STRESS MANAGEMENT FOR TENSILE FILMS
First Claim
1. A method of forming a silicon oxide layer on a substrate containing a trench, the method comprising:
- transferring the substrate into a substrate processing region in a substrate processing chamber;
flowing a plasma precursor into a remote plasma region to form plasma effluents;
combining the plasma effluents with a flow of a silicon-containing precursor in the substrate processing region, wherein the flow of the silicon-containing precursor has not been excited by a plasma;
forming a silicon-and-nitrogen-containing layer on the substrate and in the trench;
forming a compressive capping layer over the silicon-and-nitrogen-containing layer; and
heating the substrate in an oxygen-containing atmosphere to convert the carbon-free silicon-and-nitrogen containing layer to the silicon oxide layer.
1 Assignment
0 Petitions
Accused Products
Abstract
The formation of a gap-filling silicon oxide layer with reduced tendency towards cracking is described. The deposition involves the formation of a flowable silicon-containing layer which facilitates the filling of trenches. Subsequent processing at high substrate temperature causes less cracking in the dielectric film than flowable films formed in accordance with methods in the prior art. A compressive liner layer deposited prior to the formation of the gap-filling silicon oxide layer is described and reduces the tendency for the subsequently deposited film to crack. A compressive capping layer deposited after a flowable silicon-containing layer has also been determined to reduce cracking. Compressive liner layers and compressive capping layers can be used alone or in combination to reduce and often eliminate cracking. Compressive capping layers in disclosed embodiments have additionally been determined to enable an underlying layer of silicon nitride to be transformed into a silicon oxide layer.
-
Citations
9 Claims
-
1. A method of forming a silicon oxide layer on a substrate containing a trench, the method comprising:
-
transferring the substrate into a substrate processing region in a substrate processing chamber; flowing a plasma precursor into a remote plasma region to form plasma effluents; combining the plasma effluents with a flow of a silicon-containing precursor in the substrate processing region, wherein the flow of the silicon-containing precursor has not been excited by a plasma; forming a silicon-and-nitrogen-containing layer on the substrate and in the trench; forming a compressive capping layer over the silicon-and-nitrogen-containing layer; and heating the substrate in an oxygen-containing atmosphere to convert the carbon-free silicon-and-nitrogen containing layer to the silicon oxide layer. - View Dependent Claims (2, 3, 4, 5, 6, 7, 8, 9)
-
Specification