METHODS FOR MAKING SILICONE HYDROGEL LENSES FROM WATER-BASED LENS FORMULATIONS

• US 20110140292A1
• Filed: 12/09/2010
• Published: 06/16/2011
• Est. Priority Date: 12/14/2009
• Status: Active Grant

• Current Assignee: Alcon Incorporated
• Original Assignee: Novartis Ag
• Inventors: Winterton, Lynn Cook, Chang, Frank
• Granted Patent: US 9,005,492 B2
• Time in Patent Office: Days
• US Class Current: 264/1.1
• CPC Class Codes: B29D 11/00038 Production of contact lenses
• CPC Class Codes: B29D 11/00048 composed of parts with dissimilar composition B29D11/00057 takes precedence
• CPC Class Codes: C08L 101/14 the macromolecular compounds being water soluble or water swellable, e.g. aqueous gels
• CPC Class Codes: C08L 83/04 Polysiloxanes
• CPC Class Codes: G02B 1/043 Contact lenses

Abstract

Described herein are methods for producing silicone hydrogel lenses. The methods involve introducing into a mold a water-based lens-forming composition, curing the lens-forming composition in a mold to form the lens, and removing the lens from the mold. The lens-forming composition comprises (i) a polysiloxane-containing vinylic monomer or macromer, (ii) at least one hydrophilic vinylic monomer, (iii) a surfactant, and, and (iv) water. The surfactant is polysiloxane-containing surfactant that is free of actinically-polymerizable groups and is a copolymer having from about 10% to about 40% by weight of one or more polysiloxane segments and from about 90% to about 60% by weight hydrophilic units and/or segments. The methods permit the use of water as a solvent and reduce the need for organic solvents. Additionally, the lenses produced by the methods can have improved properties such oxygen permeability.

Claims

1. A method for making a silicone hydrogel contact lens, wherein the method comprises:

a. introducing into a mold a water-based lens-forming composition comprising (i) a polysiloxane-containing vinylic monomer or macromer;

(ii) optionally a hydrophilic vinylic monomer;

(iii) a polysiloxane-containing surfactant, and (iv) water, wherein the polysiloxane-containing surfactant is liquid at room temperature, free of actinically-polymerizable groups, and a copolymer comprising from about 10% to about 40% by weight of one or more polysiloxane segments and from about 90% to about 60% by weight hydrophilic units and/or segments, wherein the polysiloxane-containing surfactant is present in an amount sufficient to dissolve the polysiloxane-containing vinylic monomer or macromer in water to form a substantially clear solution;

b. curing the composition to produce the lens; and

c. removing the lens from the mold.

2. The method of claim 1, wherein the water-based lens-forming composition comprises a polysiloxane-containing vinylic macromer comprising from about 50% to about 99% by weight of one or more polysiloxane segments.

3. The method of claim 2, wherein the polysiloxane-containing vinylic monomer or macromer comprises a monomethacrylated or monoacrylated polydimethylsiloxane;

a dimethacrylated or diacrylated polydimethylsiloxane;

a vinyl carbonate-terminated polydimethylsiloxane;

a vinyl carbamate-terminated polydimethylsiloxane;

a vinyl terminated polydimethylsiloxane;

a methacrylamide-terminated polydimethylsiloxane;

an acrylamide-terminated polydimethylsiloxane;

an acrylate-terminated polydimethylsiloxane;

a methacrylate-terminated polydimethylsiloxane;

bis-3-methacryloxy-2-hydroxypropyloxypropyl polydimethylsiloxane;

N,N,N′

,N′

-tetrakis(3-methacryloxy-2-hydroxypropyl)-alpha,omega-bis-3-aminopropyl-polydimethylsiloxane;

a polysiloxanylalkyl(meth)acrylic monomer, or any combination thereof.

4. The method of claim 2, wherein the polysiloxane-containing vinylic macromer comprises a silicone-containing prepolymer.

5. The method of claim 2, wherein the water-based lens-forming composition comprises at least one hydrophilic vinylic monomer which is N,N-dimethylacrylamide (DMA), N,N-dimethylmethacrylamide (DMMA), 2-acrylamidoglycolic acid, 3-acryloylamino-1-propanol, N-hydroxyethyl acrylamide, N-[tris(hydroxymethyl)methyl]-acrylamide, N-methyl-3-methylene-2-pyrrolidone, 1-ethyl-3-methylene-2-pyrrolidone, 1-methyl-5-methylene-2-pyrrolidone, 1-ethyl-5-methylene-2-pyrrolidone, 5-methyl-3-methylene-2-pyrrolidone, 5-ethyl-3-methylene-2-pyrrolidone, 1-n-propyl-3-methylene-2-pyrrolidone, 1-n-propyl-5-methylene-2-pyrrolidone, 1-isopropyl-3-methylene-2-pyrrolidone, 1-isopropyl-5-methylene-2-pyrrolidone, 1-n-butyl-3-methylene-2-pyrrolidone, 1-tert-butyl-3-methylene-2-pyrrolidone, 2-hydroxyethylmethacrylate (HEMA), 2-hydroxyethyl acrylate (HEA), hydroxypropyl acrylate, hydroxypropyl methacrylate (HPMA), trimethylammonium 2-hydroxy propylmethacrylate hydrochloride, aminopropyl methacrylate hydrochloride, dimethylaminoethyl methacrylate (DMAEMA), glycerol methacrylate (GMA), N-vinyl-2-pyrrolidone (NVP), allyl alcohol, vinylpyridine, N-vinyl formamide, N-vinyl acetamide, N-vinyl isopropylamide, N-vinyl-N-methyl acetamide, allyl alcohol, N-vinyl caprolactam, or any combination thereof.

6. The method of claim 1, wherein the surfactant is obtained by copolymerization of a mixture comprising (a) from about 10% to about 40% by weight of at least one linear polysiloxane-containing compound terminated with two first or second functional groups, (b) from about 90% to about 60% by weight of (i) at least one linear hydrophilic compound or polymer with two terminal first or second functional groups and (ii) at least one hydrophilic polymer with only one first or second functional group, and (c) one or more branching agents which independently of each other are an organic compound with three or more first or second functional groups, wherein the first and second functional groups are different from each other and selected from the group consisting of amine group, hydroxyl, carboxy, isocyanate, epoxy, and acid halide group, and wherein the first and second functional groups are coreactive with each other in the presence or absence of a coupling agent to form a covalent linkage.

7. The method of claim 1, wherein the surfactant is obtained by copolymerization of a mixture comprising (1) from about 10% to about 40% by weight of one or more polysiloxane-containing macromers with one or two ethylenically unsaturated groups and (2) from about 90% to about 60% by weight of one or more hydrophilic vinylic monomers and/or hydrophilic prepolymers.

8. The method of claim 1, wherein the surfactant comprises at least one linear polysiloxane polymer end-capped at least one of the two ends of the polysiloxane segment with a hydrophilic polymer chain through a linkage.

9. The method of claim 1, wherein the surfactant is defined by formula (2):

10. The method of claim 1, wherein the water-based lens-forming composition comprises a polysiloxane-containing vinylic macromer has the formula I and a polysiloxane-containing surfactant has the formula II:

CP-PAO-ALK-PDMS-ALK-PAO-CP 

 

(I)

X-PAO-ALK-PDMS-ALK-PAO-X 

 

(II)

where PDMS is a divalent poly(disubstituted siloxane), ALK is an alkylene or alkylenoxy group having at least 3 carbon atoms, DU is a diurethane-containing group, PAO is a divalent polyoxyalkylene of formula —

(R^aO)_n—

(R^bO)_m—

(R^cO)_t—

in which R^a, R^b, and R^c independent of one other are ethylene (—

CH₂CH₂—

) or propylene (—

CH(CH₃)—

CH₂—

) divalent radical and n, m, and 1 independent of one other is from 0 to 100, provided that the sum of n, m and 1 is from 3 to 100 and at least one of R^a, R^b, and R^c is ethylene divalent radical, CP is an acrylate and methacrylate, and X is a non-actinically-polymerizable group.

11. The method of claim 1, wherein the lens-forming composition further comprises a hydrophobic monomer.

12. The method of claim 11, wherein the hydrophobic monomer comprises methylacrylate, ethyl-acrylate, propylacrylate, isopropylacrylate, cyclohexylacrylate, 2-ethylhexylacrylate, methylmethacrylate, ethylmethacrylate, propylmethacrylate, vinyl acetate, vinyl propionate, vinyl butyrate, vinyl valerate, styrene, chloroprene, vinyl chloride, vinylidene chloride, acrylonitrile, 1-butene, butadiene, methacrylonitrile, vinyl toluene, vinyl ethyl ether, perfluorohexylethyl-thio-carbonyl-aminoethyl-methacrylate, isobornyl methacrylate, trifluoroethyl methacrylate, hexafluoro-isopropyl methacrylate, hexafluorobutyl methacrylate, or any combination thereof.

13. The method of claim 11, wherein the lens-forming composition further comprises a silicone-containing vinylic monomer selected from the group consisting of N-[tris(trimethylsiloxy)silylpropyl]-(meth)acrylamide, N-[tris(dimethylpropylsiloxy)-silylpropyl]-(meth)acrylamide, N-[tris(dimethylphenylsiloxy)silylpropyl](meth)acrylamide, N-[tris(dimethylethylsiloxy)silylpropyl](meth)acrylamide, N-(2-hydroxy-3-(3-(bis(trimethylsilyloxy)methylsilyl)propyloxy)propyl)-2-methyl acrylamide;

N-(2-hydroxy-3-(3-(bis(trimethylsilyloxy)methylsilyl)propyloxy)propyl)acrylamide;

N,N-bis[2-hydroxy-3-(3-(bis(trimethylsilyloxy)methylsilyl) propyloxy)propyl]-2-methyl acrylamide;

N,N-bis[2-hydroxy-3-(3-(bis(trimethylsilyloxy)methylsilyl)propyloxy)propyl]acrylamide;

N-(2-hydroxy-3-(3-(tris(trimethylsilyloxy)silyl)propyloxy)propyl)-2-methyl acrylamide;

N-(2-hydroxy-3-(3-(tris(trimethylsilyloxy)silyl)propyloxy)propyl)acrylamide;

N,N-bis[2-hydroxy-3-(3-(tris(trimethylsilyloxy)silyl)propyloxy)propyl]-2-methyl acrylamide;

N,N-bis[2-hydroxy-3-(3-(tris(trimethylsilyloxy)silyl)propyloxy)propyl]acrylamide;

N-[2-hydroxy-3-(3-(t-butyldimethylsilyl)propyloxy)propyl]-2-methyl acrylamide;

N-[2-hydroxy-3-(3-(t-butyldimethylsilyl)propyloxy)propyl]acrylamide;

N,N-bis[2-hydroxy-3-(3-(t-butyldimethylsilyl)propyloxy)propyl]-2-methyl acrylamide;

N,N-bis[2-hydroxy-3-(3-(t-butyldimethylsilyl)propyloxy)propyl]acrylamide;

3-methacryloxy propylpentamethyldisiloxane, tris(trimethylsilyloxy)silylpropyl methacrylate (TRIS), (3-methacryloxy-2-hydroxypropyloxy)propylbis(trimethylsiloxy)methylsilane), (3-methacryloxy-2-hydroxypropyloxy)propyltris(trimethylsiloxy)silane, 3-methacryloxy-2-(2-hydroxyethoxy)-propyloxy)propylbis(trimethylsiloxy)methylsilane, N-2-methacryloxyethyl-O-(methyl-bis-trimethylsiloxy-3-propyl)silyl carbamate, 3-(trimethylsilyl)propylvinyl carbonate, 3-(vinyloxycarbonylthio)propyl-tris(trimethyl-siloxy)silane, 3-[tris(trimethylsiloxy)silyl]propylvinyl carbamate, 3-[tris(trimethylsiloxy)silyl]propyl allyl carbamate, 3-[tris(trimethylsiloxy)silyl]propyl vinyl carbonate, t-butyldimethyl-siloxyethyl vinyl carbonate;

trimethylsilylethyl vinyl carbonate, trimethylsilylmethyl vinyl carbonate), and combinations thereof.

14. The method of claim 11, wherein the lens-forming composition further comprises a crosslinker selected from the group consisting of tetraethyleneglycol diacrylate, triethyleneglycol diacrylate, ethyleneglycol diacylate, diethyleneglycol diacrylate, tetraethyleneglycol dimethacrylate, triethyleneglycol dimethacrylate, ethyleneglycol dimethacylate, diethyleneglycol dimethacrylate, trimethylopropane trimethacrylate, pentaerythritol tetramethacrylate, bisphenol A dimethacrylate, vinyl methacrylate, ethylenediamine dimethyacrylamide, ethylenediamine diacrylamide, glycerol dimethacrylate, triallyl isocyanurate, triallyl cyanurate, allylmethacrylate, allylmethacrylate, 1,3-bis(methacrylamidopropyl)-1,1,3,3-tetrakis(trimethylsiloxy)disiloxane, N,N′

-methylenebisacrylamide, N,N′

-methylenebismethacrylamide, N,N′

-ethylenebisacrylamide, N,N′

-ethylenebismethacrylamide, 1,3-bis(N-methacrylamidopropyl)-1,1,3,3-tetrakis-(trimethylsiloxy)disiloxane, 1,3-bis(methacrylamidobutyl)-1,1,3,3-tetrakis(trimethylsiloxy)-disiloxane, 1,3-bis(acrylamidopropyl)-1,1,3,3-tetrakis(trimethylsiloxy)disiloxane, 1,3-bis(methacryloxyethylureidopropyl)-1,1,3,3-tetrakis(trimethylsiloxy)disiloxane, and combinations thereof. A preferred cross-linking agent is tetra(ethyleneglycol) diacrylate, tri(ethyleneglycol) diacrylate, ethyleneglycol diacrylate, di(ethyleneglycol) diacrylate, methylenebisacrylamide, triallyl isocyanurate, triallyl cyanurate, and combinations thereof.

15. The method of claim 14, wherein the lens-forming composition further comprises a UV-absorber, a tinting agent, an antimicrobial agent, an inhibitor, a filler, or any combination thereof.