ANTI-FOGGING ARTICLE AND ITS PRODUCTION PROCESS

• US 20130260145A1
• Filed: 05/29/2013
• Published: 10/03/2013
• Est. Priority Date: 12/07/2010
• Status: Abandoned Application

• Current Assignee: Asahi Glass Company, Limited (AGC, Inc.)
• Original Assignee: Asahi Glass Company, Limited (AGC, Inc.)
• Inventors: Kishikawa, Noriko, Saito, Tsuyoshi, Ishioka, Hideki
• Application Number:
  US13/904,550
• Publication Number:
  US 20130260145A1
• Time in Patent Office: Days
• US Class Current: 428/337
• CPC Class Codes: B32B 2250/02 2 layers
• CPC Class Codes: B32B 27/20 using fillers, pigments, thixotroping agents
• CPC Class Codes: B32B 27/38 comprising epoxy resins
• CPC Class Codes: C03C 17/3405 with at least two coatings of organic materials C03C17/36, C03C17/42 take precedence
• CPC Class Codes: C09K 3/18 for application to surfaces to minimize adherence of ice, mist or water thereto rendering particulate materials free flowing, in general, e.g. making them hydrophobic B01J2/30; Thawing or antifreeze materials for application to surfaces used in liquids for heat-transfer, heat-exchange or heat-storage or for the production of heat or cold other than by combustion, e.g. radiator liquids, C09K5/00
• CPC Class Codes: Y10T 428/266 of base or substrate
• CPC Class Codes: Y10T 428/31515 As intermediate layer
• CPC Class Codes: Y10T 428/31518 Next to glass or quartz

Abstract

An anti-fogging article having a substrate and an anti-fogging film on at least part of the surface of the substrate, wherein the anti-fogging film comprises a resin underlayer and a water-absorptive resin layer laminated in order on the substrate surface, the water-absorptive resin layer is composed mainly of a first cured epoxy resin obtained by reacting a water-absorptive resin layer-forming composition containing a first polyepoxide component consisting of a low molecular weight polyepoxide having molecular weight of from 200 to 800 and a high molecular weight polyepoxide having molecular weight of from 900 to 2,000 combined in mass ratio of from 30:70 to 70:30, and a first curing agent, and the resin underlayer is composed mainly of a second cured epoxy resin obtained by reacting a resin underlayer-forming composition containing a second polyepoxide component and a second curing agent, and has water absorption property lower than the water-absorptive resin layer.

Claims

1. An anti-fogging article having a substrate and an anti-fogging film on at least part of the surface of the substrate, wherein:

the anti-fogging film comprises a resin underlayer and a water-absorptive resin layer laminated in order on the substrate surface;

the water-absorptive resin layer is a water-absorptive resin layer composed mainly of a first cured epoxy resin obtained by reacting a water-absorptive resin layer-forming composition containing a first polyepoxide component consisting of a low molecular weight polyepoxide having a molecular weight of from 200 to 800 and a high molecular weight polyepoxide having a molecular weight of from 900 to 2,000 in a mass ratio of the low molecular weight polyepoxide;

the high molecular weight polyepoxide of from 30;

70 to 70;

30, and a first curing agent; and

the resin underlayer is a resin underlayer composed mainly of a second cured epoxy resin obtained by reacting a resin underlayer-forming composition containing a second polyepoxide component and a second curing agent, having water absorption property lower than that of the water-absorptive resin layer.

2. The anti-fogging article according to claim 1, wherein the molecular weight of the low molecular polyepoxide is from 300 to 700, and the molecular weight of the high molecular weight polyepoxide is from 900 to 1,450.

3. The anti-fogging article according to claim 1, wherein each of the high molecular weight polyepoxide and the low molecular weight polyepoxide is a glycidyl ether type polyepoxide having no aromatic nucleus.

4. The anti-fogging article according to claim 1, wherein the high molecular weight polyepoxide is selected from the group consisting of polyethylene glycol polyglycidyl ether, polyglycerin polyglycidyl ether and polyethylene glycol sorbitol polyglycidyl ether, and the low molecular weight polyepoxide is selected from the group consisting of glycerin polyglycidyl ether, polyglycerin polyglycidyl ether and sorbitol polyglycidyl ether.

5. The anti-fogging article according to claim 1, wherein the water-absorptive resin-forming composition contains from 15 to 30 mass % of the first polyepoxide component and from 3 to 20 mass % of the first curing agent, to the entire amount of the composition, and the resin underlayer-forming composition contains from 4 to 10 mass % of the second polyepoxide component and from 0.1 to 4.0 mass % of the second curding agent, to the entire amount of the composition.

6. The anti-fogging article according to claim 1, wherein each of the first curing agent and the second curding agent comprises an amine compound having active hydrogen.

7. The anti-fogging article according to claim 6, wherein the equivalent ratio of amine'"'"'s active hydrogens to epoxy groups in all the components constituting the water-absorptive resin layer-forming composition is from 0.6 to 0.8, and the equivalent ratio of amine'"'"'s active hydrogens to epoxy groups in all the components constituting the rein underlayer-forming composition is from 1.2 to 1.5.

8. The anti-fogging article according to claim 6, wherein the first curing agent further includes an imidazole compound.

9. The anti-fogging article according to claim 8, wherein the content of the imidazole compound is from 1.0 to 20 mass % to the first polyepoxide component.

10. The anti-fogging article according to claim 1, wherein the anti-fogging film is free from peeling, cracks and whitening, in a test such that the anti-fogging film is formed on one side of a 2 mm-thick glass substrate, irradiated with light for 160 hours through the glass substrate from the non-film surface side without anti-fogging film of the glass substrate, using a sunshine carbon arc lamp weather resistance testing machine in accordance with WS D0205 (WAL-1 H), and further held in a constant temperature and constant humidity chamber at 85°

C. under 90% RH for 500 hours, and the surface of the anti-fogging film is washed with ethanol.

11. The anti-fogging article according to claim 1, wherein the second polyepoxide component consists of an aliphatic polyepoxide.

12. The anti-fogging article according to claim 1, wherein the water-absorptive resin layer-forming composition and the resin underlayer-forming composition further contain a silane coupling agent.

13. The anti-fogging article according to claim 12, wherein the content of the silane coupling agent is from 5 to 40 mass % to the total mass of the first polyepoxide component and the first curing agent in the water-absorptive resin layer-forming composition, and is from 5 to 50 mass % to the total mass of the second polyepoxide component and the second curing agent in the resin underlayer-forming composition.

14. The anti-fogging article according to claim 1, wherein the resin underlayer-forming composition further contains a tetraalkoxysilane and/or its oligomer.

15. The anti-fogging article according to claim 14, wherein the content of the tetraalkoxysilane and/or its oligomer is from 10 to 40 mass % to the total mass of the second polyepoxide component and the second curing agent.

16. The anti-fogging article according to claim 1, wherein the resin underlayer-forming composition further contains an antioxidant.

17. The anti-fogging article according to claim 16, wherein the content of the antioxidant is from 0.5 to 3 mass % to the total mass of the second polyepoxide component and the second curing agent.

18. The anti-fogging article according to claim 1, wherein the substrate is a soda lime glass.

19. A process for producing the anti-fogging article as defined in claim 1, which comprises:

a step of applying the resin underlayer-forming composition containing the second polyepoxide component and the second curing agent, to the surface of a substrate, followed by reaction to form the resin underlayer composed mainly of the second cured epoxy resin; and

a step of applying, to the surface of the resin underlayer, the water-absorptive resin layer-forming composition containing the first polyepoxide component consisting of the low molecular weight polyepoxide having a molecular weight of from 200 to 800 and the high molecular weight polyepoxide having a molecular weight of from 900 to 2,000 in a mass ratio of the low molecular weight polyepoxide;

the high molecular weight polyepoxide of from 30;

70 to 70;

30, and the first curing agent, followed by reaction to form the water-absorptive resin layer composed mainly of the first cured epoxy resin.

20. The production process according to claim 19, wherein the reaction of the resin underlayer-forming composition and the reaction of the water-absorptive resin layer-forming composition are carried out under humidified conditions of from 40 to 80% RH.

21. The production process according to claim 19, wherein after the step of forming the water-absorptive resin layer, the obtained substrate provided with the resin underlayer and the water-absorptive resin layer is dipped in warm water.