METHOD OF SURFACE TREATMENT FOR METAL GLASS PART, AND METAL GLASS PART WITH ITS SURFACE TREATED BY THE METHOD
First Claim
1. A surface treatment method for a metallic glass component, comprising:
- removing an oxide film on a surface of the metallic glass component and providing an anchor bond shape on the surface of the metallic glass component by surface active treatment with a mixed aqueous solution of nitric acid and hydrofluoric acid; and
forming a plating film on the surface of the metallic glass component by electroplating or electroless plating.
3 Assignments
0 Petitions
Accused Products
Abstract
There is provided a metallic glass component with its surface layer having both durability of a film and chromatic color properties, and a method for forming the surface layer. Surface active treatment is performed wherein the surface of the metallic glass component is reacted with a mixed aqueous solution of nitric acid and hydrofluoric acid to remove an oxide film and to provide an anchor bond shape on the surface of a metallic glass component, and electroplating or electroless plating is then performed, to form a plating film on the surface of the metallic glass component. It is thereby possible to form a surface layer of a metallic glass which has both durability and a chromatic color.
-
Citations
19 Claims
-
1. A surface treatment method for a metallic glass component, comprising:
-
removing an oxide film on a surface of the metallic glass component and providing an anchor bond shape on the surface of the metallic glass component by surface active treatment with a mixed aqueous solution of nitric acid and hydrofluoric acid; and forming a plating film on the surface of the metallic glass component by electroplating or electroless plating. - View Dependent Claims (3, 4, 6, 7, 8, 9, 12, 15)
-
-
2. A surface treatment method for a metallic glass component, comprising:
-
removing an oxide film on a surface of the metallic glass component and providing an anchor bond shape on the surface of the metallic glass component by surface active treatment with a mixed aqueous solution of nitric acid and hydrofluoric acid; and forming a metal deposition film uniformly on the surface of the metallic glass component by a dry plating method such as vacuum deposition, ion plating or sputtering. - View Dependent Claims (10, 11, 13, 14, 16, 18)
-
-
5. A surface treatment method for a metallic glass component, comprising:
-
removing an oxide film on a surface of the metallic glass component and providing an anchor bond shape on the surface of the metallic glass component by surface active treatment with a mixed aqueous solution of nitric acid and hydrofluoric acid; adding a metal gloss color to the surface of the metallic glass component by physical polishing; forming a resin coat to the surface of the metallic glass component by applying resin. - View Dependent Claims (17, 19)
-
Specification