Mould release composition

• US 20100225026A1
• Filed: 09/14/2007
• Published: 09/09/2010
• Est. Priority Date: 09/15/2006
• Status: Abandoned Application

• Current Assignee: Sika Technology Ag (Compagnie de Saint-Gobain SA)
• Original Assignee: Sika Technology Ag (Compagnie de Saint-Gobain SA)
• Inventors: Salo, Kai, Madsen, Preben
• Application Number:
  US12/310,913
• Publication Number:
  US 20100225026A1
• Time in Patent Office: Days
• US Class Current: 264/338
• CPC Class Codes: B28B 7/384 Treating agents for plastic moulding materials in general B29C33/60; lubricants in general C10M

Abstract

The present invention relates to a mould release composition comprising an aqueous emulsion of an oil, wherein the emulsion comprises preferably at least one organic acid, preferably at least one ester surfactant such as monoglycerides of lower alkanoic acids; preferably at least one further ester of polyethylene glycol and oleic acid, and preferably at lest one ether surfactant, said composition further comprising colloidal silica, said mould release composition providing an environmentally friendly, biodegradable, mould release composition and surface improver giving a rapid and lasting strengthening of the surface of the concrete rendering the surface more dense or hardened.

Claims

1. A mould release composition comprising an aqueous emulsion of an oil, and colloidal silica.

2. The mould release composition according to claim 1, wherein the aqueous emulsion is an oil-in-water emulsion.

3. The mould release composition according to claim 1, wherein said oil comprises one or more oil component.

4. The mould release composition according to claim 1, wherein said colloidal silica is a dispersion comprising silica particles in the colloidal state with a diameter of 1 to 100 nm.

5. The mould release composition according to claim 1, wherein said emulsion comprises at least one ester.

6. The mould release composition according to claim 5, wherein said at least one ester is at least one monoglyceride of lower alkanoic acids having up to 6 carbon atoms.

7. The mould release composition according to claim 1, wherein said emulsion further comprises at least one organic acid.

8. The mould release composition according to claim 7, wherein said at least one organic acid is fatty acid having from about 14 to about 36 carbon atoms.

9. The mould release composition according to claim 1, wherein said emulsion further comprises at least one ester of polyalkylene glycol and oleic acid.

10. The mould release composition according to claim 1, wherein said emulsion further comprises at least one ether surfactant.

11. The mould release composition according to claim 10, wherein said at least one ether surfactant is an alkyl substituted phenol polyglycol ether or an ethylene oxide/propylene oxide block copolymer.

12. The mould release composition according to claim 1, wherein the aqueous emulsion further comprises from 1 to 25% by weight of colloidal silica based on the total weight of the mould release composition.

13. The mould release composition according to claim 1, wherein the aqueous emulsion further comprises from 2 to 15% by weight of colloidal silica based on the total weight of the composition.

14. The mould release composition according to claim 1, wherein the aqueous emulsion further comprises a dihydric alkanol, ammonia, a saturated fatty acid, a mono unsaturated fatty acid ester, a semi solid mixture of hydrocarbons, paraffin oil, an acetic acid monoglyceride ester, in water, and colloidal silica.

15. A method for producing a mould release composition of claim 1, the method comprising:

a) preparing an oil-in-water emulsion by adding the one or more organic acids, such as fatty acids, one or more ester surfactants and/or one or more ether surfactants to water, homogenizing the emulsion to give oil droplets having a size below 5 μ

m,

b) preparing an aqueous suspension of colloidal silica, and

c) adding the suspension of colloidal silica prepared in step b) to the emulsion prepared in step a).

16. The method according to claim 15 wherein the emulsion is homogenized to give oil droplets having a size below 1 μ

m.

17. A method of releasing a moulded concrete body from a mold, the method comprising:

applying the mould release composition according to claim 1 as a mould release agent or surface hardener for improving the release of the moulded concrete body from the mould by applying an effective amount of the mould release composition to the surfaces of the mould that are to be in contact with the concrete.

18. A method for casting a concrete product, the method comprising:

a) providing a mould of a shape corresponding to the desired product,

b) applying an effective amount of a mould release composition according to claim 1 to the surfaces of the mould that are to be in contact with the concrete,

c) pouring concrete into the mould,

d) allowing the concrete to harden at least partially, and

e) de-moulding the concrete product.