Glass ribbon producing apparatus and process for producing the same

• US 20090314032A1
• Filed: 10/09/2007
• Published: 12/24/2009
• Est. Priority Date: 10/24/2006
• Status: Abandoned Application

• Current Assignee: Nippon Electric Glass Company Limited
• Original Assignee: Nippon Electric Glass Company Limited
• Inventors: Tomamoto, Masahiro, Oda, Hidetaka
• Application Number:
  US12/311,626
• Publication Number:
  US 20090314032A1
• Time in Patent Office: Days
• US Class Current: 65/29.140
• CPC Class Codes: C03B 17/064 by the overflow downdraw fusion process; Isopipes therefor
• CPC Class Codes: C03B 17/067 combined with thermal conditioning of the sheets

Abstract

A glass ribbon producing apparatus (1) which feeds molten glass (Y) to a forming member (2) and causes the molten glass (Y) to flow downward from the forming member (2) to form a sheet-like glass ribbon (G) includes reheating portion (5) provided on a transport route for the glass ribbon (G) caused to flow downward from the forming member (2), and is configured so that the glass ribbon (G) is reheated by the reheating portion (5) to cause the sheet thickness of the glass ribbon (G) below the reheating portion (5) to be smaller than that of the glass ribbon (G) thereabove.

Claims

1. A glass ribbon producing apparatus which feeds molten glass to a forming member and causes the molten glass to flow downward from the forming member to form a sheet-like glass ribbon, comprising reheating portion provided on a transport route for the glass ribbon caused to flow downward from the forming member,

wherein the reheating portion is constructed to reheat the glass ribbon to cause a sheet thickness of the glass ribbon below the reheating portion to be smaller than the sheet thickness of the glass ribbon above the reheating portion.

5. A glass ribbon producing apparatus according to claim 1, wherein the reheating portion is constructed to reheat the glass ribbon over an entire width of the glass ribbon.

6. A glass ribbon producing apparatus according to claim 1, further comprising guiding portion which is provided below the reheating portion, and has a gap with a dimension larger than the sheet thickness of the glass ribbon in a thickness direction of the glass ribbon, for performing guiding while controlling a warp or a displacement of the glass ribbon within a range of the gap.

7. A glass ribbon producing apparatus according to claim 6, wherein the guiding portion is constructed to guide only the both widthwise end portions of the glass ribbon.

8. A glass ribbon producing apparatus according to claim 7, wherein the guiding portion is constructed of guide rollers which rotate in a state in which the guide rollers are disposed in opposing relation at each of the both widthwise end portions of the glass ribbon via the gap with the dimension larger than the sheet thickness of the glass ribbon.

2. A glass ribbon producing apparatus which feeds molten glass to a forming member and causes the molten glass to flow downward from the forming member to form a sheet-like glass ribbon, comprising reheating portion for reheating and softening the glass ribbon which is temporarily cooled while being caused to flow downward from the forming member.

28. A glass ribbon producing apparatus according to claim 2, wherein the reheating portion is constructed to reheat the glass ribbon over an entire width of the glass ribbon.

30. A glass ribbon producing apparatus according to claim 2, further comprising guiding portion which is provided below the reheating portion, and has a gap with a dimension larger than the sheet thickness of the glass ribbon in a thickness direction of the glass ribbon, for performing guiding while controlling a warp or a displacement of the glass ribbon within a range of the gap.

3. A glass ribbon producing apparatus which feeds molten glass to a forming member and causes the molten glass to flow downward from the forming member to form a sheet-like glass ribbon, comprising:

controlling portion provided immediately below the forming member, for controlling a widthwise contraction of the glass ribbon; and

reheating portion provided immediately below the controlling portion, for reheating and softening the glass ribbon in which the widthwise contraction is controlled by the controlling portion.

4. A glass ribbon producing apparatus according to claim 3, wherein the controlling portion is constructed of cooling rollers which rotate while holding therebetween both widthwise end portions of the glass ribbon.

29. A glass ribbon producing apparatus according to claim 3, wherein the reheating portion is constructed to reheat the glass ribbon over an entire width of the glass ribbon.

31. A glass ribbon producing apparatus according to claim 3, further comprising guiding portion which is provided below the reheating portion, and has a gap with a dimension larger than the sheet thickness of the glass ribbon in a thickness direction of the glass ribbon, for performing guiding while controlling a warp or a displacement of the glass ribbon within a range of the gap.

9. A process for producing a glass ribbon by feeding molten glass to a forming member and causing the molten glass to flow downward from the forming member to form a sheet-like glass ribbon, comprising a reheating step of reheating the glass ribbon caused to flow downward from the forming member,

wherein, by reheating the glass ribbon in the reheating step, a sheet thickness of the glass ribbon after the reheating is made smaller than the sheet thickness of the glass ribbon before the reheating.

12. A process for producing a glass ribbon according to claim 9, wherein the glass ribbon is reheated over an entire width of the glass ribbon in the reheating step.

13. A process for producing a glass ribbon according to claim 9, wherein the reheating of the glass ribbon in the reheating step is performed at a temperature equal to or higher than a softening point of the glass ribbon.

14. A process for producing a glass ribbon according to claim 9, wherein the sheet thickness of a widthwise middle portion of the glass ribbon after forming is equal to or smaller than ½

of the sheet thickness of the widthwise middle portion of the glass ribbon before the reheating step.

15. A process for producing a glass ribbon according to claim 9, wherein the sheet thickness of the widthwise middle portion of the glass ribbon after the forming is equal to or smaller than 0.5 mm.

16. A process for producing a glass ribbon according to claim 9, further comprising a guiding step of causing the glass ribbon reheated in the reheating step to pass through a gap provided in guiding portion so as to have a dimension larger than the sheet thickness of the glass ribbon, and performing guiding while controlling a warp or a displacement of the glass ribbon within a range of the gap.

17. A process for producing a glass ribbon according to claim 16, wherein the guiding portion guides only both widthwise end portions of the glass ribbon in the guiding step.

10. A process for producing a glass ribbon by feeding molten glass to a forming member and causing the molten glass to flow downward from the forming member to form a sheet-like glass ribbon, comprising a reheating step of reheating and softening the glass ribbon which is temporarily cooled while being caused to flow downward from the forming member.

18. A process for producing a glass ribbon according to claim 10, wherein the glass ribbon is reheated over an entire width of the glass ribbon in the reheating step.

20. A process for producing a glass ribbon according to claim 10, wherein the reheating of the glass ribbon in the reheating step is performed at a temperature equal to or higher than a softening point of the glass ribbon.

22. A process for producing a glass ribbon according to claim 10, wherein the sheet thickness of a widthwise middle portion of the glass ribbon after forming is equal to or smaller than ½

of the sheet thickness of the widthwise middle portion of the glass ribbon before the reheating step.

24. A process for producing a glass ribbon according to claim 10, wherein the sheet thickness of the widthwise middle portion of the glass ribbon after the forming, is equal to or smaller than 0.5 mm.

26. A process for producing a glass ribbon according to claim 10, further comprising a guiding step of causing the glass ribbon reheated in the reheating step to pass through a gap provided in guiding portion so as to have a dimension larger than the sheet thickness of the glass ribbon, and performing guiding while controlling a warp or a displacement of the glass ribbon within a range of the gap.

11. A process for producing a glass ribbon by feeding molten glass to a forming member and causing the molten glass to flow downward from the forming member to form a sheet-like glass ribbon, comprising:

a controlling step of controlling a widthwise contraction of the glass ribbon immediately below the forming member; and

a reheating step of reheating and softening, immediately after the controlling step, the glass ribbon in which the widthwise contraction is controlled in the controlling step.

19. A process for producing a glass ribbon according to claim 11, wherein the glass ribbon is reheated over an entire width of the glass ribbon in the reheating step.

21. A process for producing a glass ribbon according to claim 11, wherein the reheating of the glass ribbon in the reheating step is performed at a temperature equal to or higher than a softening point of the glass ribbon.

23. A process for producing a glass ribbon according to claim 11, wherein the sheet thickness of a widthwise middle portion of the glass ribbon after forming is equal to or smaller than ½

of the sheet thickness of the widthwise middle portion of the glass ribbon before the reheating step.

25. A process for producing a glass ribbon according to claim 11, wherein the sheet thickness of the widthwise middle portion of the glass ribbon after the forming is equal to or smaller than 0.5 mm.

27. A process for producing a glass ribbon according to claim 11, further comprising a guiding step of causing the glass ribbon reheated in the reheating step to pass through a gap provided in guiding portion so as to have a dimension larger than the sheet thickness of the glass ribbon, and performing guiding while controlling a warp or a displacement of the glass ribbon within a range of the gap.