LOW-TEMPERATURE ADHESIVE UNDERCOAT COMPOSITION

• US 20100043945A1
• Filed: 11/20/2007
• Published: 02/25/2010
• Est. Priority Date: 11/20/2006
• Status: Abandoned Application

• Current Assignee: Sika Technology Ag (Compagnie de Saint-Gobain SA)
• Original Assignee: Sika Technology Ag (Compagnie de Saint-Gobain SA)
• Inventors: Dohner, Reto, Huck, Wolf-Rudiger
• Application Number:
  US12/312,590
• Publication Number:
  US 20100043945A1
• Time in Patent Office: Days
• US Class Current: 156/98
• CPC Class Codes: C03C 17/30 with silicon-containing compounds
• CPC Class Codes: C03C 27/048 consisting of an adhesive specially adapted for that purpose
• CPC Class Codes: C08G 77/26 nitrogen-containing groups
• CPC Class Codes: C08G 77/28 sulfur-containing groups
• CPC Class Codes: C08G 77/54 Nitrogen-containing linkages C08G77/485 takes precedence
• CPC Class Codes: C09D 183/08 containing silicon bound to organic groups containing atoms other than carbon, hydrogen, and oxygen
• CPC Class Codes: C09D 183/14 in which at least two but not all the silicon atoms are connected by linkages other than oxygen atoms C09D183/10 takes precedence
• CPC Class Codes: C09D 4/00 Coating compositions, e.g. paints, varnishes or lacquers, based on organic non-macromolecular compounds having at least one polymerisable carbon-to-carbon unsaturated bond ; Coating compositions, based on monomers of macromolecular compounds of groups C09D183/00 - C09D183/16
• CPC Class Codes: C09D 5/002 Priming paints C09D5/08 takes precedence
• CPC Class Codes: C09J 2400/143 in the substrate
• CPC Class Codes: C09J 2400/146 in the pretreated surface to be joined
• CPC Class Codes: C09J 4/00 Adhesives based on organic non-macromolecular compounds having at least one polymerisable carbon-to-carbon unsaturated bond ; adhesives, based on monomers of macromolecular compounds of groups C09J183/00 - C09J183/16
• CPC Class Codes: C09J 5/02 involving pretreatment of the surfaces to be joined
• CPC Class Codes: Y10T 156/10 Methods of surface bonding and/or assembly therefor
• CPC Class Codes: Y10T 428/2848 Three or more layers

Abstract

A method for producing an adhesive undercoat on a substrate S1 with a substrate temperature of lower than 5° C. The adhesive undercoat composition comprises at least one mercaptosilane MS or an adduct of mercaptosilane and either at least one polysilane PSA, comprising at least one secondary or tertiary amino group, or at least one polysilane PS and at least one aminosilane AS, comprising at least one secondary or tertiary amino group. This method is particularly suited for the gluing of glass, particularly of glass ceramics, preferably for repairing windows of motor vehicles in cold temperatures.

Claims

1. A method for producing a substrate S1 coated with an adhesive undercoat composition,

comprising applying an adhesive undercoat composition on a substrate S1 at a substrate temperature of less than 5°

C. wherein the adhesive undercoat composition comprises;

at least one mercaptosilane MS or an adduct of a mercaptosilane MS;

either at least one polysilane PSA which has at least one secondary or tertiary amino group or at least one polysilane PS; and

at least one aminosilane AS which has at least one secondary or tertiary amino group.

2. The method as claimed in claim 1, wherein the polysilane PSA which has at least one secondary or tertiary amino group is an aminosilane of the formula (I)

3. The method as claimed in claim 2, wherein the polysilane PSA which has at least one secondary or tertiary amino group is an aminosilane of the formula (II)

4. The method as claimed in claim 2, wherein the polysilane PSA which has at least one secondary or tertiary amino group has at least one structural element of the formula (III) (III′

) (III″

) or (III′

″

)

5. The method as claimed in claim 4, wherein the polysilane PSA which has at least one secondary or tertiary amino group is a reaction product of an epoxysilane of the formula (IV) with an aminosilane of the formula (IV′

)

6. The method as claimed in claim 1, wherein the polysilane PS has a silane equivalent weight of not more than 500 g/eq.

7. The method according to claim 1, wherein the polysilane PS contains two to four silane groups.

8. The method according to claim 1, wherein an aminosilane AS which has at least one secondary or tertiary amino group has the formula (V), (VI) or (VII)

9. The method as claimed in claim 1, wherein the mercaptosilane MS has the formula (VIII)

HS—

R^4″

—

Si(OR^2″

)_(3-c)(R^3″

)_c 

 

(VIII)

where R^2″

is independently hydrogen or an alkyl group having 1 to 4 carbon atoms or an acyl group;

R^3″

is independently H or an alkyl group having 1 to 10 carbon atoms;

R^4″

is a linear or branched alkylene group having 1 to 6 carbon atoms;

and c is 0, 1 or 2.

10. The method as claimed in claim 1, wherein the adhesive undercoat composition further comprises at least one organotitanium compound in an amount of 0.1-15% by weight, based on the weight of the adhesive undercoat composition.

11. The method as claimed in claim 1, wherein the adhesive undercoat composition further comprises a solvent in an amount of 10-99% by weight, based on the weight of the adhesive undercoat composition.

12. The method as claimed in claim 1, wherein the proportion of the mercaptosilane MS is 0.5-15% by weight, based on the weight of the adhesive undercoat composition.

13. The method as claimed in claim 1, characterized in that the proportion of the polysilane PSA which has at least one secondary or tertiary amino group is 0.5-30% by weight, based on the weight of the adhesive undercoat composition.

14. The method as claimed in claim 1, wherein the proportion of the polysilane PS is 0.5-15% by weight, based on the weight of the adhesive undercoat composition.

15. The method as claimed in claim 14, wherein the proportion of aminosilane AS which has at least one secondary or tertiary amino group is 0.5-25% by weight, based on the weight of the adhesive undercoat composition.

17. A process for adhesive bonding two substrates S1 and S2, which has at least the following steps

a) applying an adhesive undercoat composition as described in claim 1 to a first substrate S1 which has a temperature of less than 5°

C.;

b) applying an adhesive to the flashed-off adhesive undercoat composition applied in step a);

c) contacting the adhesive with a second substrate S2;

or

a′

) applying an adhesive undercoat composition—

as described in claim 1 to a first substrate S1 which has a temperature of less than 5°

C.;

b′

) applying an adhesive or sealant to the surface of a second substrate S2

c′

) contacting the adhesive with the flashed-off composition present on substrate S1;

or

a″

) applying an adhesive undercoat composition as described in claim 1 to a first substrate S1 and/or second substrate S2 which has a temperature of less than 5°

C.;

b″

) applying an adhesive to the first substrate S1 and second substrate S2, to at least one of which an adhesive undercoat composition has been applied in step a″

);

c″

) contacting the adhesives applied to one another to join the substrate parts to form an adhesive bond;

or

a′

″

) applying an adhesive undercoat composition as described in claim 1 to a first substrate S1 which has a temperature of less than 5°

C.;

b′

″

) flashing off the composition

c′

″

) applying an adhesive between the surfaces of substrates S1 and S2, the second substrate S2 consisting of the same material or a different material than substrate S1.

18. The process as claimed in claim 17, wherein step c) or c′

) or c″

) or c′

″

) is followed by a step d) for curing the adhesive.

19. The process as claimed in claim 17, wherein at least one of the substrates S1 or S2 is glass or glass ceramic.

20. The process as claimed in claim 17, wherein the substrate S1 or S2 is glass or glass ceramic, and in that the substrate S2 or S1 is a paint system or a painted metal or a painted metal alloy.

21. An article produced by performing a process as claimed in claim 17.

22. An article as claimed in claim 21, wherein the article is a means of transport.

23. A process for repairing glazing of a means of transport at an ambient temperature of less than 5°

C., comprising the steps of

i) removing the defective glass, especially a defective pane;

ii) applying an adhesive undercoat composition as described in claim 1 to a piece of glass, to be inserted by adhesive bonding, and/or to the flange of the mode of transport to be adhesive bonded;

iii) applying a moisture-curing one-component adhesive, especially a moisture-curing one-component polyurethane adhesive, which has a temperature between 10°

C. and 80°

C., to the piece of glass to be adhesive bonded and/or the flange of the mode of transport to be adhesive bonded;

iv) joining glass and flange via the adhesive present between them.

16. (canceled)