Oil dispersible polymer nanoparticles

• US 20100099590A1
• Filed: 12/12/2006
• Published: 04/22/2010
• Est. Priority Date: 12/12/2005
• Status: Abandoned Application

• Current Assignee: Queen's University At Kingston
• Original Assignee: Queen's University At Kingston
• Inventors: Liu, Guojun
• Application Number:
  US11/637,193
• Publication Number:
  US 20100099590A1
• Time in Patent Office: Days
• US Class Current: 508/478
• CPC Class Codes: B82Y 30/00 Nanotechnology for materials or surface science, e.g. nanocomposites
• CPC Class Codes: C10M 171/06 Particles of special shape or size
• CPC Class Codes: C10N 2020/06 Particles of special shape or size
• CPC Class Codes: Y10T 428/2998 including synthetic resin or polymer

Abstract

There is disclosed an oil-dispersible nanoparticle comprising metal-binding functional groups on its surface. Preferably, the nanoparticle is derived from substantially spherical polymer micelles of (A_1-yC_y)_nB_m diblocks or (A_1-yC_y)_nB_m(A_1-yC_y)_n triblocks. A method for producing the nanoparticles is also described. The nanoparticles are particularly useful as lubricant additives.

Claims

1. An oil-dispersible nanoparticle comprising an organic polymer and polar metal-binding functional groups on its surface.

2. The nanoparticle defined in claim 1, wherein the average hydrodynamic diameter of the nanoparticle ranges from about 20 to about 250 nm, preferably about 20 to about 100 nm.

3. The nanoparticle defined in claim 1 comprising a core that is substantially insoluble in oil, and a corona that is oil soluble.

4. The nanoparticle defined in claim 3, wherein the diameter of the core ranges from about 10 to about 150 nm, and is preferably between about 10 to about 80 nm.

5. The nanoparticle defined in claim 3, wherein the core is crosslinkable, optionally photo-crosslinkable.

6. The nanoparticle of defined in claim 1, which is substantially spherical or cylindrical.

7. The nanoparticle defined in claim 1, derived from the following chemical structure:

8. The nanoparticle defined in claim 7, wherein R1, R2, R3 and R4 are independently hydrogen or a methyl group.

9. The nanoparticle defined in claim 7, wherein R1, R2, R3 and R4 each are hydrogen.

10. The nanoparticle defined in claim 7, wherein the alkyl groups in J1 can be either linear or branched and have 1 to 30 carbon atoms.

11. The nanoparticle defined in claim 7, wherein the alkyl groups in J1 can be either linear or branched and have 4 to 18 carbon atoms.

12. The nanoparticle defined in claim 7, wherein the alkyl groups in J1 can be either linear or branched and have 6 to 10 carbon atoms.

13. The nanoparticle defined in claim 7, wherein the alkyl groups in J2 can be either linear or branched and have 1 to 30 carbon atoms.

14. The nanoparticle defined in claim 7, wherein the alkyl groups in J2 can be either linear or branched and have 1 to 10 carbon atoms.

15. The nanoparticle defined in claim 7, wherein the alkyl groups in J2 can be either linear or branched and have 1 to 6 carbon atoms.

16. The nanoparticle defined in claim 7, wherein A is selected from the group consisting of hydroxyl, amino, carboxyl, carboxyphenyl (where the carboxyl group can be at the para, meta, or ortho position, pyridyl, aminoalkylphenyl, carboxyalkylphenyl, N-alkylcarbamoyl, N,N-dialkylcarbamoyl, glycerylcarboxyl, hydroxyalkylcarboxyl, imidazolyl, and triazolyl

17. The nanoparticle defined in claim 7, wherein X is selected from the group consisting of hydroxyl, amino, carboxyl, carboxyphenyl (where the carboxyl group can be at the para, meta, or ortho position), pyridyl, aminoalkylphenyl, carboxyalkylphenyl, glycerylcarboxyl, hydroxyalkylcarboxyl, cinnamoyloxyalkylcarboxyl, allylcarboxyl, and acryloxyalkylcarboxyl.

18. The nanoparticle defined in claim 7, wherein X selected from the group consisting of carboxyl groups, amino groups, pyridyl groups, carbonyl groups, hydroxyl groups, sulfonyl groups, sulfate groups, phosphine groups, phosphate groups and sulfide groups.

19. The nanoparticle defined in claim 13, wherein X selected from the group consisting of carboxyl groups, amino groups, pyridyl groups, carbonyl groups, hydroxyl groups, sulfonyl groups, sulfate groups, phosphine groups, phosphate groups and sulfide groups.

20. The nanoparticle defined in claim 7, wherein m and n are the same or different and each is an integer in the range of 10 to 500.

21. The nanoparticle defined in claim 7, wherein m and n are the same or different and each is an integer in the range of 10 to 500.

22. The nanoparticle defined in claim 7, wherein o is an integer in the range of 0 to 500.

30. A method of reducing friction comprising providing an oil-dispersible nanoparticle of claim 1 as an additive to an oil employed for lubrication.

31. A method of reducing wear of machine parts comprising providing an oil-dispersible nanoparticle of claim 1 as an additive of an oil contacting said machine parts.

32. An oil composition comprising the nanoparticle defined in claim 1 and a base oil composition.

23. A method for making an oil-dispersible nanoparticle comprising 1) forming substantially spherical micelles of (A_100%-yC_y)_nB_m diblocks or (A_100%-yC_y)_nB_m(A_100%-yC_y)_n triblocks in a block-selective solvent and, optionally, 2) crosslinking the substantially spherical micelles,

where the A units are oil soluble monomers;

the C units are functional groups that are metal binding or metal binding after chemical transformation; and

the B units are oil insoluble monomers and preferably crosslinkable;

where y ranges from 0 to about 30% and preferably from about 0.1% to about 2%;

where n ranges from about 10 to about 10,000; and

where m ranges from about 10 to about 10,000.

24. The method defined in claim 23, wherein the A is selected from poly(alkyl acrylate), poly(alkyl methacrylate), poly(dimethyl siloxane), polyisoprene, poly(butadiene), poly(isobutylene), polystyrene, poly(alkylstyrene) and combinations thereof.

25. The method defined in claim 23, wherein the alkyl units are selected from C₁ to C₂₀.

26. The method defined in claim 23, wherein the alkyl units are selected from C₄ to C₁₈.

27. The method defined in claim 23, wherein the alkyl units are butyl, 2-ethylhexyl or a combination thereof.

28. The method defined in claim 23, wherein the C units are selected to contain carboxyl groups, amino groups, pyridyl groups, carbonyl groups, hydroxyl groups, sulfonyl groups, sulfate groups, phosphine groups, phosphate groups, sulfide groups, triazole groups, indole groups and combinations thereof.

29. The method defined in claim 23, wherein B is selected from poly(vinyl pyridine), poly(2-cinnamoyloxyethyl methacrylate), poly(2-cinnamoyloxyethyl acrylate), poly(2-hydroxyethyl acrylate), poly(2-hydroxyethyl methacrylate), polyisoprene, polybutadiene, poly[2-(dimethylamino)ethyl methacrylate], poly(acrylic acid), poly(methacrylic acid), poly(vinyl alcohol), poly[ally(meth)acrylate], poly[acryloxyethyl(meth)acrylate] and combinations thereof.