METHOD OF MAKING A SHEET OF BUILDING MATERIAL

• US 20100215946A1
• Filed: 10/01/2007
• Published: 08/26/2010
• Est. Priority Date: 10/01/2007
• Status: Active Grant

• Current Assignee: American Construction Materials Incorporated (Seven Group Holdings Limited)
• Original Assignee: G.R. Green Building Products, Inc.
• Inventors: Wensel, Geoffrey F., Suggitt, Robert W.
• Granted Patent: US 8,894,901 B2
• Time in Patent Office: Days
• US Class Current: 428/323
• CPC Class Codes: B29C 43/003 characterised by the choice of material
• CPC Class Codes: B29C 43/24 Calendering
• CPC Class Codes: B29C 48/07 Flat, e.g. panels
• CPC Class Codes: B29C 48/906 using roller calibration
• CPC Class Codes: B29C 48/914 cooling drums
• CPC Class Codes: B29K 2023/0608 characterised by its density
• CPC Class Codes: B29K 2105/26 Scrap or recycled material
• CPC Class Codes: B29K 2509/00 Use of inorganic materials not provided for in groups B29K2503/00 - B29K2507/00, as filler
• CPC Class Codes: B29L 2031/10 Building elements, e.g. bricks, blocks, tiles, panels, posts, beams frameless domes B29L2025/00, doors B29L2031/724
• CPC Class Codes: B29L 2031/108 Roofs
• CPC Class Codes: C08J 2323/06 Polyethene
• CPC Class Codes: C08J 5/18 Manufacture of films or sheets
• CPC Class Codes: C08L 23/06 Polyethene
• CPC Class Codes: C08L 23/0815 Copolymers of ethene with aliphatic 1-olefins
• CPC Class Codes: C08L 2666/06 Homopolymers or copolymers of unsaturated hydrocarbons; Derivatives thereof
• CPC Class Codes: E04D 5/06 by making use of plastics
• CPC Class Codes: Y10T 428/25 Web or sheet containing structurally defined element or component and including a second component containing structurally defined particles
• CPC Class Codes: Y10T 428/251 Mica
• CPC Class Codes: Y10T 428/258 Alkali metal or alkaline earth metal or compound thereof
• CPC Class Codes: Y10T 428/259 Silicic material

Abstract

A method of making a sheet of building material, useful for roofing or siding applications, and the sheet material made by such method. A mixture of a thermoplastic resin and mineral filler is prepared, the resin comprising about 10% to 40% by weight of the mixture and the filler comprising about 60% to 90% by weight. The mixture is mixed at a temperature above the melting point of the resin and is formed into a sheet at such temperature. The sheet is allowed to cool until the surface is at a temperature below the midpoint of the melting range of the thermoplastic resin, e.g. in the range of 210 to 220 degrees F. (99 to 104 degrees C.), for polyethylene, at which point it is strained by passing it through calendering rollers. The sheet material made by this process, having a high concentration of mineral filler, is fire resistant, durable, ductile, of moderate weight and resistant to weathering. It can be produced using relatively inexpensive manufacturing equipment. The sheet material can incorporate a high proportion of recycled resin, such as recycled high density polyethylene.

Claims

1. A method of making a sheet of building material for roofing or siding applications, comprising the steps of:

(a) preparing a mixture comprising a thermoplastic resin and a mineral filler, said resin comprising about 10% to 40% by weight of said mixture and said filler comprising about 60% to 90% by weight of said mixture;

(b) mixing said mixture at a temperature above the melting range of said resin;

(c) forming said mixture into a sheet, said forming step being done at said temperature of step (b);

(d) allowing a surface of said sheet to cool to a temperature below the midpoint of the melting range of said thermoplastic resin; and

(e) straining said sheet by calendering, rolling or pressing said sheet when said surface temperature is at said temperature of step (d).

2. A method according to claim 1 wherein said temperature in step (d) is in the range of 205 to 225 degrees F. (96 to 107 degrees C.).

3. A method according to claim 1 wherein said thermoplastic resin comprises polyethylene.

4. A method according to claim 3 wherein said polyethylene is a mixture of high density polyethylene and linear low density polyethylene.

5. A method according to claim 4 wherein the weight ratio of said high density polyethylene to said linear low density polyethylene is about 3:

1.

6. A method according to claim 1 wherein said temperature in step (d) is in the range of 210 to 220 degrees F. (99 to 104 degrees C.).

7. A method according to claim 1 wherein said thermoplastic resin comprises polypropylene.

8. A method according to claim 7 wherein said temperature in step (d) is in the range of 220 to 250 degrees F. (104 to 121 degrees C.).

9. A method according to claim 1 further comprising lowering said surface temperature during said step of straining.

12. A method according to claim 1 wherein said filler is limestone.

13. A method according to claim 1 wherein said filler is one of dolomite, talc, silica and flyash.

14. A method according to claim 12 wherein said limestone is about 100 mesh in particle size.

15. A method according to claim 1 wherein said thermoplastic resin comprises 10% to 35% by weight of said mixture.

17. A method according to claim 1 wherein said filler comprises 65% to 90% by weight of said mixture.

19. A method according to claim 1 wherein said mixture further comprises mica.

20. A method according to claim 19 wherein said mica comprises 0.1% to 1.0% by weight of said mixture.

21. A method according to claim 1 wherein said mixture further comprises one or more of carbon black, a UV stabilizer, a ductility enhancer and a fireproofing component.

22. A method according to claim 1 wherein said step of preparing said mixture comprises heating said filler and adding said resin to said filler.

23. A method according to claim 19 wherein said filler used to prepare said mixture is at a temperature of about 350 degrees F. (177 degrees C.).

24. A method according to claim 1 wherein said temperature of step (b) is in the range of 300 to 325 degrees F. (149 to 163 degrees C.).

26. A method according to claim 1 wherein said step of mixing is done in an open atmosphere.

27. A method according to claim 1 wherein said step of straining comprises passing said sheet between calendering rollers.

28. A method according to claim 1 wherein said step of straining increases a length of said sheet by 1% to 10%.

30. A method according to claim 27 wherein a calendering force applied by said calendering rollers is varied during the step of straining so as to cause a variation in color tone of said sheet.

32. A method according to claim 1 further comprising the step, after step (e), of applying a protective coating to said surface of said sheet.

33. A method according to claim 1 wherein said temperature in step (d) is in the range of 200 to 225 degrees F. (93 to 107 degrees C.).

34. A method according to any claim 1 wherein said temperature in step (d) is in the range of 205 to 220 degrees F. (96 to 104 degrees C.).

35. A sheet of building material made according to the method of claim 1.

10. (canceled)

11. (canceled)

16. (canceled)

18. (canceled)

25. (canceled)

29. (canceled)

31. (canceled)