SOLID ELECTROLYTIC CAPACITOR AND METHOD FOR PRODUCING SAME

• US 20090303665A1
• Filed: 12/27/2006
• Published: 12/10/2009
• Est. Priority Date: 12/27/2005
• Status: Abandoned Application

• Current Assignee: Murata Manufacturing Co Limited
• Original Assignee: Showa Denko KK
• Inventors: Oohata, Hideki
• Application Number:
  US12/159,523
• Publication Number:
  US 20090303665A1
• Time in Patent Office: Days
• US Class Current: 361/527
• CPC Class Codes: H01G 9/028 Organic semiconducting electrolytes, e.g. TCNQ
• CPC Class Codes: H01G 9/042 characterised by the material H01G11/22 takes precedence
• CPC Class Codes: H01G 9/15 Solid electrolytic capacitors H01G11/00 takes precedence

Abstract

A solid electrolytic capacitor comprising a solid electrolyte comprised of an electroconductive polymer, formed on a metal substrate with a valve action having a dielectric film formed on the surface thereof, characterized in that the dielectric film has a thickness of at least 30 nm, and the solid electrolyte contains 0.1% to 20% by mol, based on the total monomer units constituting the electroconductive polymer, of an anion of an aromatic compound, preferably an aromatic polycyclic compound having an aromatic polycyclic structure as basic skeleton and containing a Brφnsted acid group, as a dopant.

Claims

1. A solid electrolytic capacitor comprising a solid electrolyte comprised of an electroconductive polymer, formed on a metal substrate with a valve action having a dielectric film formed on the surface thereof, characterized in that said dielectric film has a thickness of at least 30 m and said solid electrolyte contains 0.1% to 20% by mol, based on the total monomer units constituting the electroconductive polymer, of an anion of an aromatic compound as dopant.

2. The solid electrolytic capacitor according to claim 1, wherein the solid electrolyte has an electrical conductivity in the range of 0.01 S/cm to 10 S/cm.

3. The solid electrolytic capacitor according to claim 1, wherein the aromatic compound has an aromatic ring structure as basic skeleton selected from p-benzoquinone, o-benzoquinone, 1,2-naphthoquinone, 1,4-naphthoquinone, 2,6-naphthoquinone, 9,10-anthraquinone, 1,4-anthraquinone, 1,2-anthraquinone, 1,4-chrysenequinone, 5,6-chrysenequinone, 6,12-chrysenequinone, acenaphthoquinone, acenaphthenequinone, camphorquinone, 2,3-bornanedion, 9,10-phenanthrenequinone and 2,7-pyrenequinone, and the aromatic compound contains a Brφ

nsted acid group.

4. The solid electrolytic capacitor according to claim 1, wherein the aromatic compound has an anthraquinone skeleton, a 1,4-naphthoquinone skeleton or a 2,6-naphthoquinone skeleton, and contains a sulfonic acid group or a carboxylic acid group.

5. The solid electrolytic capacitor according to claim 1, wherein the electroconductive polymer constituting the solid electrolyte is a polymer having repeating structural units represented by the following general formula [1]:

6. The solid electrolytic capacitor according to claim 1, wherein the electroconductive polymer constituting the solid electrolyte is a polymer having repeating structural units represented by the following general formula [2]:

7. A process for producing a solid electrolytic capacitor comprising:

at least one cycle comprising steps of coating a metal substrate having a valve action, having a dielectric film, formed on the surface of the substrate, with a solution containing an electroconductive polymer-forming monomer, and then drying the thus-formed liquid coating, and

at least one cycle comprising steps of coating the metal substrate having a valve action, having formed thereon the dielectric film, with a solution containing an oxidizing agent, and then drying the thus-formed coating of the oxidizing agent-containing solution,

whereby said monomer is polymerized to form an electroconductive polymer constituting a solid electrolyte;

characterized in that a metal substrate having formed thereon a dielectric film with a thickness of at least 30 nm is used, and a solution containing an anion of an aromatic compound in addition to the oxidizing agent is used as the oxidizing agent-containing solution, to form an electroconductive polymer containing 0.1% to 20% by mol, based on the total monomer units constituting the electroconductive polymer, of the anion of the aromatic compound as a dopant.

8. The process for producing a solid electrolytic capacitor according to claim 7, wherein the aromatic compound has an aromatic ring structure as basic skeleton selected from p-benzoquinone, o-benzoquinone, 1,2-naphthoquinone, 1,4-naphthoquinone, 2,6-naphthoquinone, 9,10-anthraquinone, 1,4-anthraquinone, 1,2-anthraquinone, 1,4-chrysenequinone, 5,6-chrysenequinone, 6,12-chrysenequinone, acenaphthoquinone, acenaphthenequinone, camphorquinone, 2,3-bornanedion, 9,10-phenanthrenequinone and 2,7-pyrenequinone, and the aromatic compound contains a Brφ

nsted acid group.

9. The process for producing a solid electrolytic capacitor according to claim 7, wherein the aromatic compound has an anthraquinone skeleton, a 1,4-naphthoquinone skeleton or a 2,6-naphthoquinone skeleton, and contains a sulfonic acid group or a carboxylic acid group.

10. The process for producing a solid electrolytic capacitor according to claim 7, wherein the electroconductive polymer-forming monomer is a compound represented by the following general formula [3]:

11. The process for producing a solid electrolytic capacitor according to claim 7, wherein the electroconductive polymer-forming monomer is a compound represented by the following general formula [4]: