SULFOPOLYESTERS FOR PAPER STRENGTH AND PROCESS

• US 20100269995A1
• Filed: 04/22/2010
• Published: 10/28/2010
• Est. Priority Date: 04/24/2009
• Status: Active Grant

• Current Assignee: Eastman Chemical Company
• Original Assignee: Eastman Chemical Company
• Inventors: Klosiewicz, Daniel William, Mitchell, Marvin Lynn, Mitchell, Melvin Glenn, Gupta, Rakesh Kumar
• Granted Patent: US 8,512,519 B2
• Time in Patent Office: Days
• US Class Current: 162/135
• CPC Class Codes: D21H 17/58 obtained by reactions forming in the main chain of the macromolecule a linkage containing sulfur
• CPC Class Codes: D21H 19/28 Polyesters
• CPC Class Codes: D21H 21/18 Reinforcing agents
• CPC Class Codes: D21H 21/20 Wet strength agents

Abstract

Sulfopolyester thermoplastic resins provide advantages in papermaking processes and in paper products including paperboard. Improvements in wet strength and dry strength of paper products are achieved by addition of sulfopolyester thermoplastic resins and cationic strength additives during the paper making process. The use of sulfopolyester thermoplastic resins in paper products also significantly enhances the repulpability of the paper.

Claims

1. A repulpable paper product comprising:

papermaking fibers;

a cationic strength additive; and

a thermoplastic sulfopolyester resin.

2. The repulpable paper products of claim 1 wherein the sulfopolyester resin comprises (i) residues of one or more dicarboxylic acids;

(ii) about 4 to about 40 mole %, based on the total repeating units, of residues of at least one sulfomonomer having 2 functional groups and one or more sulfonate groups attached to an aromatic or cycloaliphatic ring wherein said functional groups are hydroxyl, carboxyl, or a combination thereof;

(iii) one or more diol residues wherein at least 25 mole %, based on the total diol residues, is a poly(ethylene glycol) having a structure H—

(OCH₂—

CH₂)_n—

OH wherein n is an integer in the range of 2 to about 500; and

(iv) 0 to about 25 mole %, based on the total repeating units, of residues of a branching monomer having 3 or more functional groups wherein said functional groups are hydroxyl, carboxyl, or a combination thereof.

3. The repulpable paper products of claim 2 wherein the dicarboxylic acids are selected from aliphatic diacids, cycloaliphatic dicarboxylic acids, aromatic dicarboxylic acids, and combinations thereof.

4. The repulpable paper products of claim 3 wherein the dicarboxylic acids are selected from succinic, glutaric, adipic, azelaic, sebacic, fumaric, maleic, itaconic, 1,3-cyclohexane dicarboxylic, 1,4-cyclohexanedicarboxylic, diglycolic, 2,5-norbornanedicarboxylic, phthalic, terephthallc, 1,4-naphthalenedlcarboxylic, 2,5-naphthalenedicarboxylic, 2,6-naphthalenedicarboxylic, 2,7-naphthalenedicarboxylic, diphenic, 4,4′

-oxydibenzoic, 4,4′

-sulfonyldibenzoic, isophthalic, and combinations thereof.

5. The repulpable paper products of claim 2 wherein the sulfomonomer is a metal sulfonate salt of a sulfophthalic acid, sulfoterephthalic acid, sulfoisophthalic acid, or combinations thereof.

6. The repulpable paper products of claim 2 wherein the diol residues are selected from ethylene glycol, diethylene glycol, triethylene glycol, poly(ethylene) glycols, 1,3-propanediol, 2,4-dimethyl-2-ethylhexane-1,3-diol, 2,2-dimethyl-1,3-propanediol, 2-ethyl-2-butyl-1,3-propanediol, 2-ethyl-2-isobutyl-1,3-propanediol, 1,3-butanedlol, 1,4-butanediol, 1,5-pentanediol, 1,6-hexanediol, 2,2,4-trimethyl-1,6-hexanediol, thiodiethanol, 1,2-cyclohexanedimethanol, 1,3-cyclohexanedimethanol, 1,4-cyclohexanedimethanol, 2,2,4,4-tetramethyl-1,3-cyclobutanediol, p-xylylenediol, and combinations thereof.

7. The repulpable paper products of claim 2 wherein the branching monomer is 1,1,1-trimethylol propane, 1,1,1-trimethylolethane, glycerin, pentaerythritol, erythritol, threitol, dipentaerythritol, sorbitol, trimellitic anhydride, pyromellitic dianhydride, dimethylol propionic acid, or combinations thereof.

8. The repulpable paper products of claim 1 wherein the cationic strength additive is selected from polyacrylamide resins, polyamide epihalohydrin resins polyamine epihalohydrin resins, polyamidoamine epichalohydrin resins, polyalkyleneimine resins, urea-formaldehyde resins, melamine-formaldehyde resins, cationic polysaccharides or combinations thereof.

9. The repulpable paper products of claim 8 wherein the cationic strength additive is selected from cationic glyoxylated polyacrylamide resins or polyamidoamine epichlorohydrin resins.

10. The repulpable paper products according to claim 1 wherein the papermaking fibers are selected from woody fibers, softwood fibers, hardwood fibers, non-woody fibers, synthetic polymeric fibers, recycled fibers, glass fibers, or combinations thereof.

11. The repulpable paper products according to claim 10 wherein the synthetic polymeric fibers are greater than 50% of the total papermaking fiber.

12. The repulpable paper products according to claim 10 wherein the synthetic polymer fibers are greater than 70% of the total papermaking fiber.

13. The repulpable paper products according to claim 11 or 12 wherein said synthetic polymeric fibers have a mean fiber diameter of less than 5 microns.

14. The repulpable paper products of claim 1 wherein the amount of cationic strength additive is about 0.25 weight % to about 3 weight % on a dry basis and the amount of thermoplastic sulfopolyester resin is about 0.25 to about 3.00 weight %, on a dry basis relative to the weight of papermaking fiber.

15. The repulpable paper products of claim 1 wherein the amount of cationic strength additive is about 0.25 weight % to about 2 weight % on a dry basis and the amount of thermoplastic sulfopolyester resin is about 0.25 to about 2 weight %, on a dry basis relative to the weight of papermaking fiber.

16. The repulpable paper product of claim 1 wherein the amounts of cationic strength additive is about 0.25 weight % to about 1.5 weight % on a dry basis and the amount of thermoplastic sulfopolyester resin is about 0.25 to about 1.5 weight %, on a dry basis relative to the weight of papermaking fiber.

17. The repulpable paper products of claim 1 wherein the ratio of thermoplastic sulfopolyester resin to cationic strength additive is about 5:

1 to about 1;

5.

18. The repulpable paper products of claim 1 wherein the ratio of sulfopolyester to cationic strength additive is about 1:

1

19. A method of improving the wet-strength of cellulosic paper comprising adding to the papermaking fibers during the papermaking process a cationic strength additive;

and a sulfopolyester thermoplastic resin.

20. The method of claim 19 wherein the cationic strength additive and sulfopolyester thermoplastic resin are added to an aqueous slurry of papermaking fibers during the papermaking process.

21. The method of claim 19 wherein said cationic strength additive is added to an aqueous slurry of papermaking fibers and the sulfopolyester thermoplastic resin is applied onto a paper web resulting from the dewatering of said papermaking fibers.

22. The method of claim 21 wherein the thermoplastic sulfopolyester resin is applied to the paper web by spray application.

23. The method of claim 19 wherein the resulting paper products exhibit enhanced repulpability.

24. A paper product comprising:

papermaking fibers consisting of one or more of woody fibers, softwood fibers, hardwood fibers, non-woody fibers, synthetic polymeric fibers, recycled fibers, or glass fibers;

cationic strength additives consisting of one or more of polyacrylamide resins, polyamide epihalohydrin resins polyamine epihalohydrin resins, polyamidoamine epichalohydrin resins, polyalkyleneimine resins, urea-formaldehyde resins, melamine-formaldehyde resins, or cationic polysaccharides; and

thermoplastic sulfopolyester resins comprising (i) residues of one or more dicarboxylic acids;

(ii) about 4 to about 40 mole %, based on the total repeating units, of residues of at least one sulfomonomer having 2 functional groups and one or more sulfonate groups attached to an aromatic or cycloaliphatic ring wherein said functional groups are hydroxyl, carboxyl, or a combination thereof;

(iii) one or more diol residues wherein at least 25 mole %, based on the total diol residues, is a poly(ethylene glycol) having a structure H—

(OCH₂—

CH₂)_n—

OH wherein n is an integer in the range of 2 to about 500; and

(iv) 0 to about 25 mole %, based on the total repeating units, of residues of a branching monomer having 3 or more functional groups wherein said functional groups are hydroxyl, carboxyl, or a combination thereof.