METHOD FOR PREPARING MICROGEL PARTICLES BY CONTROLLED RADICAL POLYMERIZATION IN AN AQUEOUS DISPERSION USING NITROXIDE CONTROL AGENTS

• US 20100137534A1
• Filed: 01/28/2008
• Published: 06/03/2010
• Est. Priority Date: 01/29/2007
• Status: Abandoned Application

• Current Assignee: Arkema France (Arkema), Centre National De La Recherche Scientifique, Universite Paris - Sud
• Original Assignee: Arkema France (Arkema), Centre National De La Recherche Scientifique, Universite Paris - Sud
• Inventors: Save, Maud, Charleux, Bemadette, Delaittre, Guillaume, Magnet, Stephanie
• Application Number:
  US12/524,975
• Publication Number:
  US 20100137534A1
• Time in Patent Office: Days
• US Class Current: 526/193
• CPC Class Codes: A61K 2800/412 Microsized, i.e. having sizes between 0.1 and 100 microns
• CPC Class Codes: A61K 2800/54 Polymers characterized by specific structures/properties
• CPC Class Codes: A61K 8/11 Encapsulated compositions
• CPC Class Codes: A61K 8/90 Block copolymers A61K8/89 takes precedence
• CPC Class Codes: C08F 2/18 Suspension polymerisation
• CPC Class Codes: C08F 2/38 Polymerisation using regulators, e.g. chain terminating agents , e.g. telomerisation
• CPC Class Codes: C08F 20/06 Acrylic acid; Methacrylic acid; Metal salts or ammonium salts thereof
• CPC Class Codes: C08F 20/18 with acrylic or methacrylic acids
• CPC Class Codes: C08F 20/56 Acrylamide; Methacrylamide
• CPC Class Codes: C08F 2438/02 Stable Free Radical Polymerisation [SFRP]; Nitroxide Mediated Polymerisation [NMP] for, e.g. using 2,2,6,6-tetramethylpiperidine-1-oxyl [TEMPO]
• CPC Class Codes: C08F 290/00 Macromolecular compounds obtained by polymerising monomers on to polymers modified by introduction of aliphatic unsaturated end or side groups
• CPC Class Codes: C08F 290/04 Polymers provided for in subclasses C08C or C08F
• CPC Class Codes: C08F 293/005 using free radical "living" or "controlled" polymerisation, e.g. using a complexing agent
• CPC Class Codes: C08F 4/00 Polymerisation catalysts
• CPC Class Codes: C08L 2666/02 Organic macromolecular compounds, natural resins, waxes or and bituminous materials
• CPC Class Codes: C08L 53/00 Compositions of block copolymers containing at least one sequence of a polymer obtained by reactions only involving carbon-to-carbon unsaturated bonds; Compositions of derivatives of such polymers
• CPC Class Codes: C09D 153/00 Coating compositions based on block copolymers containing at least one sequence of a polymer obtained by reactions only involving carbon-to-carbon unsaturated bonds; Coating compositions based on derivatives of such polymers

Abstract

The invention relates to a method for preparing microgel particles according to a method of controlled radical polymerization in an aqueous dispersion using particular control agents of the nitroxide type. Use in the biomedical field, and in the field of agrochemistry, cosmetics, surface coatings.

Claims

1. A process for preparing microgel particles in aqueous medium, comprising the following steps:

a) preparing a living macroinitiator obtained by polymerization of one or more monomers in the presence of a control agent corresponding to one of the following formulae;

in which;

R₁ and R₃, which may be identical or different, represent a linear or branched alkyl group having a number of carbon atoms ranging from 1 to 3;

R₂ represents a hydrogen atom, a linear or branched alkyl group having a number of carbon atoms ranging from 1 to 8, a phenyl group, an alkali metal or an ammonium ion;

Z represents an aryl group or a group of formula Z₁—

[X—

C(O)]_n, in which Z₁ represents a polyfunctional structure, X is an oxygen atom, a nitrogen atom bearing a carbon-based group or a hydrogen atom, or a sulfur atom; and

n is an integer greater than or equal to 2;

b) adding to the reaction medium obtained after step a) at least one vinyl monomer that is different than that of step a);

c) adding to the reaction medium at least one crosslinking comonomer, the crosslinking comonomer being different than the monomers of steps a) and b), this addition step being performed simultaneously or consecutively relative to the addition step b),

wherein the constituent monomer(s) of the living macroinitiator of step a) and/or the vinyl monomers of step b) and/or the crosslinking comonomer(s) of step c) comprise at least one function chosen from —

CO₂H, —

SO₃H, ammonium, ethylene oxide, amino and amide, said function possibly existing in the form of salts.

2. The process as claimed in claim 1, in which the constituent monomers of the living macroinitiator of step a) comprise at least one function chosen from —

CO₂H, —

SO₃H, ammonium, ethylene oxide, amino and amide, said function possibly existing in the form of salts.

3. The process as claimed in claim 1, in which the constituent monomers of the living macroinitiator of step a) are chosen from the group consisting of (meth)acrylic monomers, dialkylaminoalkyl(meth)acrylate monomers, trialkylammoniumalkyl(meth)acrylate halides, (alkoxy)polyalkylene glycol(meth)acrylate monomers, (meth)acrylamide monomers optionally comprising a sulfonate group, and styrene monomers comprising a sulfonate group.

4. The process as claimed in claim 1, in which the constituent monomers of the living macroinitiator of step a) are acrylic acid or methacrylic acid.

5. The process as claimed in claim 1, in which the control agent corresponds to the following formula:

6. The process as claimed in claim 1, in which the control agent corresponds to the following formula:

7. The process as claimed in claim 1, in which the vinyl monomers introduced in step b) are chosen from vinylaromatic monomers, acrylic monomers such as alkyl or aryl acrylates, methacrylic monomers such as alkyl or aryl methacrylates, acrylamide monomers and methacrylamide monomers.

8. The process as claimed in claim 1, in which the vinyl monomers introduced in step b) are monoalkylacrylamide or dialkylacrylamide monomers.

9. The process as claimed in claim 8, in which the dialkylacrylamide monomer is N,N-dimethylacrylamide, N,N-diethylacrylamide or N,N-diisopropylacrylamide.

10. The process as claimed in claim 8, in which the monoalkylacrylamide monomer is N-methylacrylamide, N-ethylacrylamide or N-isopropylacrylamide.

11. The process as claimed in claim 1, in which the vinyl monomers are introduced into the reaction medium in a proportion of at least 10% by weight, based on the total weight of monomers added.

12. The process as claimed in claim 1, in which the crosslinking monomers are chosen from divinylbenzenes, trivinylbenzenes, allyl(meth)acrylates, diallyl maleate polyol(meth)acrylates, alkylene glycol di(meth)acrylates containing from 2 to 10 carbon atoms in the carbon chain, and N,N′

-alkylenebisacryl amides.

13. The process as claimed in claim 12, in which the crosslinking comonomer is N,N′

-methylenebisacrylamide.

14. The process as claimed in claim 1, in which the crosslinking comonomer is introduced into the reaction medium in a content ranging from 1% to 12% by weight relative to the weight of vinyl monomer(s) introduced in step b).

15. The process as claimed in claim 1, in which the addition step c) is performed consecutively to the addition step b).

16. The process as claimed in claim 1, further comprising a step of adding to the reaction medium components intended to be encapsulated by the particles.

17. Microgel particles that may be obtained via a process as defined according to claim 1.

18. The microgel particles as defined in claim 17, wherein said microgel particle is an encapsulation material.

19. The use of microgel particles as defined in claim 17, wherein said microgel particle is a thickener.

20. The microgel particles of claim 17, comprising a pharmaceutical, biomedical, agrochemical, human or animal nutrition, cosmetic, paint, or surface coating composition.