PROCESS AND COMPOSITION FOR THE IMMOBILIZATION OF RADIOACTIVE AND HAZARDOUS WASTES IN BOROSILICATE GLASS

• US 20100022380A1
• Filed: 06/22/2009
• Published: 01/28/2010
• Est. Priority Date: 02/23/2004
• Status: Active Grant

• Current Assignee: Geomatrix Solutions, Inc.
• Original Assignee: Geomatrix Solutions, Inc.
• Inventors: CHEKHMIR, Anatoly, GRIBETZ, Arthur
• Granted Patent: US 7,825,288 B2
• Time in Patent Office: Days
• US Class Current: 501/79
• CPC Class Codes: C03C 1/002 Use of waste materials, e.g. slags
• CPC Class Codes: C03C 3/072 containing boron
• CPC Class Codes: C03C 3/074 containing zinc

Abstract

The present invention provides processes to immobilize radioactive and/or hazardous waste in a borosilicate glass, the waste containing one or more of radionuclides, hazardous elements, hazardous compounds, and/or other compounds. The invention also provides borosilicate glass compositions for use in immobilizing radioactive and/or hazardous waste.

Claims

1-11. -11. (canceled)

12. A borosilicate glass consisting essentially of:

about 1 to about 1.3 mole parts of a combination of monovalent cation oxides (R₂O) and divalent cation oxides (RO);

about 1 to about 1.4 mole parts trivalent cation oxides (R₂O₃);

about 1.2 to about 4.2 mole parts of a combination of tetravalent cation oxides (RO₂) and pentavalent cation oxides (R₂O₅); and

wherein SiO₂ is present in an amount greater than 30 weight percent, B₂O₃ is present in an amount between 8.7 and 15.3 weight percent, Al₂O₃ is present in an amount between 7 and 15.1 weight percent, CaO is present in an amount between 0.2 and 2.3 weight percent, and fluorine is present in an amount between about 1 to about 3 weight percent.

13. The borosilicate glass, according to claim 12, consisting essentially of:

about 1 to about 1.3 mole parts of a combination of monovalent cation oxides (R₂O) and divalent cation oxides (RO), including alkaline oxides and alkaline earth oxides;

about 1 to about 1.4 mole parts trivalent cation oxides (R₂O₃), including alumina, boric oxide, and ferric oxide;

about 1.2 to about 4.2 mole parts of a combination of tetravalent cation oxides (RO₂) and pentavalent cation oxides (R₂O₅), including silica, zirconia, titania, and phosphoric oxide; and

about 1 to about 3 weight percent fluorine;

wherein SiO₂ is present in an amount greater than 30 weight percent, B₂O₃ is present in an amount between 8.7 and 15.3 weight percent, Al₂O₃ is present in an amount between 7 and 15.1 weight percent, and CaO is present in an amount between 0.2 and 2.3 weight percent.

14. The borosilicate glass of claim 12, wherein the borosilicate glass is peraluminous.

15. The borosilicate glass of claim 12, wherein the borosilicate glass has a viscosity of 2 to 10 Pascal second at a temperature of about 1150 to about 1200 degrees Celsius.

16. The borosilicate glass of claim 12, wherein the borosilicate glass has a calculated degree of polymerization (K) less than about 15.

17. The borosilicate glass of claim 12, wherein the borosilicate glass has a calculated degree of polymerization (K) less than about 7.

18. The borosilicate glass of claim 12, wherein the borosilicate glass has crystallinity of less than 1 volume percent at about 1150 degrees Celsius, and crystallinity of up to 2 volume percent after three days at about 950 degrees Celsius.

19. The borosilicate glass of claim 12, wherein the borosilicate glass has specific electrical resistivity ranging between about 1.40 cm to about 10 Ω

cm at about 1150 degrees Celsius, that is acceptable for processing in vitrification melters.

20. The borosilicate glass of claim 12, wherein the borosilicate glass meets the leaching requirements of less than about 1.19 grams per square meter per day for boron, less than about 0.69 grams per square meter per day for lithium, and less than about 0.95 grams per square meter per day for sodium, for acceptance in U.S. high-level waste repositories.

21. The borosilicate glass of claim 12, wherein the borosilicate glass contains fluorine in an amount between about 1.2 and about 2.5 weight percent.