METHODS OF MAKING AN IMPROVED PHOTORECEPTOR OUTER LAYER

• US 20110014563A1
• Filed: 07/20/2009
• Published: 01/20/2011
• Est. Priority Date: 07/20/2009
• Status: Active Grant

• Current Assignee: Xerox Corporation (Xerox Holdings Corp.)
• Original Assignee: Xerox Corporation (Xerox Holdings Corp.)
• Inventors: Kim, Woo Soo, Gagnon, Yvan, Hu, Nan-Xing, Junginger, Johann
• Granted Patent: US 8,227,166 B2
• Time in Patent Office: Days
• US Class Current: 430/127
• CPC Class Codes: G03G 5/14713 Macromolecular material
• CPC Class Codes: G03G 5/14726 Halogenated polymers
• CPC Class Codes: G03G 5/14747 obtained otherwise than by reactions only involving carbon-to-carbon unsaturated bonds
• CPC Class Codes: G03G 5/14752 Polyesters
• CPC Class Codes: G03G 5/14791 Macromolecular compounds characterised by their structure, e.g. block polymers, reticulated polymers, or by their chemical properties, e.g. by molecular weight or acidity

Abstract

The presently disclosed embodiments relate generally to layers that are useful in imaging apparatus members and components, for use in electrophotographic, including digital, apparatuses. Embodiments pertain to an improved electrophotographic imaging member incorporating an outer layer having a nano- to micron-scale pattern imprinted into its surface to lower friction with the cleaning blade and improve print quality and performance. Embodiments also pertain to methods for making the improved imaging member.

Claims

1. A method for forming an imaging member having a patterned surface in the outer layer, comprising:

providing a mold for imprinting, wherein the mold comprises a pattern on one face of the mold, the pattern comprising an array of periodically ordered protrusions or indentations;

providing an imaging member comprising a substrate and disposed thereover the substrate a soft outer layer coating for being imprinted;

pressing the patterned face of the mold and the outer layer coating of the imaging member together in a manner such that the pattern structure of the mold is replicated onto the outer layer coating; and

hardening the outer layer coating to form a patterned structure on an outer surface of the imaging member.

2. The method of claim 1, wherein the indentations or protrusions on the mold have a regular shape selected from the group consisting of circles, rods, ovals, squares, triangles, polygons, and mixtures thereof.

3. The method of claim 1, wherein each of the indentations or protrusions has a perimeter of from about 5 nanometers to about 200 microns.

4. The method of claim 1, wherein the indentations have a depth of from about 5 nanometers to about 5 microns, and the protrusions have height of from about 5 nanometers to about 5 microns.

5. The method of claim 1, wherein the array of indentations or protrusions are regularly positioned over a surface of the outer layer.

6. The method of claim 1, wherein the indentations or protrusions have a two-dimensional periodicity from hexagonal arrays, tetragonal arrays, quasi-crystal arrays, and linear arrays, and mixtures thereof.

7. The method of claim 1, wherein the array of indentations or protrusions have a center-to-center distance of from about 5 nanometers to about 500 microns.

8. The method of claim 1, wherein the mold comprises an elastic material.

9. The method of claim 8, wherein the elastic material is selected from the group consisting of polysiloxane, polyurethane, polyester, fluoro-silicone, and mixtures thereof.

10. The method of claim 1, wherein the outer layer coating of the imaging member comprises a charge transport component and a polymer binder.

11. The method of claim 10, wherein the charge transport component comprises a tertiary arylamine selected from the group consisting of N,N′

-diphenyl-N,N′

-bis(3-methylphenyl)-(1,1′

-biphenyl)-4,4′

-diamine, N,N′

-diphenyl-N,N′

-bis(4-methylphenyl)-(1,1′

-biphenyl)-4,4′

-diamine, N,N,N′

,N′

-tetrakis(4-methylphenyl)-1,1′

-biphenyl)-4,4′

-diamine, N,N′

-bis(4-butylphenyl)-N,N′

-di-p-tolyl-[p-terphenyl]-4,4′

-diamine, and N,N′

-bis(4-butylphenyl)-N,N′

-di-m-tolyl-[p-terphenyl]-4,4′

-diamine, and mixtures thereof.

12. The method of claim 1, wherein the outer layer coating of the imaging member comprises a curable composition further comprising a charge transport component and a curing agent.

13. The method of claim 12, wherein the curing agent is selected from the group consisting of a melamine-formaldehyde resin, a phenol resin, an isocyalate or a masking isocyalate compound, an acrylate resin, a polyol resin, or the mixture thereof.

14. The method of claim 12, wherein the charge transport component is comprised of a tertiary arylamine having at least a curable functional group selected from the group consisting of a hydroxyl, a hydroxymethyl, an alkoxymethyl, a hydroxyalkyl having from 1 to about 15 carbons, an acrylate, and the mixture thereof.

15. The method of claim 1, wherein the imaging member further comprises, positioned in between the substrate and the outer layer coating, a charge generation layer comprising a photosensitive pigment selected from the group consisting of metal free phthalocyanine, titanyl phthalocyanine, chlorogallium phthalocyanine, hydroxygallium phthalocyanine, and a mixture of alkylhydroxy gallium phthalocyanine and hydroxygallium phthalocyanine, and a perylene, and the mixtures thereof.

16. The method of claim 1, wherein the hardening step is achieved by a process selected from the group consisting of thermal drying, thermal curing, photo-induced curing, electron beam cuing, and mixtures thereof.

17. The method of claim 1, wherein the mold further comprises a substrate to support the pattern, and the substrate is made of a material selected from the group consisting of a metal, a polymer, a glass, a ceramic, and wood.

18. The method of claim 17, wherein the substrate is in a cylinder, a drum, or a belt configuration.

19. The method of claim 1, further comprising applying a release agent onto the mold prior to imprinting.

20. The method of claim 19, wherein the release agent comprises a low surface energy material.

21. A method for forming an imaging member having a patterned surface in the outer layer, comprising:

providing a mold for imprinting, wherein the mold comprises a pattern on one face of the mold, the pattern comprising an array of periodically ordered protrusions or indentations;

providing an imaging member comprising a substrate and disposed thereover the substrate a soft outer layer coating for being imprinted;

pressing the patterned face of the mold and the outer layer coating of the imaging member together in a manner that the pattern structure of the mold is replicated onto the outer layer coating; and

hardening the outer layer coating to form a patterned structure on an outer surface of the imaging member, wherein the periodically ordered protrusions have a height of from about 100 nanometers to about 2 microns and the indentations have a depth of from about 100 nanometers to about 2 microns.

22. A method for forming an imaging member having a patterned surface in the outer layer, comprising:

providing a mold for imprinting, wherein the mold comprises a pattern on one face of the mold, the pattern comprising an array of periodically ordered protrusions or indentations;

providing an imaging member comprising a substrate and disposed thereover the substrate a soft outer layer coating for being imprinted;

pressing the patterned face of the mold and the outer layer coating of the imaging member together in a manner that the pattern structure of the mold is replicated onto the outer layer coating; and

hardening the outer layer coating to form a patterned structure on an outer surface of the imaging member, wherein the array of periodically ordered protrusions or indentations are regularly positioned over a surface of the outer layer and further wherein each of the indentations and protrusions has a perimeter of from about 5 nanometers to about 200 microns.