class Codes: C08J 3/28 Treatment by wave energy or particle radiation
• CPC Class Codes: C08L 2666/04 Macromolecular compounds according to groups C08L7/00 - C08L49/00, or C08L55/00 - C08L57/00; Derivatives thereof
• CPC Class Codes: C08L 33/02 Homopolymers or copolymers of acids; Metal or ammonium salts thereof

Abstract

This invention is to provide a method for producing a modified water absorbent resin excelling in water absorbing properties. This invention relates to a method for producing a modified water absorbent resin, which comprises a) mixing a water absorbent resin and a water-soluble radical polymerization initiator or a heat-degradable radical polymerization initiator without addition of an ethylenically unsaturated monomer and b) irradiating the resultant mixture with active energy rays. The method is particularly capable of exalting the absorbency against pressure and the saline flow conductivity.

Claims

1. A method for the production of a modified water absorbent resin, which comprises:

a) mixing a water absorbent resin and a water-soluble radical polymerization initiator without addition of an ethylenically unsaturated monomer and

b) irradiating the resultant mixture with active energy rays.

2. A method according to claim 1, wherein said water-soluble radical polymerization initiator is at least one member selected from the group consisting of persulfates, hydrogen peroxide and water-soluble azo compounds.

5. A method according to claim 1 wherein the amount of said radical polymerization initiator to be added to 100 parts by weight of said water absorbent resin is in the range of 0.01-20 parts by weight.

6. A method according to claim 1, wherein said radical polymerization initiator is mixed in the form of an aqueous solution.

7. A method according to claim 1, wherein the mixture of said water absorbent resin and said radical polymerization initiator is accompanied by further mixture of water in the range of 1-20 parts by weight based on 100 parts by weight of the water absorbent resin.

8. A method according to claim 1, wherein a mixing aid other than water is added at the same time as or prior to the step a).

9. A method according to claim 8, wherein said mixing aid is at least one water-soluble or water-dispersible compound selected from the group consisting of surfactants, water-soluble polymers, hydrophilic organic solvents, water-soluble inorganic compounds, inorganic acids, inorganic acid salts, organic acids, and organic acid salts.

10. A method according to claim 8, wherein said mixing aid is at least one water-soluble or water-dispersible compound selected from the group consisting of polyoxyethylene alkyl ethers, polyethylene glycol, water-soluble polyvalent metals, sodium chloride, ammonium hydrogen sulfate, ammonium sulfate, sulfuric acid, and hydrochloric acid.

11. A method according to claim 8, wherein said mixing aid is added in an amount in the range of 0.01 to 40 parts by weight based on 100 parts by weight of said water absorbent resin.

12. A method according to claim 1, wherein said water absorbent resin has an acid group and a neutralization ratio (mol % of the neutralized acid group in the whole acid group) in the range of 50-75 mol %.

13. A method according to claim 1, wherein said active energy rays are ultraviolet rays.

14. A method according to claim 1, wherein said water absorbent resin is a powdery resin obtained by polymerizing a monomer having acrylic acid (salt) as a main component.

15. A method according to claim 1, wherein said water absorbent resin is obtained by producing a water absorbent resin precursor having a low neutralization ratio, and mixing said water absorbent resin precursor with a base.

16. A method according to claim 1, wherein said water absorbent resin contains particles having diameters in the range of 150-850 μ

m in a ratio in the range of 90-100 wt. %.

17. A method according to claim 1, wherein the absorbency of physiological saline against pressure of 4.83 kPa of said water absorbent resin subsequent to modification is improved not less than 1 g/g comparing with the absorbency against pressure of the resin prior to the modification.

18. A method according to claim 1, wherein the absorbency of physiological saline against pressure of 4.83 kPa of the water absorbent resin subsequent to modification is in the range of 8-40 g/g.

19. A method according to claim 1, wherein the saline flow conductivity of the water absorbent resin subsequent to modification is not less than 10 (10⁻

7·

cm³·

s·

g<sup>−

1</sup>).

3. A method for the production of a modified water absorbent resin, which comprises:

a) mixing a water absorbent resin and a heat-degradable radical polymerization initiator without addition of an ethylenically unsaturated monomer and

b) irradiating the resultant mixture with active energy rays.

4. A method according to claim 3, wherein said heat-degradable radical polymerization initiator is at least one member selected from the group consisting of persulfates, hydrogen peroxide and azo compounds.

20. A powdery modified water absorbent resin to be obtained by polymerizing monomer components including as a main component acrylic acid (salt), characterized by having

(i) saline flow conductivity of not less than 40 (10⁻

7·

cm³·

s·

g<sup>−

1</sup>),

(ii) a solid content of not more than 95%, and

(iii) a residual monomer content of not more than 150 ppm.

21. A powdery modified water absorbent resin according to claim 20, which has free swelling capacity of physiological saline of not less than 25 g/g.

22. A powdery modified water absorbent resin according to claim 20, which has absorbency of physiological saline against pressure of 4.83 kPa of not less than 22 g/g.

23. A method for the production of a modified water absorbent resin, which comprises:

a) mixing a water absorbent resin and a persulfate without addition of an ethylenically unsaturated monomer,

b) adding a mixing aid other than water at the same time as or prior to the step a), and

c) irradiating the resultant mixture with active energy rays.

24. A method for the production of a modified water absorbent resin, which comprises:

a) mixing a water absorbent resin and a persulfate without addition of an ethylenically unsaturated monomer, and

b) irradiating the resultant mixture with active energy rays,

wherein said water absorbent resin has an acid group and a neutralization ratio (mol % of the neutralized acid group in the whole acid group) in the range of 50-75 mol %.

25. A method for the production of a modified water absorbent resin, which comprises:

a) mixing a water absorbent resin and a persulfate without addition of an ethylenically unsaturated monomer,

b) adding a mixing aid other than water at the same time as or prior to the step a), and

c) irradiating the resultant mixture with active energy rays,

wherein said water absorbent resin has an acid group and a neutralization ratio (mol % of the neutralized acid group in the whole acid group) in the range of 50-75 mol %.