PROCESS OF MANUFACTURING A CURVED MEMBER HAVING A HIGH-GRADE DESIGN SURFACE AND MEMBER MANUFACTURED BY THE PROCESS

• US 20120225241A1
• Filed: 10/15/2010
• Published: 09/06/2012
• Est. Priority Date: 10/20/2009
• Status: Active Grant

• Current Assignee: Teijin Chemicals Ltd. (Teijin Limited)
• Original Assignee: Teijin Chemicals Ltd. (Teijin Limited)
• Inventors: Suga, Takehiro, Niimi, Ryo, Hotaka, Toshiaki, Kashima, Keiichi, Miura, Junichi
• Granted Patent: US 9,296,143 B2
• Time in Patent Office: Days
• US Class Current: 428/80
• CPC Class Codes: B29C 43/18 incorporating preformed parts or layers, e.g. compression moulding around inserts or for coating articles B29C43/206 takes precedence
• CPC Class Codes: B29C 45/0055 Shaping
• CPC Class Codes: B29C 45/561 Injection-compression moulding
• CPC Class Codes: B29C 51/02 Combined thermoforming and manufacture of the preform
• CPC Class Codes: B29C 51/08 Deep drawing or matched-mould forming, i.e. using mechanical means only
• CPC Class Codes: B29C 53/04 of plates or sheets B29C63/04 takes precedence; bending or folding paper B31F1/0003; folding films B65H45/00
• CPC Class Codes: B29C 53/84 Heating or cooling
• CPC Class Codes: B29K 2069/00 Use of PC, i.e. polycarbonates or derivatives thereof, as moulding material
• CPC Class Codes: B29K 2105/12 of short lengths, e.g. chopped filaments, staple fibres or bristles
• CPC Class Codes: B29L 2031/3052 Windscreens
• CPC Class Codes: B29L 2031/7782 Glazing

Abstract

It is an object of the present invention to provide a process capable of manufacturing various types of curved members having a high-grade design surface which are used as glazing members for means of transport such as automobiles at a low cost.

The present invention is the process of manufacturing a curved member having a high-grade design surface, comprises the steps of:

• (1) preparing a sheet having a high-grade design surface by injection compression molding a resin material containing a thermoplastic resin;
• (2) preheating the sheet at a temperature of (Tg+5)° C. to (Tg+70)° C. (Tg(° C.) is the glass transition temperature of the resin material) to soften it; and
• (3) applying pressure to the softened sheet to curve the high-grade design surface.

Claims

1. A process of manufacturing a curved member having a high-grade design surface, comprising the steps of:

(1) preparing a sheet having a high-grade design surface by injection compression molding a resin material containing a thermoplastic resin (step (1));

(2) preheating the sheet at a temperature of (Tg+5)°

C. to (Tg+70)°

C. (Tg(°

C.) is the glass transition temperature of the resin material) to soften it (step (2)); and

(3) applying pressure to the softened sheet to curve the high-grade design surface (step (3)).

2. The manufacturing process according to claim 1, wherein the high-grade design surface has a surface roughness (Ra) of not more than 0.06 μ

m and an average amplitude (y) of a surface waviness component of not more than 0.5 μ

m, and y satisfies the following expression (1) when the average wavelength (x) of the surface waviness component is detected on both sides.

Y≦

0.0004x²+0.0002x 

 

(1)

(In the above expression (1), y is the average amplitude (Wa) (μ

m) of a filtered waviness curve specified in JIS B0610 of the sheet and x is the average wavelength (WSm) (mm) of the filtered waviness curve of the sheet.)

3. The manufacturing process according to claim 1, wherein the thermoplastic resin comprises a polycarbonate resin as the main component.

4. The manufacturing process according to claim 1, wherein the sheet is manufactured by an injection compression molding method in which a molten resin material is filled into a mold cavity from a single gate or from a plurality of gates by a cascade molding system in accordance with a sequential valve gating method.

5. The manufacturing process according to claim 4, wherein the sheet is manufactured by an injection compression molding method in which the molten resin material is filled into the mold cavity from a single gate.

6. The manufacturing process according to claim 1, wherein the step (3) is the step of curving the sheet by using a mold.

7. The manufacturing process according to claim 6, wherein pressure is applied to buffer pressure from the mold surface on the high-grade design surface of the sheet.

8. The manufacturing process according to claim 1, wherein the sheet is a printed sheet at least one side of which is printed with a pattern.

9. The manufacturing process according to claim 1 comprising the step of printing a pattern on at least one side of the sheet between the step (1) and the step (2) (step (P)).

10. The manufacturing process according to claim 1 comprising the step of coating at least one side of the sheet with a hard coating solution (step (C)).

11. The manufacturing process according to claim 1 comprising the step of removing an unrequired portion of the sheet (step (T)).

12. The manufacturing process according to claim 1 comprising the step of attaching another member to the curved member (step (A)).

13. The manufacturing process according to claim 1 comprising the step of fixing the obtained curved member to a final product (step (F)).

14. The manufacturing process according to claim 1, wherein the step (C) and the step (T) are carried out after the step (3) in the mentioned order.

15. The manufacturing process according to claim 1, wherein the curved member is translucent and satisfies the above expression (1).

16. A curved member having a high-grade design surface manufactured by the process of claim 1.