Laminated Glass Having Plastic Film Inserted Therein

• US 20100215952A1
• Filed: 07/15/2008
• Published: 08/26/2010
• Est. Priority Date: 07/31/2007
• Status: Abandoned Application

• Current Assignee: Central Glass Company Limited
• Original Assignee: Central Glass Company Limited
• Inventors: Miyazaki, Makoto, Takamatsu, Atsushi, Izutani, Kensuke, Yonekura, Masaaki
• Application Number:
  US12/671,262
• Publication Number:
  US 20100215952A1
• Time in Patent Office: Days
• US Class Current: 428/339
• CPC Class Codes: B32B 1/00 Layered products having a non-planar shape
• CPC Class Codes: B32B 17/10005 laminated safety glass or glazing
• CPC Class Codes: B32B 17/10036 comprising two outer glass sheets
• CPC Class Codes: B32B 17/10201 Dielectric coatings
• CPC Class Codes: B32B 17/10871 in combination with particular heat treatment
• CPC Class Codes: B32B 2367/00 Polyesters, e.g. PET, i.e. polyethylene terephthalate
• CPC Class Codes: Y10T 428/24628 Nonplanar uniform thickness material
• CPC Class Codes: Y10T 428/269 including synthetic resin or polymer layer or component

Abstract

There is provided a plastic film-inserted laminated glass prepared by laminating a glass plate, an interlayer film, a plastic film, an interlayer film, and a glass plate in this order. The plastic film-inserted laminated glass is characterized in that an infrared reflective film is formed by stacking dielectric films on the plastic film and that the plastic film having the infrared ray reflective film formed satisfies any one condition of the following (A), (B) and (C),

• • (A) thermal contraction percentage of the infrared ray reflective film-formed plastic film is in a range of 0.5-3% in a temperature range of 90-150° C.;
  • (B) elastic modulus of the plastic film is in a range of 30-2000 MPa in a temperature range of 90-150° C.; and
  • (C) elongation percentage of the plastic film is 0.3% or less when a tension of 10N is added per 1 m width of the plastic film in a temperature range of 90-150° C.

Claims

1. A plastic film-inserted laminated glass prepared by laminating a glass plate, an interlayer film, a plastic film, an interlayer film, and a glass plate in this order, the plastic film-inserted laminated glass being characterized in that an infrared reflective film is formed by stacking dielectric films on the plastic film and that the plastic film having the infrared ray reflective film formed satisfies any one condition of the following (A), (B) and (C),

(A) thermal contraction percentage of the infrared ray reflective film-formed plastic film is in a range of 0.5-3% in a temperature range of 90-150°

C.;

(B) elastic modulus of the plastic film is in a range of 30-2000 MPa in a temperature range of 90-150°

C.; and

(C) elongation percentage of the plastic film is less than 0.3% when a tension of 10N is added per 1 m width of the plastic film in a temperature range of 90-150°

C.

2. A plastic film-inserted laminated glass according to claim 1, which is characterized in that the glass plate is a curved glass plate having a radius of curvature of 0.9 m to 3 m.

3. A plastic film-inserted laminated glass according to claim 1, which is characterized in that the plastic film is a plastic film prepared by an elongation method.

4. A plastic film-inserted laminated glass according to claim 1, which is characterized in that thickness of the plastic film is 30 μ

m to 200 μ

m.

5. A plastic film-inserted laminated glass according to claim 1, which is characterized in that the plastic film is a plastic film having a hard coating layer formed.

6. A plastic film-inserted laminated glass according to claim 1, which is characterized in that the infrared ray reflective film is a dielectric multilayer film prepared by alternately stacking 4 layers to 11 layers of dielectric films of low refractive index and dielectric films of high refractive index.

7. A plastic film-inserted laminated glass according to claim 1, which is characterized in that the dielectric film is a dielectric film formed of a dielectric selected from TiO₂, Nb₂O₅, Ta₂O₅, SiO₂, Al₂O₃, ZrO₂, and MgF₂.